Estudo dos aços supermartensíticos submetidos à diferentes tratamentos térmicos por meio da análise de difração de elétrons retroespalhados por varredura (EBSD)

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorPerez, Geronimo-
Autor(es): dc.contributorhttp://lattes.cnpq.br/3022724661554315-
Autor(es): dc.contributorMoraes Junior, José-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9794837921209596-
Autor(es): dc.contributorAlmeida, Brígida-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0556387605441792-
Autor(es): dc.contributorhttps://lattes.cnpq.br/5910347459046429-
Autor(es): dc.creatorMonteiro, João Pedro-
Data de aceite: dc.date.accessioned2024-07-11T18:09:30Z-
Data de disponibilização: dc.date.available2024-07-11T18:09:30Z-
Data de envio: dc.date.issued2023-08-02-
Data de envio: dc.date.issued2023-08-02-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/29734-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/764745-
Descrição: dc.descriptionOs aços inoxidáveis supermartensíticos (AISM) são aços que contém baixo teor de carbono, menor que 0,03% em sua matriz. Esse material está sendo bastante utilizado na fabricação de tubos de aço na indústria de óleo e gás devido a sua alta resistência a corrosão, e por ser uma opção financeiramente mais viável ao aço super duplex. A formação da estrutura martensítica está diretamente ligada a não formação de precipitados Carbeto de Cromo que ocorrem durante o tratamento térmico do aço. Os precipitados de Carbeto de Cromo são compostos inorgânicos que em condições padrõesse apresentam sólidos cinzentos, extremamente duros, onde nos aços supermartensíticos eles reduzem o teor de cromo efetivo na liga reduzindo a resistência a corrosão. Neste trabalho foi realizado experimentalmente uma análise de difração deelétrons retroespalhados (EBSD) em aços inoxidáveis supermartensíticos submetidos a diferentes tratamentos térmicos, com o objetivo de procurar precipitados de Carbonetos de Cromo e identificar austenita retidas na matriz martensítica. Pelas imagens obtidasda análise de EBSD não foi possível identificar o carbeto de cromo presente na matriz,uma vez que para isto era necessário inserir no sistema todos as estruturas deste, foi possível quantificar a austenita retida na matriz.-
Descrição: dc.descriptionSupermartensitic stainless steels (SMSS) are steels that contain low carbon content, lessthan 0.03%, in their matrix. This material has been extensively utilized in the manufacturing of steel pipes in the oil and gas industry due to its high corrosion resistance and being a financially more viable alternative to super duplex steel. The formation of the martensitic structure is directly linked to the absence of Chromium Carbide precipitates that occur during the heat treatment of the steel. Chromium Carbide precipitates are inorganic compounds that, under standard conditions, appear as solid grey materials with extreme hardness. In supermartensitic stainless steels, theseprecipitates reduce the effective chromium content in the alloy, thus diminishing the corrosion resistance. In this study, an experimental analysis of backscattered electron diffraction (EBSD) was performed on supermartensitic stainless steels subjected to different heat treatments, aiming to search for Chromium Carbide precipitates and identify retained austenite in the martensitic matrix. Based on the obtained EBSD images, it was not possible to identify the presence of chromium carbide within the matrix, as doing so required the incorporation of all its structures into the system. However, it was possible to quantify the retained austenite in the matrix.-
Descrição: dc.description55 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectAços Inoxidáveis Supermartensíticos-
Palavras-chave: dc.subjectCarbeto de Cromo-
Palavras-chave: dc.subjectResistência à Corrosão-
Palavras-chave: dc.subjectEBSD-
Palavras-chave: dc.subjectAço baixo carbono-
Palavras-chave: dc.subjectAço inoxidável-
Palavras-chave: dc.subjectAço de alta resistência-
Palavras-chave: dc.subjectSupermartensitic Stainless Steels-
Palavras-chave: dc.subjectHeat treatment-
Palavras-chave: dc.subjectCorrosion Resistance-
Palavras-chave: dc.subjectChromium Carbide-
Título: dc.titleEstudo dos aços supermartensíticos submetidos à diferentes tratamentos térmicos por meio da análise de difração de elétrons retroespalhados por varredura (EBSD)-