Avaliação da estabilidade de cor de laminados cerâmicos após ciclagem térmica em soluções corantes e luz ultravioleta

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorPoskus, Laiza Tatiana-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1589157970272919-
Autor(es): dc.contributorNoronha Filho, Jaime Dutra-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1785530002642447-
Autor(es): dc.contributorMiragaya, Luciana Meireles-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8923032431096718-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0632789589802764-
Autor(es): dc.creatorPereira, Juliana Ferreira Batista-
Data de aceite: dc.date.accessioned2024-07-22T13:56:03Z-
Data de disponibilização: dc.date.available2024-07-22T13:56:03Z-
Data de envio: dc.date.issued2024-07-12-
Data de envio: dc.date.issued2024-07-12-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/33276-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/823251-
Descrição: dc.descriptionEste estudo objetivou avaliar a estabilidade de cor de laminados cerâmicos após termociclagem em soluções pigmentantes (TSP), água destilada (TAD) e ciclagem de luz ultravioleta (LUV), utilizando cimentos resinosos duais (CD) e fotoativados (CF). Primeiramente, foi manipulado um material de base, contendo na matriz orgânica (40% p/p) os monômeros BisGMA (70%p/p) e TEGDMA (30%p/p), e na porção inorgânica (60% p/p), partículas de bário alumino silicato (0.7μm) (75%p/p) e de sílica (0.04nm) (25%p/p), ambas pré-silanizadas. Na pasta base dos cimentos duais foi adicionado o peróxido de benzoíla (0,5%p/p), e na pasta catalisadora foram adicionados o EDMAB (1%p/p), a canforoquinona (0,5%p/p) e o N N-Dihidroxietil-P-TOLUIDINA (0,25%p/p). No cimento fotoativado adicionaram-se o EDMAB (1%p/p) e a canforoquinona (0,5%p/p). O grau de conversão (GC%) (FTIR), e a sorção (SO) e solubilidade (SL) (ISO4049) foram analisadas para os cimentos experimentais. 72 fragmentos cerâmicos (6 x 5 x 0,8 mm) foram cimentados utilizando os cimentos experimentais sobre 72 fragmentos de dentes bovinos (5 x 4 x 2 mm). Após aferição inicial da cor com um espectrofotômetro (CIELaB), os espécimes foram divididos em três grupos (n=12): TSP, TAD e LUV. A cor final foi aferida para cálculo da alteração de cor (ΔEab). Os dados foram submetidos ao teste de normalidade (Shapiro-Wilk) e homogeneidade (Levene). Desse modo, foi realizada a análise de variância e o teste de Tukey (5%) para GC%, SO e SL, e o teste de Kruskall Wallis e Mann-Whitney para ΔEab. Observou-se que o CD apresentou maior grau de conversão e sorção (p<0.05), além de maior ΔEab após TSP e TAD (p<0.05). A solubilidade foi semelhante para ambos os cimentos (p=0). O AEab para o CD foi semelhante para os tipos de ciclagem TSP, TAD e ambos maiores que LUV, e para o CF, a LUV alterou mais a cor do que a TAD (p<0.05) e foi semelhante TSP (p=0). Conclui-se que o modo de ativação dual de cimentos resinosos pode influenciar em suas propriedades físicas, e promover maior alteração de cor em laminados cerâmicos após envelhecimento por ação de soluções pigmentantes e luz.-
Descrição: dc.descriptionThe objective of the present study was to evaluate the color stability of ceramic laminates after thermocycling in staining beverages (TSP), destiled water (TAD) and ultraviolet light cycling (LUV), using dual (CD) and photoactivated (CF) resin cements. Firstly, a base material was manipulated, containing in the organic matrix (40% p/p) the monomers BisGMA (70% p/p) and TEGDMA (30% p/p), and in the organic portion (60% p/p), barium aluminosilicate (0.7um) (75% p/p) and silica (0.04nm) (25% p/p) particles, both pre-silanized. Benzoyl peroxide (0.5% p/p) was added to the base paste of the dual cements, and EDMAB (1% p/p), camphorquinone (0.5% p/p) and N N-DihydroxyethylP-TOLUIDINE (0.25% p/p) were added to the catalyst paste. In the photoactivated cement was added only EDMAB (1% p/p) and camphorquinone (0.5% p/p). The degree of conversion (GC %) (FTIR), and the sorption (SO) and solubility (SL) (ISO4049) were analyzed for the experimental cements. 72 ceramic fragments (6 x 5 x 0,8 mm) were cemented using experimental cements on 72 fragments (5 x 4 x 2 mm) of bovine teeth. After initial color measurement with a spectrophotometer (CIELAB), the specimens were divided into three groups (n=12): TSP, TAD and LUV. The final color was measured to calculate the color change (ΔEab). The data were subjected to normality (Shapiro-Wilk) and homogeneity (Levene) tests. Therefore, the analysis of variance and the Tukey test (5%) were performed for GC%, SO and SL, and the Kruskall Wallis and Mann-Whitney tests for ΔEab. It was observed that the CD presented a higher degree of conversion and sorption (p<0.05), and a higher ΔEab after TSP and TAD (p<0.05). Solubility was similar for both cements (p=0). The ΔEab for CD was similar for TSP, TAD and both higher than LUV, and for CF, LUV changed the color more than TAD (p<0.05) and was equal to TSP (p= 0). It is concluded that the dual activation mode of resin cements can influence their physical properties and promote higher color changes in ceramic laminates after aging, due to the action of pigments and light.-
Descrição: dc.description27 f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectAlteração de cor-
Palavras-chave: dc.subjectLaminados cerâmicos-
Palavras-chave: dc.subjectCimentos resinosos-
Palavras-chave: dc.subjectFacetas dentárias-
Palavras-chave: dc.subjectCor-
Palavras-chave: dc.subjectCorantes-
Palavras-chave: dc.subjectCimentos de resina-
Palavras-chave: dc.subjectColor change-
Palavras-chave: dc.subjectCeramic laminate-
Palavras-chave: dc.subjectResin cements-
Título: dc.titleAvaliação da estabilidade de cor de laminados cerâmicos após ciclagem térmica em soluções corantes e luz ultravioleta-
Título: dc.titleEvaluation of stability of ceramic laminate veneer’s color after thermocycling with staining beverages and UV light-