Análise da presa final de 5 cimentos biocerâmicos em canais amplos submetidos a diferentes condições de pH

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorVianna, Gustavo André de Deus Carneiro-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8005271079083909-
Autor(es): dc.contributorMaciel, Ana Carolina de Carvalho-
Autor(es): dc.contributorhttp://lattes.cnpq.br/5938210577790399-
Autor(es): dc.contributorSouza, Erick Miranda-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4091726534822849-
Autor(es): dc.contributorOliveira, Henrique Eduardo-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0366567315989831-
Autor(es): dc.contributorSassone, Luciana Moura-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4822604598628329-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1543425536003313-
Autor(es): dc.creatorAmaral, Clarissa Costa-
Data de aceite: dc.date.accessioned2025-01-03T11:37:08Z-
Data de disponibilização: dc.date.available2025-01-03T11:37:08Z-
Data de envio: dc.date.issued2024-11-21-
Data de envio: dc.date.issued2024-11-21-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/35456-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/919058-
Descrição: dc.descriptionO tempo de presa de um cimento impacta diretamente no desempenho clínico do mesmo, e essa habilidade ainda não foi completamente explicada. Assim como o Agregado Trióxido Mineral (MTA), os cimentos biocerâmicos são afetados pelo ambiente em que estão inseridos. O objetivo do presente estudo foi avaliar se houve presa de 5 cimentos biocerâmicos, utilizando canais amplos, em condições de pH ácido e neutro. Após o cálculo amostral, 45 amostras teriam 80% de poder de teste para encontrar um erro de no máximo 1%. No entanto, com o objetivo de se obter uma margem de segurança e aumentar a confiabilidade estatística do experimento, foram utilizados 96 incisivos superiores humanos extraídos em clínicas capacitadas da FOUFF, junto do TCLE devidamente assinado e com a aprovação do Comitê de Ética em Pesquisa da UFF. Os elementos foram acessados, as coroas e 2 mm dos ápices foram removidos e as raízes padronizadas com 10mm de comprimento, sendo então preparadas até o comprimento de trabalho (CT) com os instrumentos R25, R40 e R50. Depois, foram utilizados alargadores Peeso até o CT numa sequência #2-4. Os espécimes foram divididos aleatoriamente em 6 grupos: G1: Grupo de Referência- AH Plus Jet (Dentsply Sirona, Carolina do Norte, EUA); G2: AH Plus Biocerâmico (Dentsply Sirona, Carolina do Norte, EUA); G3: Endosequence (Brasseler USA, Geórgia, EUA); G4: Bio Root (Septodont Pensilvânia, EUA); G5: NeoSealer (Avalon Biomed, Texas, EUA); G6: Cimento Experimental. Para a obturação, cada amostra foi embutida em esponja floral umedecida com soluções de pH 7 ou pH 4, os canais foram secos com cones de papel R50 (Dentsply Sirona, Carolina do Norte, EUA), e obturados com cones de guta #40 taper 02 (MK Life, Rio Grande do Sul, Brasil) associados a 80 μL de cada um dos cimentos testados e radiografados. 50% dos espécimes de cada grupo foram armazenados a 37°C, 100% de umidade, por 21 dias, com pH 4; a outra metade, foi armazenada nas mesmas condições, mas com pH 7. Após 21 dias, foram radiografados, feitos cortes com labcut (Extec, Connecticut, EUA), resultando em fatias de 3 mm de espessura, e avaliados usando um aparelho Gillmore para determinar se o cimento se solidificou ou não. A análise estatística foi feita através de um teste não paramétrica (Kruskal-Wallis) para variáveis independentes sobre a variável dependente. As comparações foram feitas através de um teste post-hoc de Mann-Whitney U, com ajuste de Bonferroni. Os resultados indicaram que houve diferença estatisticamente significativa na presa do cimento AH Plus Biocerâmico (P=0,000), mas que não houve diferença significativa quando analisado o pH (P = 0,608). Portanto, concluiu-se que os cimentos testados obtiveram presa independentemente do pH em que se encontravam, e que o cimento AH Plus Biocerâmico obteve o pior resultado. Cabe realizar mais testes com o intuito de entendermos esse resultado.-
Descrição: dc.descriptionThe setting time of a cement directly impacts its clinical performance, and this ability has not yet been fully explained. Just like Mineral Trioxide Aggregate (MTA), bioceramic cements are affected by the environment they are placed in. The aim of the present study was to evaluate the setting ability of 5 bioceramic cements, using wide canals, under acidic and neutral pH conditions. After sample size calculation, 45 samples would have 80% test power to detect a maximum error of 1%. However, aiming for a margin of safety and to increase the statistical reliability of the experiment, 96 extracted human upper incisors were used from accredited clinics of FOUFF, with properly signed informed consent forms and approval from the Research Ethics Committee of UFF. The teeth were accessed, crowns and 2 mm of apices were removed, and roots were standardized to 10mm in length, then prepared to working length (WL) using R25, R40, and R50 instruments. Peeso reamers were then used up to WL in a #2-4 sequence. Specimens were randomly divided into 6 groups: G1: Control Group - AH Plus Jet (Dentsply Sirona, North Carolina, USA); G2: Bioceramic AH Plus (Dentsply Sirona, North Carolina, USA); G3: Endosequence (Brasseler USA, Georgia, USA); G4: Bio Root (Septodont Pennsylvania, USA); G5: NeoSealer (Avalon Biomed, Texas, USA); G6: Experimental Cement. For obturation, each sample was embedded in moist floral foam with pH 7 or pH 4 solutions, canals were dried with R50 paper points (Dentsply Sirona, North Carolina, USA), and obturated with #40 taper 02 gutta-percha cones (MK Life, Rio Grande do Sul, Brazil) combined with 80 μL of each of the tested cements and radiographed. Fifty percent of specimens from each group were stored at 37°C, 100% humidity, for 21 days, at pH 4; the other half were stored under the same conditions but at pH 7. After 21 days, they were radiographed, cut with labcut (Extec, Connecticut, USA) resulting in 3 mm thick slices, and evaluated using a Gillmore apparatus to determine if the cement had set or not. Statistical analysis was done using non-parametric tests (Kruskal-Wallis) for independent variables on the dependent variable. Comparisons were made using Mann-Whitney U post-hoc test, with Bonferroni adjustment. Results indicated a statistically significant difference in setting time of AH Plus Bioceramic cement (P=0.000, Kruskal-Wallis), but no significant difference was found when pH was analyzed (P = 0.608, Kruskal-Wallis). Therefore, it was concluded that the tested cements set independently of the pH they were in, and AH Plus Bioceramic cement had the poorest setting result. Further tests are needed to understand this outcome.-
Descrição: dc.description47 f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectBiocerâmicos-
Palavras-chave: dc.subjectPresa-
Palavras-chave: dc.subjectAH Plus-
Palavras-chave: dc.subjectEndosequence-
Palavras-chave: dc.subjectBio root-
Palavras-chave: dc.subjectNeoSealer-
Palavras-chave: dc.subjectCimentos dentários-
Palavras-chave: dc.subjectCerâmicas modificadas organicamente-
Palavras-chave: dc.subjectMateriais restauradores do canal radicular-
Palavras-chave: dc.subjectBioceramics-
Palavras-chave: dc.subjectSetting ability-
Palavras-chave: dc.subjectAH Plus-
Palavras-chave: dc.subjectEndosequence-
Palavras-chave: dc.subjectBio root-
Palavras-chave: dc.subjectNeoSealer-
Título: dc.titleAnálise da presa final de 5 cimentos biocerâmicos em canais amplos submetidos a diferentes condições de pH-
Título: dc.titleAnalysis of the final setting time of 5 bioceramic cements in wide root canals exposed to different pH conditions-
Tipo de arquivo: dc.typeDissertação-
Aparece nas coleções:Repositório Institucional da Universidade Federal Fluminense - RiUFF

Não existem arquivos associados a este item.