Estudo do efeito da soldagem na microestrutura e resistência à corrosão do aço inoxidável duplex SAF 2205

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorFonseca, Gláucio Soares da-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9663765935778795-
Autor(es): dc.contributorNogueira, Tânia Maria Cavalcanti-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1309300835320812-
Autor(es): dc.contributorRios, Paulo Rangel-
Autor(es): dc.contributorhttp://lattes.cnpq.br/2150558011507981-
Autor(es): dc.contributorReis, Danieli Aparecida Pereira-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7058867464306125-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7197679933678385-
Autor(es): dc.creatorGarcia, Thaís da Silva Leite-
Data de aceite: dc.date.accessioned2024-07-11T18:29:19Z-
Data de disponibilização: dc.date.available2024-07-11T18:29:19Z-
Data de envio: dc.date.issued2022-10-25-
Data de envio: dc.date.issued2022-10-25-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26678-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/771551-
Descrição: dc.descriptionO presente trabalho teve como objetivo analisar a microestrutura e a resistência à corrosão de um aço inoxidável duplex SAF 2205 (UNS S31803) soldado por um processo MIG/MAG. Esse aço tem por característica apresentar as fases austenita (γ) e ferrita (α) balanceadas, ou seja; em torno de 50% de cada uma, o que confere ao aço boa resistência mecânica e a corrosão. Devido ao processo de soldagem ocorre a formação de três regiões distintas na microestrutura do aço, sendo elas: zona fundida (ZF), zona termicamente afetada (ZTA) e metal base (MB). Principalmente na ZF e ZTA pode ocorrer o desbalanceamento das fases γ e α. podendo prejudicar suas propriedades mecânicas e/ou químicas. Assim um estudo sobre essas alterações é necessário para se conhecer o comportamento do aço mediante a soldagem. Primeiramente foram feitas análises da fração volumétrica (VV) de ferrita na microestrutura do aço por meio de microscopia ótica (MO) e ferritoscopia. Os estudos realizados nas três regiões da microestrutura foram baseados de acordo com: a espessura dos corpos de prova (10 e 20 mm), a energia de soldagem (0,66; 1,23; 1,93 e 2,57kJ/mm) e gases de proteção (ArCO2-N2) e (Ar-O2) utilizados na soldagem. Em seguida foi analisada a resistência à corrosão por pites das amostras utilizando ensaios de polarização potenciostática realizada em solução de 3,5% NaCl nas três regiões presentes no corpo de prova (MB, ZTA e ZF) , avaliando se o processo de soldagem interfere nos potenciais de pite, de corrosão e na densidade de corrente de pite do aço SAF 2205. Foi verificado que com os parâmetros de ensaio de polarização utilizados, o potencial de pite e densidade de corrente de pites sofrem poucas alterações significativas ao processo, ou seja, independente da região analisada os valores de potencial de pite pouco é influenciado pela energia e os gases de proteção utilizados na soldagem.-
Descrição: dc.descriptionThe present work aims to analyze the microstructure and corrosion resistance of the duplex stainless steel SAF 2205 (UNS S31803) welded by a MIG/MAG process. The SAF 2205 (UNS S31803) presents balanced austenite (γ) and ferrite (α) phases, in other words, around 50% of each one, which gives to it mechanical and corrosion resistance. Due to weld process there is a formation of three distinct regions on steel microstructure: melting zone (MZ), heated-affected zone (HAZ) and base metal (BM). Mainly on MZ and HAZ can occur γ and α phases unbalance, that can damage their mechanicals and/or chemical properties. Thus a study about this changes are necessary to know the duplex steel behavior through welding. Firstly were made analyses of the volumetric percentage (%v) of the ferrite microstructure by an optical microscopy (OM) and a ferritoscopy. The study were carried out on three regions according with: samples thickness (10 and 20 mm), the heat input (0.66; 1.23;1.93 and 2.57 kJ/mm) and protection gases (Ar-CO2-N2 and Ar-O2) used on welding. Afterward the pitting corrosion resistance of the welded samples were analyzed by a potenciostatic polarization test carry out on a solution of 3.5% NaCl in three regions presents on the samples (BM, HAZ and MZ), to consider if the welding process interfere on pitting and corrosion potentials and in the pitting current density of the steel SAF 2205. It was verified that with the polarization parameters used, the pitting potential and pitting current density suffer a little significant changes about process, in other words, independent of analyzed region the pitting potential values is a little influenced by energy and protection gases used on welding-
Descrição: dc.description150 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectAço inoxidável duplex-
Palavras-chave: dc.subjectSoldagem-
Palavras-chave: dc.subjectResistência à corrosão-
Palavras-chave: dc.subjectProcessamento e caracterização de materiais-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectSoldagem MIG/MAG-
Palavras-chave: dc.subjectCorrosão do aço-
Palavras-chave: dc.subjectMicroestrutura-
Palavras-chave: dc.subjectAço inoxidável-
Palavras-chave: dc.subjectProdução Intelectual-
Palavras-chave: dc.subjectDuplex stainless steel-
Palavras-chave: dc.subjectWelding-
Palavras-chave: dc.subjectCorrosion resistance-
Título: dc.titleEstudo do efeito da soldagem na microestrutura e resistência à corrosão do aço inoxidável duplex SAF 2205-
Tipo de arquivo: dc.typeDissertação-
Aparece nas coleções:Repositório Institucional da Universidade Federal Fluminense - RiUFF

Não existem arquivos associados a este item.