Caracterização do ruído magnético Barkhausen do aço USI SAR 80T retificado com rebolo de carboneto de silício

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorBenini, Lucas-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7687650050636319-
Autor(es): dc.contributorMoraes Júnior, José Mauro-
Autor(es): dc.contributorMirres, Sandro Pimentel-
Autor(es): dc.contributorhttp://lattes.cnpq.br/5617251697195671-
Autor(es): dc.creatorCoelho, Romulo Rossi-
Data de aceite: dc.date.accessioned2024-07-11T18:42:29Z-
Data de disponibilização: dc.date.available2024-07-11T18:42:29Z-
Data de envio: dc.date.issued2023-11-16-
Data de envio: dc.date.issued2023-11-16-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/31179-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/775902-
Descrição: dc.descriptionOs aços alta resistência e baixa liga (ARBL) são materiais de grande relevância para a indústria mecânica por combinarem boas propriedades mecânicas com alta resistência à corrosão e economia de peso. O aço USI SAR 80T vem ganhando espaço em diversos setores industriais devido à alta resistência mecânica, elevada tenacidade e considerável resistência à corrosão e à fadiga, sendo utilizados em construção de embarcações, vasos de pressão e aplicações automobilísticas. No contexto do processamento dos ARBL, a retificação plana é de grande relevância na qualidade do acabamento superficial e precisão dimensional. Contudo, devido à alta geração de calor durante a retificação, há a possibilidade de alteração microestrutural da superfície usinada, resultando na diminuição da resistência, além de alterar as tensões residuais. Um método não destrutivo que pode detectar essas alterações é o ruído magnético Barkhausen (RMB), uma vez que o ruído é influenciado pelo estado de tensão residual e dureza da superfície usinada. O objetivo deste trabalho é avaliar o RMB gerado na retificação plana de amostras de aço USI SAR 80T empregando um rebolo de SiC. Foram variadas a profundidade de corte e a velocidade de avanço da peça, e, posteriormente, mensurados os sinais RMB. A medição da rugosidade e da dureza complementaram os resultados. O aumento da velocidade de avanço e da profundidade de corte não gerou diferenças significativas nos sinais RMB. Observou-se também que o aumento da velocidade de avanço e da profundidade de corte contribuiu para a redução dos valores de rugosidade. A variação nos parâmetros de usinagem não exerceu influência significativa sobre a dureza Vickers das amostras-
Descrição: dc.descriptionHigh-strength, low-alloy steels (HSLA) are materials of great relevance to the mechanical industry because they combine good mechanical properties with high corrosion resistance and weight savings. USI SAR 80T steel has been gaining ground in various industrial sectors due to its high mechanical strength, elevated toughness, and considerable resistance to corrosion and fatigue, being used in shipbuilding, pressure vessels, and automotive applications. In the context of HSLA processing, flat grinding is of great importance for the quality of surface finish and dimensional precision. However, due to the high heat generation during grinding, there is the possibility of microstructural alteration of the machined surface, resulting in a decrease in strength, as well as altering residual stresses. A non-destructive method that can detect these changes is the Barkhausen magnetic noise (MBN), as the noise is influenced by the residual stress and hardness of the machined surface. The objective of this work is to evaluate the BMN generated in the flat grinding of USI SAR 80T steel samples using a SiC grinding wheel. The cutting depth and workpiece feed rate were varied, and the MBN signals were subsequently measured. Roughness and hardness measurements complemented the results. The increase in feed rate and cutting depth did not result in significant differences in the MBN signals. It was also observed that the increase in feed rate and cutting depth contributed to the reduction of roughness values. Variation in machining parameters did not exert a significant influence on the Vickers hardness of the samples-
Descrição: dc.description40 p.-
Formato: dc.formatapplication/pdf-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectAço USI SAR 80T-
Palavras-chave: dc.subjectRetificação plana-
Palavras-chave: dc.subjectRugosidade-
Palavras-chave: dc.subjectDureza Vickers-
Palavras-chave: dc.subjectRuído magnético Barkhausen-
Palavras-chave: dc.subjectAço de alta resistência e baixa liga-
Palavras-chave: dc.subjectRugosidade (Superfície)-
Palavras-chave: dc.subjectDureza-
Palavras-chave: dc.subjectUSI SAR 80T steel-
Palavras-chave: dc.subjectSurface grinding-
Palavras-chave: dc.subjectRoughness-
Palavras-chave: dc.subjectMagnetic Barkhausen noise-
Palavras-chave: dc.subjectHardness Vickers-
Título: dc.titleCaracterização do ruído magnético Barkhausen do aço USI SAR 80T retificado com rebolo de carboneto de silício-