Avaliação visual e microscópica do efeito de materiais fluoretados na prevenção da desmineralização do esmalte bovino adjacente a bráquetes ortodônticos

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorCoutinho, Thereza Christina Lopes-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0830876392851574-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9325691799716501-
Autor(es): dc.creatorPaula, Ligia Dias de-
Data de aceite: dc.date.accessioned2024-07-11T18:20:48Z-
Data de disponibilização: dc.date.available2024-07-11T18:20:48Z-
Data de envio: dc.date.issued2019-10-24-
Data de envio: dc.date.issued2019-10-24-
Data de envio: dc.date.issued2015-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/11804-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/768738-
Descrição: dc.descriptionO objetivo deste estudo in vitro foi comparar o efeito de materiais fluoretados na prevenção da desmineralização do esmalte adjacente a bráquetes ortodônticos. Cinqüenta e dois incisivos bovinos foram planificados e polidos e bráquetes foram colados na superfície vestibular por meio de uma resina composta fotopolimerizável (Transbond XT - 3M). Após, as coroas foram protegidas por três camadas de um verniz ácido-resistente, exceto para uma área de 4 milímetros ao redor do bráquete. Em seguida, os dentes foram divididos aleatoriamente em 4 grupos experimentais (n = 13): Grupo 1 (CO) - controle - esmalte não tratado; Grupo 2 (DF) - esmalte foi tratado com verniz fluoretado (Duofluoride XII® - FGM); Grupo 3 (CL) - esmalte foi tratado com selante de ionômero de vidro modificado por resina (ClinproTM XT - 3M); Grupo 4 (NP) - esmalte foi tratado com pasta de nanopartículas de fosfato de cálciohidroxiapatita (Desensibilize Nano P com 9000 ppmF como NaF - FGM). Os materiais foram aplicados sobre o esmalte em torno dos bráquetes de acordo com as instruções do fabricante. Todos os dentes foram mantidos em saliva artificial durante 12 horas antes do experimento. As amostras foram submetidas à ciclagem de pH, sendo mantidos em uma solução remineralizante por 18h e em uma solução desmineralizante por 6 horas durante 14 dias. Após esse período, os espécimes foram fotografados usando uma câmera digital de acordo com procedimentos padronizados e estas fotografias foram avaliadas, duplo-cego, por três examinadores calibrados para a verificação da ocorrência de lesões de mancha branca (LMB) por análise visual, utilizando escala de Geiger et al (1988). A área e o percentual de cada LMB foram obtidos por meio da análise das fotos no software Imagem Tool® 3.0. Após a remoção dos bráquetes, os dentes foram analisados ao MEV sob aumentos de 1250x 5000x a fim de examinar o padrão de desmineralização da LMB em cada grupo. Os dados foram analisados estatisticamente por meio do software SPSS para Windows v. 20 utilizando os testes de Mann-Whitney e Kruskall-Walis. Observou-se que, em 100% das amostras do grupo de NP e em 92,3% no grupo CO tinha um grau de desmineralização 3. No grupo CL, 100% das amostras apresentaram grau 2 e no grupo DF, 61,5% tinham grau 1 e 38,5%, grau 2. Considerando-se a área da LMB, o grupo DF teve uma menor desmineralização estatisticamente significativa (H=23,36; p=0,000) (5.98mm2 ) quando comparado aos grupos CO (118.14mm2 ), NP (113.98mm2 ) e CL (108.44mm2) que não diferiram entre si e do CO (p> 0,05). A percentagem da desmineralização do esmalte (H = 28,91; p = 0,000) foi em ordem decrescente: DF (4,14%) <NP (72,41%) = CL (73,37%) = CO (78,84%). A análise qualitativa das imagens ao MEV mostrou que, com exceção do grupo DF, os demais grupos experimentais apresentaram padrão de desmineralização semelhante ao grupo CO. Concluiu-se que, o verniz fluoretado teve maior efeito protetor contra a formação de LMB em comparação com os outros materiais testados, sendo eficaz na inibição da desmineralização do esmalte adjacente a bráquetes ortodônticos-
Descrição: dc.descriptionThe aim of this in vitro study was to compare the effect of fluoride materials in the prevention of enamel demineralization adjacent to orthodontic brackets. Fifty two bovine incisors were ground flat and polished, and orthodontic brackets were bonded on their buccal surface by means of a light-cured composite resin (TransbondTM XT – 3M). Afterwards, the crown of the specimens was protected by three layers of an acid-resistant varnish except for an area of 4mm around the bracket. Then, the teeth were randomly divided into 4 experimental groups (n=13): Group 1 (CO) – control - untreated enamel; Group 2 (VF) - enamel was treated with fluoride varnish (Duofluoride XII® - FGM); Group 3 (CL) - enamel was treated with resin modified glass ionomer sealant (Clinpro TM XT - 3M); Group 4 (NP) - enamel was treated with calcium phosphate nanoparticles paste - hydroxyapatite (Desensibilize Nano P with 9000 ppmF as NaF - FGM). The materials were applied on the enamel around the brackets according to manufacturer’s instructions. All teeth were kept in artificial saliva for 12 hours prior to the experiment. The samples were submitted to pH cycling, being kept in a remineralizing solution for 18h and in a demineralizing solution for 6h during 14 days. After this period, the specimens were photographed using a digital camera following standardized procedures and these photographs were evaluated double-blind by three calibrated examiners for the occurrence of white spot lesions (WSL) by visual analysis using a 4-grade scale. The area and the percentage of each WSL were obtained by analysis of these photos in the software Image Tool® 3.0. After brackets removal, the teeth were analyzed by SEM under 1250x and 5000x magnifications in order to examine the demineralization pattern of the WSL in each group. Data were statistically analized by means of SPSS for Windows v. 20 software using Kruskall-Walis and Mann-Whitney tests. It was observed that, 100 % of the samples in the NP group and 92.3 % in the CO group had a grade 3 demineralization. In the CL group, 100 % of the samples had grade 2 and in the DF group, 61.5% had grade 1 and 38.5%, grade 2. Considering the WSL area, DF group had a statistically significant (H=23,36; p=0.000) less demineralization (5.98mm2 ) when compared to CO (118.14mm2 ), NP (113.98mm2) and CL (108.44mm2) groups that did not differ from each other and from CO (p>0.05). The percentage of the enamel demineralization (H=28.91; p=0.000) was in descending order: DF (4.14%) < NP (72.41%) = CL (73.37%) = CO (78.84%). The qualitative analysis of the SEM images has shown that with exception of DF group, the other experimental groups had demineralization pattern similar to CO group. It was concluded that, fluoride varnish had more protective effect against WSL formation compared to the other materials tested, being effective in inhibiting enamel demineralization adjacent to orthodontic brackets-
Descrição: dc.description44f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectMaterial dentário-
Palavras-chave: dc.subjectDesmineralização-
Palavras-chave: dc.subjectVerniz fluoretado-
Palavras-chave: dc.subjectSelante de fóssulas e fissuras-
Palavras-chave: dc.subjecthidroxiapatita-
Palavras-chave: dc.subjectResina composta-
Palavras-chave: dc.subjectSelante de fossa e fissura-
Palavras-chave: dc.subjectDesmineralização do dente-
Palavras-chave: dc.subjectHidroxiapatita-
Palavras-chave: dc.subjectBovino-
Palavras-chave: dc.subjectDental material-
Palavras-chave: dc.subjectDemineralization-
Palavras-chave: dc.subjectFluoride varnish-
Palavras-chave: dc.subjectPit and fissure sealant-
Palavras-chave: dc.subjectHydroxyapatite-
Título: dc.titleAvaliação visual e microscópica do efeito de materiais fluoretados na prevenção da desmineralização do esmalte bovino adjacente a bráquetes ortodônticos-
Título: dc.titleVisual and microscopic examination of the effect of fluoride materials in preventing enamel demineralization adjacent to orthodontic brackets-