Análise comparativa da microestrutura e propriedades mecânicas do ferro fundido nodular austemperado

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorLopes, Luiz Carlos Rolim-
Autor(es): dc.contributorhttp://lattes.cnpq.br/6791638384395800-
Autor(es): dc.contributorFonseca, Gláucio Soares da-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9663765935778795-
Autor(es): dc.contributorPimenta, André Rocha-
Autor(es): dc.contributorhttp://lattes.cnpq.br/2962103182860488-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1638057149760085-
Autor(es): dc.creatorBaracho, Luciano Lobo de Almeida-
Data de aceite: dc.date.accessioned2024-07-11T18:37:27Z-
Data de disponibilização: dc.date.available2024-07-11T18:37:27Z-
Data de envio: dc.date.issued2022-11-15-
Data de envio: dc.date.issued2022-11-15-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26932-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/774156-
Descrição: dc.descriptionOs ferros fundidos nodulares austemperados (ADI), são materiais de engenharia que adquiriram grande importância tecnológica e comercial, devido à combinação de propriedades como boa ductilidade e alta resistência mecânica, elevada tenacidade a fratura, alta resistência à fadiga e excelente resistência ao desgaste, aliadas ao baixo custo de produção. Tais propriedades são resultantes de sua microestrutura que é composta basicamente de uma mistura de ferrita acicular, austenita retida com elevado teor de carbono e nódulos de grafita. Neste trabalho, o efeito de diferentes temperaturas de austêmpera em uma liga comercial de ADI- Cu, Ni, Mo, produziram ADI’s com alta resistência mecância, correspondendo ao GRAU IV da ASTM. Os principais resultados mostram que existe uma forte relação entre temperatura de austêmpera e propriedades mecânicas, assim como microestruturas. O maior limite de resistência foi a austêmpera em 280ºC, 1473 Mpa, e a maior energia absorvida em impacto foi a austêmpera em 320ºC, 99,90J, que também obteve maior quantidade de austenita retida, 27%.-
Descrição: dc.descriptionCoordenação de Aperfeiçoamento de Pessoal de Nível Superior-
Descrição: dc.descriptionAustempered ductile cast irons (ADI) have been received great attention in last years because their combined properties of good ductility, high strength and fracture toughness, good fatigue strength, good wear properties and low production cost. Such combination of properties can be reach because of their microstructures consist of a mixture acicular ferrite (bainite), residual austenite with a high carbon content and nodular graphite. In this work, the effect of different austempering treatment on the microstructure of a commercial ADI-Cu, Ni, Mo alloy produced ADI’s with elevated mechanical properties, corresponding to the ASTM grade IV requirements. The main results show that there is strong relationship between austempering temperatures and mechanical properties. The highest tensile strength obtained, was the austempering of 280ºC, 1473 Mpa, the highest charpy impact energy absortion was 320ºC, 99,90 J, and the highest measured austenite % volume content was 27% in 320ºC too.-
Descrição: dc.description63 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectFerro fundido nodular austemperado-
Palavras-chave: dc.subjectAustenita retida-
Palavras-chave: dc.subjectASTM-
Palavras-chave: dc.subjectCaracterização microestrutural-
Palavras-chave: dc.subjectFerro fundido nodular-
Palavras-chave: dc.subjectTratamento térmico-
Palavras-chave: dc.subjectLiga (Metalurgia)-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectProdução intelectual-
Palavras-chave: dc.subjectAustempered ductile iron-
Palavras-chave: dc.subjectRetained austenite-
Palavras-chave: dc.subjectASTM-
Palavras-chave: dc.subjectMicrostructure characterization-
Título: dc.titleAnálise comparativa da microestrutura e propriedades mecânicas do ferro fundido nodular austemperado-
Tipo de arquivo: dc.typeDissertação-
Aparece nas coleções:Repositório Institucional da Universidade Federal Fluminense - RiUFF