Avaliação da rugosidade na superfície da zircônia, produzida com o jateamento de óxido de alumínio e com os lasers Erbium-YAG, Neodymium-Doped-YAG e CO2: uma revisão sistemática com meta-análise

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorFonseca, Edgard de Mello-
Autor(es): dc.contributorNoronha, Jaime-
Autor(es): dc.contributorSantana, Ronaldo Barcellos de-
Autor(es): dc.contributorAndreiuolo, Rafael Ferrone-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4157345552710867-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4161140131440509-
Autor(es): dc.creatorMartins, Felipe Villela-
Data de aceite: dc.date.accessioned2024-07-11T18:13:25Z-
Data de disponibilização: dc.date.available2024-07-11T18:13:25Z-
Data de envio: dc.date.issued2020-12-16-
Data de envio: dc.date.issued2020-12-16-
Data de envio: dc.date.issued2017-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/16409-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/766123-
Descrição: dc.descriptionO sucesso clínico e a confiabilidade de um sistema cerâmico estão diretamente ligados à integridade mecânica dos materiais e à resistência da união nas interfaces: ceramo-cerâmica ou cerâmica-adesivo. A fratura adesiva, também chamada de delaminação e a decimentação da peça protética, tem se mostrado como as falhas mais frequentes nas restaurações que utilizam a zircônia como infraestrutura. Com o objetivo de aumentar a força da união na interface, alguns autores propõem que seja feito um tratamento para aumentar a rugosidade na superficie da zircônia. Diferentes tipos de laser e jateamento com óxido de alumínio tem sido utilizados em pesquisas in-vitro, mas até o presente momento os resultados encontrados são divergentes. O objetivo desta Meta-Análise foi avaliar os resultados da rugosidade média na superfície da zircônia produzida com o jateamento de óxido de alumínio e com os lasers Erbium-YAG, Neodymium-Doped-YAG e CO2. Este estudo foi realizado de acordo com o PRISMA checklist. O processo PICO foi usado para desenvolver as estratégias de busca. A pesquisa bibliográfica foi realizada para identificar os artigos relevantes até abril de 2017 nas bases de buscas: MEDLINE via PubMed; Web of Science e Scopus . Os estudos selecionados foram submetidos à avaliação do risco de viés. Na meta-análise foram avaliados os dados das rugosidades médias, o desvio padrão do grupo experimental e, posteriormente, comparados com o grupo controle sem o tratamento da superfície. As análises foram realizadas no Review Manager Software versão 5.3. Dos 2724 estudos potencialmente elegíveis, 17 preencheram todos os critérios de inclusão e apresentaram risco de viés médio. Na análise global e por subgrupos, foi constatado que há diferença estatística (p ≤ 0,05) favorecendo os grupos experimentais. Os valores dos testes de I² foram maiores que 90% representando a alta heterogeneidade entre os estudos. Os corpos de prova pré-sinterizados submetidos ao jateamento, apresentaram maior rugosidade superficial se comparados ao jateamento após o processo de sinterização. Esta modificação possibilitou evitar a transformação da fase tetragonal para a fase monoclínica. Os resultados indicaram que o laser de Nd:YAG e CO2 formaram microfissuras superficiais. O laser de Erbium utilizado com menor intensidade de energia se apresenta como um método promissor para o tratamento superficial da zircônia-
Descrição: dc.descriptionThe clinical success and reliability of the ceramic system are directly related to the mechanical integrity of the materials and the bond strength at the interface. Adhesive fracture, also called delamination, and the decementation of the prosthetic crown, has been shown to be the most frequent failure in restorations using zirconia as an infrastructure. In order to increase the bond strength at the interface, some authors propose a treatment to increase the zirconia surface roughness. In laboratory studies, different types of laser and sand blasting with aluminum oxide have been applied. However, up to the present time, the studies performed presented divergent results. Different types of laser and sand blasting with aluminum oxide have been used in in-vitro research, but up to the present time the results found are divergent. The objective of this Meta-Analysis was to evaluate the results of the average roughness on the Y-TZP zirconia surface, produced with the aluminum oxide sand blasting and the Erbium-YAG, Neodymium-Doped-YAG or CO2 lasers. This study was performed according to the PRISMA checklist. The PICO process was used to develop search strategies. The bibliographic research was carried out to identify the relevant articles until April 2017 in the search bases: MEDLINE via PubMed; Web of Science and Scopus. The selected studies were submitted to bias risk assessment. In the meta-analysis were evaluated the data of the roughness mean, the standard deviation of the experimental group and compared with the control group without the surface treatment. The analyzes were performed in Review Manager Software version 5.3. Of the 2724 potentially eligible studies, 17 met all inclusion criteria and presented an medium risk of bias. In the global analysis and by subgroups, it was found that there is statistical difference (p ≤ 0.05) favoring the experimental groups. The I² test values were greater than 90% representing the high heterogeneity among the studies. The pre-sintered specimens submitted to sand blasting had higher surface roughness compared to sand blasting after the sintering process. This modification made it possible to avoid the transformation of the tetragonal phase into the monoclinic phase. The results indicated that the Nd: YAG and CO2 laser formed superficial microcracks. The Erbium laser used with lower energy intensity is presented as a promising method for surface treatment of zirconia-
Descrição: dc.description52f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectZircônia-
Palavras-chave: dc.subjectJateamento-
Palavras-chave: dc.subjectÓxido de alumínio-
Palavras-chave: dc.subjectLaser-
Palavras-chave: dc.subjectTratamento de superfície-
Palavras-chave: dc.subjectRugosidade-
Palavras-chave: dc.subjectZircônio-
Palavras-chave: dc.subjectRugosidade (Superfície)-
Palavras-chave: dc.subjectÓxido de alumínio-
Palavras-chave: dc.subjectLaser-
Palavras-chave: dc.subjectZirconia-
Palavras-chave: dc.subjectSandblast-
Palavras-chave: dc.subjectAluminum oxide-
Palavras-chave: dc.subjectLaser-
Palavras-chave: dc.subjectSurface treatment-
Palavras-chave: dc.subjectRoughness-
Título: dc.titleAvaliação da rugosidade na superfície da zircônia, produzida com o jateamento de óxido de alumínio e com os lasers Erbium-YAG, Neodymium-Doped-YAG e CO2: uma revisão sistemática com meta-análise-
Título: dc.titleEvaluation of the roughness on the zirconia surface produced with the aluminum oxide sand blasting and the Erbium-YAG, Neodymium-Doped-YAG or CO2 lasers: a systematic review and meta-analysis-