Desenvolvimento de compósitos restauradores remineralizantes com partículas de hidrogel dopadas com CaF2

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorReis, Renata Nunes Jardim-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9482803270572801-
Autor(es): dc.contributorSilva, Eduardo Moreira da-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0084980191573168-
Autor(es): dc.contributorSantos, Glauco Botelho dos-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4279178900289101-
Autor(es): dc.contributorWeig, Karin de Mello-
Autor(es): dc.contributorhttp://lattes.cnpq.br/6582316308756435-
Autor(es): dc.contributorhttp://lattes.cnpq.br/5205476336358913-
Autor(es): dc.creatorCosta, Ana Carolina Augusto-
Data de aceite: dc.date.accessioned2024-07-11T18:41:10Z-
Data de disponibilização: dc.date.available2024-07-11T18:41:10Z-
Data de envio: dc.date.issued2023-07-20-
Data de envio: dc.date.issued2023-07-20-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/29445-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/775459-
Descrição: dc.descriptionO desenvolvimento de materiais restauradores com partículas capazes de liberar íons possibilita uma potencialização no processo remineralizante dos tecidos dentários que foram desmineralizados por ácidos orgânicos produzidos pelo biofilme oral. Visto que a cárie recorrente ainda é uma das maiores causas de troca de restaurações no mundo, o desenvolvimento de materiais capazes de remineralizar as estruturas dentárias e com boas características mecânicas se faz necessário. Diante disso, o objetivo do presente projeto foi a síntese de compósitos restauradores remineralizantes com partículas poliméricas carregadas com fluoreto de cálcio. As partículas de hidrogel foram sintetizadas por meio de polimerização térmica de uma mistura de trimetacrilato (TMPTMA) com 2-hidroxietilmetacrilato (HEMA) numa proporção de 50/50% em peso e 0,5%p de peróxido de benzoíla. À essa mistura, foram adicionadas diferentes concentrações de CaF2: 5%, 10% e 15% em peso e a mesma foi levada à estufa à 120oC por 18h para a polimerização. Quatro compósitos restauradores experimentais foram sintetizados: C, CaF5, CaF10 e CaF15, com matriz orgânica (30 % p/p) composta de Bis-GMA (70% p/p) e TEGDMA (30% p/p) e canforoquinona/etil N,N-dimetil-4aminobenzoato (0,5/1% p/p). Como referência comercial, foi utilizada a resina Durafill VS – Kulzer (DF). Foram realizados testes para avaliação do potencial remineralizante após a ciclagem de pH. Foram realizados testes físicos de dureza Knoop (DK) e rugosidade (Ra). Após a realização, foram feitos testes estatísticos específicos, os valores obtidos por CaF10 e CaF15 foram eficazes no processo de remineralização do esmalte adjacente. Ra apresentou valores semelhantes entre todos os grupos e DK apresentou valores menores para DF e maiores para C (p<0,05). O acréscimo do TMP-TMA-HEMA-CaF2 nos compósitos experimentais não resultou em alterações negativas nas propriedades físicas e foi capaz de remineralizar o esmalte.-
Descrição: dc.descriptionThe development of restorative materials with particles capable of releasing ions enables a potentiation in the remineralizing process of dental tissues that were demineralized by organic acids produced by the oral biofilm. Since recurrent caries is still one of the biggest causes of replacement of restorations in the world, the development of materials capable of remineralizing dental structures and with good mechanical characteristics is necessary. Therefore, the objective of the present project was the synthesis of remineralizing restorative composites with polymeric particles loaded with calcium fluoride. The hydrogel particles were synthesized by means of thermal polymerization of a mixture of trimethacrylate (TMPTMA) with 2- hydroxyethylmethacrylate (HEMA) in a ratio of 50/50% by weight and 0.5%w of benzoyl peroxide. Different concentrations of CaF2 were added to this mixture: 5%, 10% and 15% by weight and it was taken to an oven at 120oC for 18h for polymerization. Four experimental restorative composites were synthesized: C, CaF5, CaF10 and CaF15, with organic matrix (40% w/w) composed of Bis-GMA (70% w/w) and TEGDMA (30% w/w) and camphorquinone/ethyl N,N-dimethyl-4aminobenzoate (0.5/1% w/w). As a commercial reference, Durafill VS – Kulzer (DF) resin was used. Tests were performed to evaluate the remineralizing potential after pH cycling. Physical tests of Knoop hardness (DK) and roughness (Ra) were performed. After performing, specific statistical tests were performed, the values obtained by CaF10 and CaF15 were effective in the process of remineralization of adjacent enamel. Ra showed similar values between all groups and DK showed lower values for DF and higher for C (p<0.05). The addition of TMP-TMA-HEMA-CaF2 in the experimental composites did not result in negative changes in physical properties and was able to remineralize the enamel.-
Descrição: dc.description27 f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Publicador: dc.publisherNiterói-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectCompósitos remineralizantes-
Palavras-chave: dc.subjectcárie-
Palavras-chave: dc.subjectfluoreto de cálcio-
Palavras-chave: dc.subjectCárie dentária-
Palavras-chave: dc.subjectRestauração dentária permanente-
Palavras-chave: dc.subjectFluoreto de Cálcio-
Palavras-chave: dc.subjectResinas Compostas-
Palavras-chave: dc.subjectPlaca Dentária-
Palavras-chave: dc.subjectDesmineralização do Dente-
Palavras-chave: dc.subjectRemineralizing composites-
Palavras-chave: dc.subjectcaries-
Palavras-chave: dc.subjectcalcium fluoride-
Título: dc.titleDesenvolvimento de compósitos restauradores remineralizantes com partículas de hidrogel dopadas com CaF2-