Caracterização microestrutural destrutiva de molas de aço inoxidável austenítico AISI 316L suscetíveis à falha por corrosão sob tensão

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorAlmeida, Brígida Bastos de-
Autor(es): dc.contributorPardal, Juan Manuel-
Autor(es): dc.contributorGarcia, Pedro Soucasaux Pires-
Autor(es): dc.creatorCosta, Caio Brandão da-
Autor(es): dc.creatorGuimarães, Kelvin Peres-
Data de aceite: dc.date.accessioned2024-07-11T18:45:48Z-
Data de disponibilização: dc.date.available2024-07-11T18:45:48Z-
Data de envio: dc.date.issued2022-02-16-
Data de envio: dc.date.issued2022-02-16-
Data de envio: dc.date.issued2021-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/24572-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/777053-
Descrição: dc.descriptionOs componentes mecânicos molas podem ser expostos a milhões de ciclos de carga durante o serviço, ou ter que manter uma força constante por vários anos. Também podem ser expostos a ambientes corrosivos, inclusive em altas temperaturas. Como a aplicação das molas, estudada neste trabalho, é para um ambiente offshore, a utilização do aço inoxidável austenítico AISI 316L se torna interessante, devido à sua elevada resistência à corrosão. Para a caracterização microestrutural de molas de aço inoxidável austenítico AISI 316L suscetíveis à falha por corrosão sob tensão, foram realizados diferentes ensaios, como difratometria por raios X, micrografia, ensaio mecânico de dureza, ensaio eletromagnético de ferritoscopia e ensaio de resistividade elétrica. Em seguida, foi realizado um tratamento térmico de solubilização e, para comparação, alguns testes foram refeitos para a amostra solubilizada.-
Descrição: dc.descriptionThe mechanical components springs can be exposed to millions of load cycles during service, or have to maintain a constant force for several years. They also can be exposed to corrosive environments, including high temperatures. As the application of mechanical springs, studied in this work, is for an offshore environment, the use of AISI 316L austenitic stainless steel becomes interesting, due to its high corrosion resistance. For the microstructural characterization of AISI 316L austenitic stainless steel springs susceptible to stress corrosion cracking, different tests were performed, such as X-ray diffractometry, micrography, mechanical hardness test, an electromagnetic test of ferritoscopy, and electrical resistivity test. Then, a solution heat treatment was carried out, and, for comparison, some tests were redone for the solubilized sample.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Publicador: dc.publisherUniversidade Federal Fluminense-
Publicador: dc.publisherNiterói-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectMolas-
Palavras-chave: dc.subjectAço inoxidável austenítico AISI 316L-
Palavras-chave: dc.subjectCaracterização microestrutural-
Palavras-chave: dc.subjectMola-
Palavras-chave: dc.subjectAço inoxidável austenítico-
Palavras-chave: dc.subjectMicroestrutura-
Palavras-chave: dc.subjectCorrosão-
Palavras-chave: dc.subjectAISI 316L austenitic stainless steel-
Palavras-chave: dc.subjectSprings-
Palavras-chave: dc.subjectMicrostructural characterization-
Título: dc.titleCaracterização microestrutural destrutiva de molas de aço inoxidável austenítico AISI 316L suscetíveis à falha por corrosão sob tensão-
Tipo de arquivo: dc.typeTrabalho de conclusão de curso-