Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Lins, Jefferson Fabrício Cardoso | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/7528952471956006 | - |
Autor(es): dc.contributor | Silva, Fabiane Roberta Freitas da | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/1166347988791004 | - |
Autor(es): dc.contributor | Magnago, Roberto de Oliveira | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/1905410995938951 | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/7821941090269806 | - |
Autor(es): dc.creator | Lima, Virgínia Cruz Rangel Albuquerque e | - |
Data de aceite: dc.date.accessioned | 2024-07-11T18:12:02Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T18:12:02Z | - |
Data de envio: dc.date.issued | 2022-11-16 | - |
Data de envio: dc.date.issued | 2022-11-16 | - |
Fonte completa do material: dc.identifier | http://app.uff.br/riuff/handle/1/26970 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/765617 | - |
Descrição: dc.description | Os objetivos principais deste trabalho foram o estudo da cinética de recristalização e a evolução da textura cristalográfica de um ferro puro laminado a frio até uma redução de 80% da área transversal da chapa. Após a deformação plástica, o material foi recozido à temperatura 550ºC por tempos três, sete, treze, dezesseis e trinta minutos, determinando, deste modo, o comportamento do material durante o recozimento. Com o auxílio da técnica de microscopia óptica (MO) podese acompanhar a mudança no formato dos grãos e o aumento das regiões recristalizadas com o tempo de recozimento. Após 30 minutos de recozimento, observase que o material está quase totalmente recristalizado e que o tamanho de grão não é constante ao longo da microestrutura. Através da técnica de difração de elétrons retroespalhados (EBSD – Electron Backscattered Diffraction), as funções de distribuição de orientações cristalográficas (ODF Orientation Distribution Function) foram calculadas, obtendose que as orientações cristalográficas de maior intensidade para o material deformado são (𝟏̅𝟏𝟏) [𝟏̅𝟏̅𝟎], (𝟑̅𝟑𝟐) [𝟏̅𝟏̅𝟎], (𝟐̅𝟐𝟑) [𝟏̅𝟏̅𝟎], (𝟏̅𝟏𝟐) [𝟏̅𝟏̅𝟎], localizadas sobre a fibra 𝜶. Após 30 minutos de recozimento, observouse que as orientações de maior intensidade estão localizadas sobre a fibra 𝜸. Em relação à cinética de recristalização, os parâmetros 𝑿𝑽𝑬𝑿 e 𝑺𝑿𝑬𝑽 foram obtidos e concluiuse que tanto o modelo JMAK (de Johnson, Mehl, Avrami e Kolmogorov) quanto o modelo do método do caminho microestrutural (MPMMicrostructural Path Method) não se adequam aos dados obtidos nesse trabalho, pois possuem limitações para descrever a cinética de recristalização de situações reais. | - |
Descrição: dc.description | The main objectives of this work were the study of the kinetics of recrystallization and the evolution of the crystallographic texture of a pure cold rolled iron up to a reduction of 80% of the transversal area of the sheet. After the plastic deformation, the material was annealed at 550 ° C for times three, seven, thirteen, sixteen and thirty minutes, thereby determining the behavior of the material during annealing. With the aid of the optical microscopy (OM) technique, it is possible to follow the change in the shape of the grains and the increase of the recrystallized regions with the annealing time. After 30 minutes of annealing, the material is almost completely recrystallized and the grain size is not constant along the microstructure. Electron Backscattered Diffraction (EBSD), the functions of crystallographic orientation distribution (ODFOrientation Distribution Function) were calculated, obtaining that the crystallographic orientations of greater intensity for the deformed material are (1̅11) [1̅1̅0], (3̅32) [1̅1̅0], (2̅23) [1̅1̅0], (1̅12) [1̅1̅0], located on the αfiber. After 30 minutes of annealing, it was observed that the orientations of higher intensity are located on the γ fiber. In relation to the kinetics of recrystallization, the XVEX e SXEV parameters were obtained and it was concluded that both the JMAK model (from Johnson, Mehl, Avrami and Kolmogorov) and the model of the MPMMicrostructural Path Method do not fit to the data obtained in this work, because they have limitations to describe the kinetics of recrystallization of real situations. | - |
Descrição: dc.description | 128 p. | - |
Formato: dc.format | application/pdf | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Open Access | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | Ferro puro | - |
Palavras-chave: dc.subject | Recristalização | - |
Palavras-chave: dc.subject | Textura cristalográfica e cinética de recristalização. | - |
Palavras-chave: dc.subject | Cinética | - |
Palavras-chave: dc.subject | Recristalização (Metalurgia) | - |
Palavras-chave: dc.subject | Cristalografia | - |
Palavras-chave: dc.subject | Engenharia Metalúrgica | - |
Palavras-chave: dc.subject | Produção intelectual | - |
Palavras-chave: dc.subject | Pure iron | - |
Palavras-chave: dc.subject | Recrystallization | - |
Palavras-chave: dc.subject | Crystallographic texture and recrystallization kinetics | - |
Título: dc.title | Estudo da cinética de recristalização e da evolução da textura cristalográfica de um ferro puro | - |
Tipo de arquivo: dc.type | Dissertação | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: