Efeito da temperatura no crescimento e resistência à corrosão de filmes de óxidos anódicos formados sobre a liga AZ31 tratada termicamente

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorFerreira, Elivelton Alves-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9791486511562981-
Autor(es): dc.contributorCarvalho, Adriana Evaristo de-
Autor(es): dc.contributorhttp://lattes.cnpq.br/6039969237116219-
Autor(es): dc.contributorAssis, Weslley Luiz da Silva-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8444210181194986-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4523051229968637-
Autor(es): dc.creatorZenóbio, Isadora Rapoza-
Data de aceite: dc.date.accessioned2024-07-11T18:36:12Z-
Data de disponibilização: dc.date.available2024-07-11T18:36:12Z-
Data de envio: dc.date.issued2022-11-09-
Data de envio: dc.date.issued2022-11-09-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26915-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/773731-
Descrição: dc.descriptionAs ligas de magnésio são consideradas um dos materiais mais promissores para uso futuro em muitas aplicações de engenharia. Elas vêm sendo usadas como implantes biodegradáveis graças à sua biocompatibilidade e excelentes propriedades mecânicas, que se assemelham às do osso humano. No entanto, devido à sua alta reatividade química e eletroquímica, essas ligas possuem baixa resistência à corrosão em ambientes aquosos, como o fisiológico. Melhorar essa propriedade por meio da aplicação de um revestimento pode ser uma ótima alternativa para expandir o uso dessas ligas. O procedimento de oxidação a microarco (MicroArc Oxidation – MAO) é um método bemsucedido na formação de revestimentos de óxidos sobre substratos de ligas de magnésio. A natureza da camada de óxidos formada e o desempenho frente à corrosão dependem tanto dos parâmetros do processo MAO (eletrólito, tempo de processamento, temperatura, etc), como das características específicas do substrato. No presente estudo, filmes de óxidos anódicos foram crescidos via oxidação a microarco em eletrólito alcalino de KOH + Na2SiO3, em duas temperaturas distintas, sobre amostras da liga de magnésio AZ31 (3% em peso Al e 1% Zn), as quais sofreram diferentes tratamentos térmicos a fim de proporcionar diferentes características microestruturais. O revestimento MAO formado foi caracterizado por Microscopia Eletrônica de Varredura e por Difração de RaiosX, e a resistência à corrosão foi avaliada por meio de análises de Espectroscopia de Impedância Eletroquímica em solução de Hank. Os revestimentos formados a 25° C apresentaram maior resistência à corrosão, com a amostra envelhecida por mais tempo tendo obtido o melhor desempenho, enquanto que, à temperatura ambiente, o comportamento observado foi o oposto.-
Descrição: dc.descriptionCoordenação de Aperfeiçoamento de Pessoal de Nível Superior.-
Descrição: dc.descriptionMagnesium alloys are considered the one of the most promising materials for future engineering applications. They have been used as biodegradable implants due to their biocompatibility and excellent mechanical properties, which resemble those of human bone. However, because of their high chemical and electrochemical reactivity, these alloys have low resistance to corrosion in aqueous environments, such as physiological. Improving this property through the application of a coating can be a great alternative to expand their use. The microarc oxidation procedure (MAO) is a successful method for producing oxide coatings on magnesium alloy substrates. The nature of the oxide layer formed and the performance against corrosion depend both on the parameters of the MAO process (electrolyte, processing time, temperature, etc.), as well as on the specific characteristics of the substrate. In this study, anodic oxide films grew through microarc oxidation in KOH + Na2SiO3 alkaline electrolyte at two different temperatures, on samples of magnesium alloy AZ31 (3% by weight Al and 1% Zn), which were processed by different heat treatments in order to provide different microstructural characteristics. The MAO coating was characterized by Scanning Electron Microscopy and XRay Diffraction. The corrosion resistance was evaluated by means of Electrochemical Impedance Spectroscopy analyzes in Hank's solution. The coatings formed at 25 ° C showed greater resistance to corrosion, with the sample aged for a longer time having obtained the best performance, whereas, at room temperature, the observed behavior was the opposite.-
Descrição: dc.description89 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectLigas de magnésio-
Palavras-chave: dc.subjectRevestimento MAO-
Palavras-chave: dc.subjectTemperatura do eletrólito-
Palavras-chave: dc.subjectMicroestrutura do substrato-
Palavras-chave: dc.subjectEspectroscopia de impedância eletroquímica-
Palavras-chave: dc.subjectCorrosão-
Palavras-chave: dc.subjectResistência à corrosão-
Palavras-chave: dc.subjectLiga de magnésio-
Palavras-chave: dc.subjectÓxido anódico-
Palavras-chave: dc.subjectTratamento térmico-
Palavras-chave: dc.subjectProcessamento e caracterização de materiais-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectProdução intelectual-
Palavras-chave: dc.subjectMagnesium alloys-
Palavras-chave: dc.subjectMAO coating-
Palavras-chave: dc.subjectElectrolyte temperature-
Palavras-chave: dc.subjectSubstrate microstructure-
Palavras-chave: dc.subjectElectrochemical impedance spectroscopy-
Palavras-chave: dc.subjectCorrosion-
Título: dc.titleEfeito da temperatura no crescimento e resistência à corrosão de filmes de óxidos anódicos formados sobre a liga AZ31 tratada termicamente-