Atenção: Todas as denúncias são sigilosas e sua identidade será preservada.
Os campos nome e e-mail são de preenchimento opcional
Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Muterlle, Palloma Vieira | - |
Autor(es): dc.creator | Brandão, Nilo José Lima da Silva | - |
Data de aceite: dc.date.accessioned | 2024-10-23T15:09:22Z | - |
Data de disponibilização: dc.date.available | 2024-10-23T15:09:22Z | - |
Data de envio: dc.date.issued | 2017-02-16 | - |
Data de envio: dc.date.issued | 2017-02-16 | - |
Data de envio: dc.date.issued | 2017-02-16 | - |
Data de envio: dc.date.issued | 2016-12-01 | - |
Fonte completa do material: dc.identifier | http://repositorio.unb.br/handle/10482/22619 | - |
Fonte completa do material: dc.identifier | http://dx.doi.org/10.26512/2016.12.D.22619 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/875817 | - |
Descrição: dc.description | Dissertação (mestrado)—Universidade de Brasília, Faculdade UnB Gama, Programa de Pós-Graduação em Integridade de Materiais da Engenharia, 2016. | - |
Descrição: dc.description | As ligas com memória de forma possuem a capacidade de recuperar sua forma original após deformações severas. No comportamento pseudoelástico a liga possui capacidade dissipativa de energia, em decorrência do laço de histerese. Com o objetivo de conhecer a influência das temperaturas de envelhecimento na histerese de ligas de NiTi, adotou-se como metodologia a fabricação de molas helicoidais feitas com um fio comercial de NiTi com composição em peso de aproximadamente 56% de níquel e 44% de titânio, diâmetro de 2,16 mm e microestrutura em fase austenítica. Os corpos de prova (molas) passaram por tratamento térmico de 500 °C para alívio de tensão e foram envelhecidos nas temperaturas de 350 °C, 450 °C, 550 °C e 600 °C com isoterma de 30 minutos e têmpera em água. As molas foram ensaiadas mecanicamente para obtenção dos gráficos de histerese e caracterizadas por calorimetria exploratória diferencial (DSC), difração de raio X (DRX) e ensaios de microdureza vickers. O tratamento térmico de alívio de tensão (500 °C) e os envelhecimentos de 350 °C, 450 °C e 550 °C desenvolveram fase R. As temperaturas de transformação martensítica diminuíram para todas as amostras tratadas termicamente. Os tratamentos térmicos reduziram o valor da microdureza nas amostras quando comparadas à liga como recebida. Os tratamentos de envelhecimento de 350 °C e 450 °C em temperatura ambiente apresentam fase austenita, fase R e precipitação Ni2Ti. O envelhecimento de 350 °C aparentemente apresentou menor laço de histerese e o tratamento térmico de 500 °C o maior laço de histerese quando comparados todos os tratamentos. | - |
Descrição: dc.description | The shape memory alloys have the ability to recover the original form, after large deformations. In pseudoelasticity, the alloy having energy dissipation capacity, as a result of the hysteresis loop. The objective is to know the influence of aging temperatures on the mechanical properties of a NiTi pseudoelastic. Springs were made with commercial wire NiTi, with composition 54% of Ni and 42 % of Ti, diameter 2.16 mm and austenitic microstructure. The springs had heat treatment for stress relief (500 °C), posteriorly the samples were heat-aging treatment at temperatures of 350 °C, 450 °C, 550 °C and 600 °C. The springs underwent mechanical testing, DSC, RXD, vickers microhardness. The aging treatment of 350 ° C, 450 ° C, 500 ° C and 550 ° C developed R phase. Heat treatment reduced the hardness of the samples. The martensitic transformation temperatures decreased for all thermally treated samples. The aging treatments of 350 °C and 450 °C at ambient temperature exhibit in their austenite phase, R phase and Ni2Ti precipitation. The aging treatment of 350 ° C apparently showed smallest hysteresis loop and heat treatment of 500 ° C the largest hysteresis loop when comparing with the all treatments. | - |
Formato: dc.format | application/pdf | - |
Direitos: dc.rights | Acesso Aberto | - |
Direitos: dc.rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data. | - |
Palavras-chave: dc.subject | Pseudoelasticidade | - |
Palavras-chave: dc.subject | Ligas (Metalurgia) | - |
Palavras-chave: dc.subject | Deformações (Mecânica) | - |
Título: dc.title | Influência da temperatura de envelhecimento na histerese de molas de NiTi, Distrito Federal, 2016 | - |
Tipo de arquivo: dc.type | livro digital | - |
Aparece nas coleções: | Repositório Institucional – UNB |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: