Influência do tempo e da temperatura de austêmpera na microestrutura e nas propriedades mecânicas no ferro fundido nodular austemperado (ADI)

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorFonseca, Gláucio Soares da-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9663765935778795-
Autor(es): dc.contributorFreitas, Maria Carolina dos Santos-
Autor(es): dc.contributorhttp://lattes.cnpq.br/5037625890837841-
Autor(es): dc.contributorMagnago, Roberto de Oliveira-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1905410995938951-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0959095925917950-
Autor(es): dc.creatorTissi, Giulliana Victória-
Data de aceite: dc.date.accessioned2024-07-11T18:29:29Z-
Data de disponibilização: dc.date.available2024-07-11T18:29:29Z-
Data de envio: dc.date.issued2023-06-12-
Data de envio: dc.date.issued2023-06-12-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/29090-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/771611-
Descrição: dc.descriptionO ferro fundido nodular austemperado, do inglês Austempered Ductile Iron (ADI), apresenta excelentes propriedades mecânicas como alta resistência à tração, boa ductilidade, alta resistência à fadiga e à fratura e excelente resistência ao desgaste, que o torna um material interessante para um grande número de aplicações de engenharia. As excelentes propriedades do ADI estão relacionadas com a microestrutura do material, denominada ausferrita, e com o ciclo de tratamento térmico de austêmpera, várias propriedades mecânicas podem ser obtidas a partir de uma mesma liga, variando o tempo e a temperatura de austêmpera. Sendo assim, com o intuito de avaliar a influência do tempo e da temperatura de austêmpera no ADI, neste trabalho, analisou­se as modificações microestruturais e as propriedades mecânicas das amostras de ferro fundido nodular, sujeitos ao tratamento térmico de austêmpera com temperatura e tempo de austenitização, de 910°C e 90 minutos para todas as amostras, e em seguida, durante o banho de austêmpera, as amostras foram submetidas a diferentes temperaturas, 300, 320, 340, 360 e 380°C, e em quatro tempos distintos para cada temperatura, 75, 110, 145 e 180 minutos. Para as análises microestruturais, foram utilizadas as técnicas microscópicas óptica e eletrônica de varredura e as propriedades mecânicas foram obtidas por meio de ensaios mecânicos de tração, dureza e impacto. Os resultados deste estudo mostram que existe uma grande relação entre temperatura de austêmpera com a microestrutura e as propriedades mecânicas. O maior valor de austenita retida e impacto foi 25,73% e 130 J, respectivamente, para a amostra austemperada a 380°C e 180 minutos, por outro lado, o maior valor de dureza e limite de resistência à tração foi 458 HB e 1384 MPa, respectivamente, para a amostra austemperada a 300°C e 75 minutos.-
Descrição: dc.descriptionAustempered Ductile Iron (ADI) has excellent mechanical properties such high tensile strength, good ductility, fatigue strength, fracture strength, and high wear resistance, that makes an interesting material for a large number of engineering applications. The excellent properties of ADI are related to the microstructure of the material, called ausferrite, and with the cycle of austempering heat treatment many mechanical properties can be obtained from the same alloy, simply changing the austempering time and austempering temperature. Thus, in order to evaluate the influence of austempering time and austempering temperature on the ADI, in this work, analyzed the modifications in the microstructures and mechanical properties of the samples of nodular cast iron, subjected to austempering heat treatment with and austenitizing time and temperature of 910°C and 90 minutes for all samples, and then, during the austempering bath, the samples were submitted to different temperatures, 300, 320, 340, 360 e 380°C, and for four different times for each temperature, 75, 110, 145 and 180 minutes. For the microstructural analysis the microscopic techniques were used optical and scanning electronics and the mechanical properties were obtained by mechanical testing of tensile, hardness and impact. The results of this study show that there is a strong relationship between austempering temperature with microstructure and mechanical properties. The highest retained austenite and impact value was 25,73% and 130 J, respectively, for the autempered sample at 380°C and 180 minutes, on the other hand, the highest hardness and tensile strength limit value was 458 HB and 1384 MPa, respectively, for the autempered sample at 300°C and 75 minutes.-
Descrição: dc.description77 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectFerro fundido nodular austemperado (ADI)-
Palavras-chave: dc.subjectTemperatura de austêmpera-
Palavras-chave: dc.subjectTempo de austêmpera-
Palavras-chave: dc.subjectMicroestrutura-
Palavras-chave: dc.subjectPropriedades mecânicas-
Palavras-chave: dc.subjectTratamento térmico de austêmpera-
Palavras-chave: dc.subjectBanho de austêmpera-
Palavras-chave: dc.subjectProdução intelectual-
Palavras-chave: dc.subjectEngenharia Mecânica-
Palavras-chave: dc.subjectAustempered Ductile Iron (ADI)-
Palavras-chave: dc.subjectAustempering temperature-
Palavras-chave: dc.subjectAustempering time-
Palavras-chave: dc.subjectMicrostructure-
Palavras-chave: dc.subjectMechanical properties-
Título: dc.titleInfluência do tempo e da temperatura de austêmpera na microestrutura e nas propriedades mecânicas no ferro fundido nodular austemperado (ADI)-
Tipo de arquivo: dc.typeDissertação-
Aparece nas coleções:Repositório Institucional da Universidade Federal Fluminense - RiUFF

Não existem arquivos associados a este item.