Efeito da natureza do eletrólito na reação de desprendimento do oxigênio durante a anodização do titânio

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorFerreira, Elivelton Alves-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9791486511562981-
Autor(es): dc.contributorAlmeida, Lucio Cesar de-
Autor(es): dc.contributorhttp://lattes.cnpq.br/6233656045399753-
Autor(es): dc.contributorAssis, Weslley Luiz da Silva-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8444210181194986-
Autor(es): dc.contributorhttp://lattes.cnpq.br/3899674621858639-
Autor(es): dc.creatorSaldanha, Renata Leal-
Data de aceite: dc.date.accessioned2024-07-11T18:14:34Z-
Data de disponibilização: dc.date.available2024-07-11T18:14:34Z-
Data de envio: dc.date.issued2022-11-03-
Data de envio: dc.date.issued2022-11-03-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26810-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/766536-
Descrição: dc.descriptionO óxido de titânio pode ser crescido por anodização e as consequentes propriedades de resistência à corrosão destes dependem de muitas variáveis, tais como a perturbação eletroquímica, o potencial de crescimento final, temperatura do banho eletrolítico e a natureza do eletrólito. Durante essa anodização, a reação de desprendimento de oxigênio é frequentemente observada, o que contribui para a redução da eficiência da corrente de formação do filme de óxido anódico. Com base nesses fatores foi avaliado neste trabalho o efeito eletrolítico na formação destes filmes na reação de desprendimento de oxigênio durante a anodização do Ti em soluções aquosas de H3PO4 e H2SO4 (com pH = 1). Os filmes anódicos foram formados sobre o titânio, sob condições de perturbações voltamétricas (VL) a 25 ºC. Os resultados obtidos por voltametria linear mostraram que os filmes crescidos na solução de H3PO4 acima de 3,0 V apresentaram densidades de correntes menores do que os filmes formados em H2SO4. Os filmes de óxido foram caracterizados por Espectroscopia de Impedância Eletroquímica (EIE) indicando que o filme mais resistivo foi o anodizado em solução de H3PO4. A partir das medidas de elipsometria foi possível determinar a permissividade elétrica dos óxidos formados nos diferentes eletrólitos. A avaliação das propriedades semicondutoras foi estimada pelo método de MottSchottky (MS), no qual, relacionase a densidade doadora dos filmes (ND) com as densidades de corrente, comprovando a maior ND no filme formado em H2SO4 com velocidade de varredura de 50 mV s1. Além disso, pôdese também avaliar o efeito dos eletrólitos de crescimento nas resistências à corrosão destes diferentes óxidos por meio da voltametria cíclica onde foi observado que em meios contendo íons cloreto e em soluções que simulam os fluídos corpóreos, a corrosão localizada não foi identificada. Finalmente, as caracterizações por Microscopia Eletrônica de Varredura (MEV) e Espectroscopia de raiosX por dispersão em energia (EDS) evidenciaram que as amostras não sofreram corrosão nos diferentes meios contendo cloreto.-
Descrição: dc.descriptionCoordenação de Aperfeiçoamento de Pessoal de Nível Superior.-
Descrição: dc.descriptionTitanium oxide can be grown by anodizing and the consequent corrosion resistance properties of these depend on many variables, such as electrochemical disturbance, final growth potential, temperature of the electrolytic bath and the nature of the electrolyte. During this anodization, the oxygen shedding reaction is frequently observed, which contributes to reducing the efficiency of the anodic oxide film formation current. Based on these factors, the electrolytic effect on the formation of these films in the oxygen shedding reaction during the anodization of Ti in aqueous solutions of H3PO4 and H2SO4 (with pH = 1) was evaluated in this work. Anodic films were formed on titanium, under conditions of voltammetric disturbances (VL) at 25 ºC. The results obtained by linear voltammetry showed that the films grown in the H3PO4 solution above 3.0 V showed lower current densities than the films formed in H2SO4. The oxide films were characterized by Electrochemical Impedance Spectroscopy (EIE) indicating that the most resistive film was anodized in H3PO4 solution. From the ellipsometry measurements it was possible to determine the electrical permittivity of the oxides formed in the different electrolytes. The evaluation of semiconductor properties was estimated by the MottSchottky (MS) method, in which the donor density of the films (ND) is related to the current densities, proving the highest ND in the film formed in H2SO4 with scanning speed 50 mV s1. Furthermore, it was also possible to evaluate the effect of growth electrolytes on the corrosion resistance of these different oxides by means of cyclic voltammetry where it was observed that in media containing chloride ions and in solutions that simulate body fluids, localized corrosion was not identified . Finally, the characterizations by Scanning Electron Microscopy (SEM) and Xray spectroscopy by energy dispersion (EDS) showed that the samples did not suffer corrosion in the different media containing chloride.-
Descrição: dc.description84 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectTitânio-
Palavras-chave: dc.subjectIncorporação de eletrólitos-
Palavras-chave: dc.subjectCorrosão-
Palavras-chave: dc.subjectImpedância-
Palavras-chave: dc.subjectMott-Schottky-
Palavras-chave: dc.subjectTitânio-
Palavras-chave: dc.subjectEletrólito-
Palavras-chave: dc.subjectAnodização-
Palavras-chave: dc.subjectProcessamento e caracterização de materiais-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectProdução intelectual-
Palavras-chave: dc.subjectTitanium-
Palavras-chave: dc.subjectIncorporation of electrolytes-
Palavras-chave: dc.subjectCorrosion-
Palavras-chave: dc.subjectImpedance-
Palavras-chave: dc.subjectMott-Schottky-
Palavras-chave: dc.subjectProcessamento e caracterização de materiais-
Título: dc.titleEfeito da natureza do eletrólito na reação de desprendimento do oxigênio durante a anodização do titânio-
Tipo de arquivo: dc.typeDissertação-
Aparece nas coleções:Repositório Institucional da Universidade Federal Fluminense - RiUFF

Não existem arquivos associados a este item.