Avaliação das diferentes formas de utilização da proantocianidina como agente biomodificador de dentina

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorPortela, Maristela Barbosa-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7374992387363131-
Autor(es): dc.contributorSilva, Eduardo Moreira-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0084980191573168-
Autor(es): dc.contributorNeves, Aline de Almeida-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4013097333638910-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0323380043915102-
Autor(es): dc.creatorMachado Neto, Carlos Roberto-
Data de aceite: dc.date.accessioned2024-07-11T18:20:23Z-
Data de disponibilização: dc.date.available2024-07-11T18:20:23Z-
Data de envio: dc.date.issued2024-07-09-
Data de envio: dc.date.issued2024-07-09-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/33111-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/768590-
Descrição: dc.descriptionA proantocianidina (PA), polifenol de origem natural, extraído da semente de uva, é um agente biomodificador da dentina que preserva a camada híbrida, tornando o colágeno menos degradável e diminuindo a ação das proteases dentinárias. Este trabalho comparou diferentes formas de utilização da PA (solução de pré-tratamento dentinário, incorporada no ácido fosfórico e acrescentada a um sistema adesivo) com relação à força de adesão dentinária, propriedades mecânicas da camada híbrida e degradação da dentina através da inibição da atividade proteolítica. O estudo foi realizado a partir de testes de microtração, testes de nanodureza e módulo de elasticidade da camada híbrida, e também mensuração da atividade proteolítica das enzimas da matriz dentinária. Foram utilizados 72 dentes onde foram confeccionados blocos de resina de acordo com 4 grupos: controle, PA 6,5% em uma solução de pré-tratamento (PAPT), PA 2% incorporada em um ácido fosfórico 10% (PAAF) e PA 4,5% adicionada a um sistema adesivo de 2 passos experimental (PASA). Cada grupo foi subdividido em 3 tempos de análise (após 24 horas, após 12 meses de estocagem em água e após desafio cariogênico microbiano). De cada dente restaurado, foi removida uma fatia de 1,5 mm para o teste de nanodureza e o restante foi cortado em palitos de 1 mm2 para o teste de microtração. A degradação da dentina foi medida pela dosagem de hidroxiprolina liberada de amostras de dentina que foram previamente desmineralizadas e incubadas nas soluções citadas acima. Os resultados foram submetidos a análise estatística em um nível de significância de 95%. Os grupos com PA apresentaram maior resistência de união quando comparados ao grupo controle após envelhecimento de 12 meses, sendo que PAPT e PAAF apresentaram os maiores valores. Não foram encontradas diferenças significantes entre o grupos controle, PAPT, PAAF e PASA com relação a dureza e módulo de elasticidade da camada híbrida. Os grupos com PA apresentaram baixos níveis de degradação comparado ao controle, mas sem diferença estatística entre eles. Conclui-se que o uso da PA como solução de pré-tratamento da dentina e incorporada ao ácido fosfórico 10% apresentaram melhores resultados quanto à preservação da força de adesão ao longo do tempo, sem modificação nas propriedades mecânicas da camada híbrida e nos níveis de degradação do colágeno dentinário.-
Descrição: dc.descriptionProanthocyanidin (PA), a polyphenol of natural origin, extracted from grape seeda, is a dentin biomodifier agent that preserves the hybrid layer, making collagen less degradable and observed the action of dentin proteases. This work compares different presentation forms of PA: 1) dentin pre-treatment solution, 2) incorporated into phosphoric acid and 3) added to an adhesive system regarding dentin bond strength, hybrid layer mechanics properties and dentin degradation (through the mechanics of proteolytic activity). The study was carried out with the aid of microtensile tests, nanohardness, evaluation of the modulus of elasticity of the hybrid layer and measurement of the proteolytic activity of enzymes in the dentin matrix. Seventy-two teeth were used where resin blocks were made according to 4 groups: control, 6.5% PA in a pre-treatment solution (PAPT), 2% PA incorporated in 10% phosphoric acid solution (PAAF) and 4.5% PA added to an experimental 2-step adhesive system (PASA). Each group was subdivided into 3 analysis times (after 24 hours, after 12 months of storage in water and after microbial cariogenic challenge). From each specimen, a 1.5 mm slice was removed for the nanohardness test and the remaining was cut into 1mm2 sticks for the microtensile test. Dentin degradation was measured by measuring hydroxyproline released from a dentin beans that was previously demineralized and incubated in the solutions mentioned above. The results were confirmed by statistical analysis at a significance level of 95%. The groups with PA showed higher bond strength when compared to the control group after aging for 12 months, where PAPT and PAAF showed higher values than PASA. No significant differences were found between the control, PAPT, PAAF and PASA groups regarding hardness and modulus of elasticity of the hybrid layer. The groups with PA showed low levels of degradation compared to the control, but with no statistical difference between them. The use of PA as a pre-treatment dentin solution or incorporated into a 10% phosphoric acid solution showed better results in terms of preservation of bond strength over time, without changing the mechanical properties of the hybrid layer and the levels of dentin collagen degradation.-
Descrição: dc.description45 f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectProantocianidina-
Palavras-chave: dc.subjectDentina-
Palavras-chave: dc.subjectColágeno-
Palavras-chave: dc.subjectAdesão dentária-
Palavras-chave: dc.subjectMódulo de elasticidade-
Palavras-chave: dc.subjectMicrotração-
Palavras-chave: dc.subjectProtease-
Palavras-chave: dc.subjectDentina-
Palavras-chave: dc.subjectPolifenóis-
Palavras-chave: dc.subjectProantocianidinas-
Palavras-chave: dc.subjectSolubilidade da dentina-
Palavras-chave: dc.subjectAdesivos dentinários-
Palavras-chave: dc.subjectResistência à tração-
Palavras-chave: dc.subjectTeste de dureza-
Palavras-chave: dc.subjectMódulo de elasticidade-
Palavras-chave: dc.subjectProanthocyanidin-
Palavras-chave: dc.subjectDentin-
Palavras-chave: dc.subjectCollagen-
Palavras-chave: dc.subjectDental adhesion-
Palavras-chave: dc.subjectElastic modulus-
Palavras-chave: dc.subjectMicrotensile-
Palavras-chave: dc.subjectProtease-
Título: dc.titleAvaliação das diferentes formas de utilização da proantocianidina como agente biomodificador de dentina-
Título: dc.titleEvaluation of the different presentation forms of proanthocyanidin as a dentin biomodifier agent-