Atenção: Todas as denúncias são sigilosas e sua identidade será preservada.
Os campos nome e e-mail são de preenchimento opcional
Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.creator | Paiva, José Antônio Euzébio | - |
Autor(es): dc.creator | Daza, Paola Cristina Cajas | - |
Autor(es): dc.creator | Rodrigues, Fernanda Amaral | - |
Autor(es): dc.creator | Ortiz Mosquera, Jairo F. | - |
Autor(es): dc.creator | Silva, Cosme Roberto Moreira da | - |
Autor(es): dc.creator | Muñoz, Marly Montero | - |
Autor(es): dc.creator | Meneses, Rodrigo Arbey Muñoz | - |
Data de aceite: dc.date.accessioned | 2024-10-23T16:46:16Z | - |
Data de disponibilização: dc.date.available | 2024-10-23T16:46:16Z | - |
Data de envio: dc.date.issued | 2020-05-26 | - |
Data de envio: dc.date.issued | 2020-05-26 | - |
Data de envio: dc.date.issued | 2019 | - |
Fonte completa do material: dc.identifier | https://repositorio.unb.br/handle/10482/37874 | - |
Fonte completa do material: dc.identifier | https://doi.org/10.1016/j.ceramint.2020.04.212 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/916862 | - |
Descrição: dc.description | In this study, we prepared strontium-doped lanthanum ferrites with the perovskite-type structure for application as solid oxide fuel cell (SOFC) cathodes. We used the Pechini method to prepare strontium-doped lanthanum ferrites with the strontium:lanthanum molar ratios of 20:80 and 40:60. The resulting doped materials were characterized using various analytical tools. The calcination process was conducted at 450 °C because above this temperature, the stabilization of mass loss occurred and no phase transformation was observed. The X-ray diffraction results confirmed the mixing of the powder phases after the calcination process and the presence of a single powder phase in the air-sintered samples. The high-resolution transmission electron microscopy results revealed the presence of agglomerated nanoparticles smaller than 20 nm in size in the samples. The electrochemical impedance spectroscopy results revealed that the sample with 20% strontium exhibited a conductivity of 3.9 × 10−3 S cm−1 at 95 °C and activation energy of 0.37 eV. In contrast, the sample with 40% strontium exhibited a conductivity of 3.5 × 10−2 S cm−1 and activation energy of 0.29 eV. These results suggest that with an increase in the strontium content, the conductivity of the samples increased, where as the activation energy of the conduction process decreased. Therefore, the ferrites synthesized in this work are potential catalysts for SOFC cathodes. | - |
Descrição: dc.description | Faculdade UnB Gama (FGA) | - |
Publicador: dc.publisher | Elsevier | - |
Relação: dc.relation | https://www.sciencedirect.com/science/article/pii/S0272884220311561?via%3Dihub | - |
Direitos: dc.rights | Acesso Restrito | - |
Palavras-chave: dc.subject | Método de Pechini | - |
Palavras-chave: dc.subject | Ferrita de lantânio dopado com estrôncio | - |
Palavras-chave: dc.subject | Células a combustível de óxido sólido | - |
Palavras-chave: dc.subject | Espectroscopia de impedância | - |
Título: dc.title | Synthesis and electrical properties of strontium-doped lanthanum ferrite with perovskite-type structure | - |
Tipo de arquivo: dc.type | livro digital | - |
Aparece nas coleções: | Repositório Institucional – UNB |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: