Análise da influência do tratamento de superfície da vitrocerâmica à base de dissilicato de lítio com primer cerâmico autocondicionante e com ácido fluorídrico

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorSantos, Claudinei dos-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1355748902111663-
Autor(es): dc.contributorElias, Carlos Nelson-
Autor(es): dc.contributorhttp://lattes.cnpq.br/3220111929133519-
Autor(es): dc.contributorMagnago, Roberto de Oliveira-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1905410995938951-
Autor(es): dc.contributorhttp://lattes.cnpq.br/6493994580946194-
Autor(es): dc.creatorKlippel, Gesinete Gonçalves Pinto-
Data de aceite: dc.date.accessioned2024-07-11T18:41:39Z-
Data de disponibilização: dc.date.available2024-07-11T18:41:39Z-
Data de envio: dc.date.issued2022-11-10-
Data de envio: dc.date.issued2022-11-10-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26931-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/775626-
Descrição: dc.descriptionO objetivo deste estudo foi avaliar o efeito do prétratamento superficial de vitrocerâmicas dentárias à base de dissilicato de lítio (Li2Si2O5) usando um primer autocondicionante na resistência ao cisalhamento (SBS) e na topografia de superfície em comparação ao prétratamento padrão com ácido fluorídrico. Amostras comerciais de dissilicato de lítio utilizadas em fresagem CAD/CAM foram distribuídas em 3 grupos: 1 – sem tratamento (C); 2 –tratamento de superfície com ácido fluorídrico (HF) 10% por 20s seguido da aplicação de um agente silano (S) e um adesivo (A) (HF + S + A); 3 –tratamento de superfície com primer cerâmico autocondicionante (MBEP). Amostras comerciais de metassilicato de lítio (Li2SiO3) contendo 54,5 % de fase amorfa, foram submetidas a tratamento térmico de cristalização a 840°C7min, e caracterizadas quanto a sua microestrutura utilizando MEV, identificação e quantificação de fases por difração de raiosX e rugosidade utilizando perfilometria 3D. Para a análise de resistência de união por cisalhamento, foram polimerizados pinos de cimento resinoso divididos igualmente entre os grupos (n=12). Os resultados foram submetidos a análise estatística. Após o tratamento térmico, as amostras continham Li2Si2O5 como única fase cristalina presente e 21,4 % de fase amorfa residual. Grãos alongados com alta razão de aspecto foram observados nesse material. Os resultados da morfologia superficial do dissilicato de lítio após diferentes ataques químicos indicam que o G2 e G3 produziram alterações superficiais em relação ao G1. O G2 com alterações estruturais mais severas que o G3. Os grupos G1, G2 e G3 apresentaram resistência ao cisalhamento de, 5,3 ± 0,9 MPa, 24,25 ± 1,2 MPa e 24,8 ± 1,8 MPa, respectivamente. A análise estatísticas ANOVA e teste de Turkey mostraram que não há diferença significativa entre os grupos G2 e G3 e ambos apresentam diferenças estatísticas em relação ao G1. Os módulos de Weibull do grupo G2 (mG2 = 19) e G3 (mG3 = 13) foram superiores ao grupo controle G1 (mG1 = 6). O tratamento convencional com ácido fluorídrico e com primer cerâmico autocondicionante apresentaram resultados semelhantes de resistência de união, portanto, possuem o mesmo efeito na adesividade nas próteses de dissilicato de lítio.-
Descrição: dc.descriptionThe aim of this study was to evaluate the effect of the surface pretreatment of lithium disilicate (Li2Si2O5) based glass ceramic using a selfetching primer on shear strength (SBS) and surface topography compared to standard acid pretreatment hydrofluoric. Commercial samples of lithium disilicate used in CAD / CAM milling were distributed in 3 groups: 1 without treatment (C); 2 surface treatment with 10% hydrofluoric acid (HF) for 20s followed by the application of a silane agent (S) and an adhesive (A) (HF + S + A); 3 surface treatment with selfetching ceramic primer (MBEP). Commercial samples of lithium metasilicate (Li2SiO3) containing 54,5 % of amorphous phase, were subjected to thermal crystallization treatment at 840 ° C7min, and characterized for their microstructure using SEM, identification and quantification of phases by ray diffraction X and roughness using 3D profiling. For the analysis of shear bond strength, resin cement pins were polymerized and divided equally between groups (n = 12). The results were subjected to statistical analysis. After heat treatment, the samples contained Li2Si2O5 as the only crystalline phase present and 21,4 % residual amorphous phase. Elongated grains with a high aspect ratio were observed in this material. The results of the superficial morphology of lithium disilicate after different chemical attacks indicate that G2 and G3 produced superficial changes in relation to G1. G2 with structural changes more severe than G3. Groups G1, G2 and G3 showed shear strength of 5.3 ± 0.9 MPa, 24.25 ± 1.2 MPa and 24.8 ± 1.8 MPa, respectively. The ANOVA statistical analysis and the Turkey test showed that there is no significant difference between groups G2 and G3 and both show statistical differences in relation to G1. Weibull modules in the G2 (mG2 = 19) and G3 (mG3 = 13) groups were superior to the G1 control group (mG1 = 6). Conventional treatment with hydrofluoric acid and selfetching ceramic primer showed similar results of bond strength, therefore, they have the same effect on adhesion in lithium disilicate prostheses.-
Descrição: dc.description89 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectDissilicato de lítio-
Palavras-chave: dc.subjectResistência ao cisalhamento-
Palavras-chave: dc.subjectÁcido fluorídrico-
Palavras-chave: dc.subjectPrimer cerâmico autocondicionante-
Palavras-chave: dc.subjectVitrocerâmica-
Palavras-chave: dc.subjectDissilicato de lítio-
Palavras-chave: dc.subjectPrimer autocondicionante-
Palavras-chave: dc.subjectResistência de materiais-
Palavras-chave: dc.subjectÁcido fluorídrico-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectProdução intelectual-
Palavras-chave: dc.subjectLithium disilicate-
Palavras-chave: dc.subjectShear strength-
Palavras-chave: dc.subjectHydrofluoric acid-
Palavras-chave: dc.subjectSelfetching ceramic primer-
Título: dc.titleAnálise da influência do tratamento de superfície da vitrocerâmica à base de dissilicato de lítio com primer cerâmico autocondicionante e com ácido fluorídrico-