Autor(es): dc.creator | MacDonogh, Kieran Matthew Ferreira | - |
Data de aceite: dc.date.accessioned | 2024-07-11T18:12:16Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T18:12:16Z | - |
Data de envio: dc.date.issued | 2022-02-16 | - |
Data de envio: dc.date.issued | 2022-02-16 | - |
Data de envio: dc.date.issued | 2021 | - |
Fonte completa do material: dc.identifier | http://app.uff.br/riuff/handle/1/24573 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/765696 | - |
Descrição: dc.description | A retificação é um dos últimos processos de usinagem aplicado na fabricação de componentes mecânicos. Este processo consiste na retirada de material por meio de abrasão entre os grãos abrasivos e o material usinado, sendo capaz de produzir um excelente acabamento superficial. Para o controle da retificação é necessário que a escolha do rebolo seja adequada as características do material a ser retificado. Os aços do tipo maraging são utilizados em diversas indústrias devido a suas características de alta resistência e tenacidade. Embora possua boa usinabilidade quando solubilizado, a literatura é bastante escassa no estudo de retificação desse tipo de aço com rebolos convencionais. Esse trabalho tem como objetivo analisar a influência da retificação plana no acabamento superficial do aço maraging 300 utilizando um rebolo de Al2O3 solgel. As amostras de aço maraging foram submetidas a iferentes velocidades de avanço de retificação. Nas amostras foram avaliados o ruído magnético Barkhausen (RMB), a dureza Vickers e os parâmetros de rugosidade. Os resultados mostram que o óxido de alumínio consegue resultados comparáveis ao SiC em aços maraging de dureza semelhante, obtendo o melhor acabamento superficial na velocidade de avanço mais baixa testada. O RMB foi inversamente proporcional à rugosidade e proporcional às medições de dureza. Os resultados de RMB não apresentaram mudança significativa com a variação da velocidade de avanço indicando que não houve alteração significativa das tensões residuais das amostras. | - |
Descrição: dc.description | Grinding is one the last machining process applied to the manufacture of mechanical components. This process consists of the material removal through abrasion of the workpiece and the abrasive grains and it’s capable of producing an excellent surface finish. For the grinding control it’s necessary that the selection of the grinding wheel matches the grinded material. The maraging steels are used in various industries due to their high strength and toughness. Despite having good machinability in its solution-treated state, studies of grinding this type of steel with conventional grinding wheels are scarce. The present work aims to analyse the influence of the peripheral surface grinding on the surface finish of the maraging 300 steel using an Al2O3 sol-gel grinding wheel. The maraging steel samples were submitted to different workspeeds. For each sample the magnetic Barkhausen noise (MBN), Vickers hardness and roughness parameters were evaluated. The results showed that the Al2O3 can produce comparable results to the SiC on maraging steels of similar hardness, achieving the best surface finish at the lowest workspeed tested. The MBN was inversely proportional to the roughness and proportional to the hardness measurements. The MBN did not present significant change with the workspeed variation; this indicates that there wasn’t significant change to the residual stresses of the samples. | - |
Formato: dc.format | application/pdf | - |
Idioma: dc.language | pt_BR | - |
Publicador: dc.publisher | Universidade Federal Fluminense | - |
Publicador: dc.publisher | Niterói | - |
Direitos: dc.rights | Open Access | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | Maraging 300 | - |
Palavras-chave: dc.subject | retificação plana | - |
Palavras-chave: dc.subject | óxido de alumínio sol-gel | - |
Palavras-chave: dc.subject | ruído magnético Barkhausen | - |
Palavras-chave: dc.subject | rugosidade superficial | - |
Palavras-chave: dc.subject | Retificação | - |
Palavras-chave: dc.subject | Ferramenta de corte | - |
Palavras-chave: dc.subject | Aço de alta resistência | - |
Palavras-chave: dc.subject | Rugosidade (Superfície) | - |
Palavras-chave: dc.subject | Maraging 300 | - |
Palavras-chave: dc.subject | surface grinding | - |
Palavras-chave: dc.subject | aluminium oxide sol-gel | - |
Palavras-chave: dc.subject | magnetic Barkhausen noise | - |
Palavras-chave: dc.subject | surface roughness | - |
Título: dc.title | Influência da velocidade de avanço na retificação plana tangencial do aço maraging 300 com rebolo de alumina sol-gel | - |
Tipo de arquivo: dc.type | Trabalho de conclusão de curso | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: