Síntese e caracterização do BaTiO3 obtido pelos métodos sol-gel e sol-precipitação

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorSilva, Alysson Martins Almeida-
Autor(es): dc.contributorgeorgenalmeida@hotmail.com-
Autor(es): dc.creatorAlmeida, George do Nascimento-
Data de aceite: dc.date.accessioned2024-10-23T16:36:52Z-
Data de disponibilização: dc.date.available2024-10-23T16:36:52Z-
Data de envio: dc.date.issued2021-06-09-
Data de envio: dc.date.issued2021-06-09-
Data de envio: dc.date.issued2021-06-09-
Data de envio: dc.date.issued2021-01-12-
Fonte completa do material: dc.identifierhttps://repositorio.unb.br/handle/10482/41126-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/912866-
Descrição: dc.descriptionDissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2020.-
Descrição: dc.descriptionO objetivo geral deste trabalho é obter pós nanométricos de BaTiO3 através do método sol-gel e sol-precipitação, acompanhados de sua adequada caracterização estrutural, ótica e elétrica para entender seu mecanismo de formação. Os precursores utilizados no método sol-gel foram o Ortotitanato de Tetraisopropil dissolvido em 2-propanol, ácido acético e acetato de bário. As amostras do gel obtidas foram calcinadas a 600°C, 800°C e 1000°C. Pelo método sol-precipitação, os precursores utilizados foram Ortotitanato de Tetraisopropil dissolvido em ácido acético, água deionizada. A esta solução foi adicionada uma solução concentrada de KOH e outra de Acetato de Bário. Os produtos foram caracterizados por DRX, MEV, UV-VIS e espectroscopia de impedância. O resultado dessas análises permitiu observar nas amostras produzidas pelo método sol-gel um aumento da fase tetragonal e da constante dielétrica (15 – 50 em 20Hz) com o aumento da temperatura, enquanto as amostras obtidas por sol-precipitação são cúbicas. A presença do BaCO3 é mais evidente nas amostras produzidas por sol-precipitação e o band-gap dos produtos obtidos não mostrou variação significativa alterando-se o método de síntese (3,363 – 3,594 eV).-
Descrição: dc.descriptionThe general objective of this work is to obtain nanometric powders of BaTiO3 through the sol-gel and sol-precipitation method, accompanied by their proper structural, optical and electrical characterization to understand their formation mechanism. The precursors used in the sol-gel method were Tetraisopropyl Orthotitanate dissolved in 2-propanol, acetic acid and barium acetate. The gel samples obtained were calcined at 600 °C, 800 °C and 1000 °C. Through the sol-precipitation method, the precursors used were Tetraisopropyl Orthotitanate dissolved in acetic acid, deionized water. To this solution was added a concentrated solution of KOH and another of Barium Acetate. The products were characterized by XRD, SEM, UV-VIS and impedance spectroscopy. The results of these analyzes allowed to observe in the samples produced by the sol-gel method an increase in the tetragonal phase and the dielectric constant with the increase in temperature, while the samples obtained by sol-precipitation are cubic. The presence of BaCO3 is more evident in the samples produced by sol-precipitation and the band-gap of the obtained products did not show significant variation, changing the synthesis method (3,363 - 3,594 eV).-
Formato: dc.formatapplication/pdf-
Direitos: dc.rightsAcesso Aberto-
Direitos: dc.rightsA concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data.-
Palavras-chave: dc.subjectTitanato de bário-
Palavras-chave: dc.subjectSol-precipitação-
Título: dc.titleSíntese e caracterização do BaTiO3 obtido pelos métodos sol-gel e sol-precipitação-
Tipo de arquivo: dc.typelivro digital-