Abordagens de tratamentos de superfícies de vitrocerâmica: estabilidade de adesão e análise morfológica

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorNoronha Filho, Jaime Dutra-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1785530002642447-
Autor(es): dc.contributorRabello, Tiago Braga-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9942765523151478-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1440423563339492-
Autor(es): dc.creatorDelforge, Gabriella Edde-
Data de aceite: dc.date.accessioned2024-07-11T18:05:50Z-
Data de disponibilização: dc.date.available2024-07-11T18:05:50Z-
Data de envio: dc.date.issued2022-11-28-
Data de envio: dc.date.issued2022-11-28-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/27104-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/763445-
Descrição: dc.descriptionObjetivo: Avaliar diferentes tratamentos além de distintos métodos de tratamento da superfície de cerâmicas a base de dissilicato de lítio, após o condicionamento com ácido fluorídrico e a aplicação do silano, por meio de teste de resistência adesiva à microtração e análise microestrutural. Materiais e métodos: Para atender ao objetivo proposto foram elaborados 6 grupos experimentais de acordo com o tratamento de superfície de vitrocerâmicas: grupo HF-Sil (ácido fluorídrico + silano); grupo HF-P-Sil (ácido fluorídrico + ácido fosfórico + silano); grupo HF-U-Sil (ácido fluorídrico + cuba ultrassônica + silano); grupo HF-P-U-Sil (ácido fluorídrico + ácido fosfórico + cuba ultrassônica + silano); grupo MEP (Monobond Etch and Prime); grupo MEP-H (Monobond Etch and Prime + aquecimento). Para cada grupo foi analisada a energia de superfície, por meio de ensaio em goniômetro, e a penetração do cimento resinoso na superfície condicionada, por meio da análise da interface na microscopia eletrônica de varredura (MEV). O ensaio de microtração foi feito de forma imediata (24 h) e após envelhecimento por meio de ciclagens térmicas (5000 ciclos – 5°C e 55°C). Os padrões de falha foram analisados por microscopia Confocal após os ensaios de resistência de união. Os dados foram analisados estatisticamente por análise de variância e teste Fisher (α=0.05). Resultados: As micrografias observadas tanto para análise da superfície quanto para a penetração de cimento na interface adesiva sugeriram que os grupos MEP e MEP-H promoveram uma dissolução da matriz vítrea distinta e mais suave do que a observada nos outros grupos condicionados com HF, enquanto os métodos de limpeza pós HF parecem expor mais esse condicionamento, aumentando os valores de resistência de união (RU). Conclusão: Os grupos HF-P-U-Sil, HF-U-Sil obtiveram maiores valores de SE e RU imediatos, sendo o valor do MEP semelhante apenas ao avaliar a RU. Porém, após o envelhecimento através de ciclagens térmicas (TC) foi observado maior manutenção da estabilidade adesiva para o grupo HF-P-SIL e MEP-H e os resultados mais baixos foram obtidos para o grupo sem método de limpeza HF-SIL.-
Descrição: dc.descriptionThis study aimed at evaluating the use of different treatments besides different methods of cleaning on the surface of lithium disilicate glass ceramic, between the steps of the hydrofluoric acid conditioning and the silane application, through microtensile bond strength and microstructural analysis. In order to meet the proposed objective, 6 experimental groups were prepared according to surface treatment: HF-Sil group (hydrofluoric acid + silane), HF-P-Sil group (hydrofluoric acid + phosphoric acid + silane), HF-U-Sil group (hydrofluoric acid + ultrasonic bath + silane) HF-P-U-Sil group (hydrofluoric acid + phosphoric acid + ultrasonic bath + silane), MEP group (Monobond etch and Prime), MEP-H group (Monobond etch and Prime + heating). For each group the surface energy were analyzed by means of a goniometer test and the penetration of the resin cement in the conditioned surface by analysis of the interface in scanning electron microscopy (SEM). The microtensile bond test was made immediately (24 h) and after thermal cycles (5000 cycles - 5 ± 2 °C and 55 ± 2 °C). Failure patterns was analyzed by Confocal microscopy after bond strength tests. The data were statistically analyzed by analysis of variance and Fisher test (α = 0.05). Results: The micrographs observed for both surface analysis and cement penetration at the adhesive interface suggested that the MEP and MEP-H groups promoted a distinct and smooth dissolution of the vitreous matrix than that observed in the other groups conditioned with HF, while cleaning methods appear to more expose this conditioning and increase surface energy (SE) and consequently bond strength (RU) values. Conclusion: The HF-P-U-Sil, HF-U-Sil groups obtained higher values of SE and immediate RU, and the MEP value was similar only when evaluating RU. However, after aging (TC), greater maintenance of adhesive stability was observed for the HF- P-SIL and MEP-H groups and the lowest results were obtained for the group without HF-SIL cleaning method.-
Descrição: dc.description57 f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectVitrocerâmicas-
Palavras-chave: dc.subjectdissilicato de lítio-
Palavras-chave: dc.subjectadesão-
Palavras-chave: dc.subjecttratamento de superfície-
Palavras-chave: dc.subjectciclagem termomecânica-
Palavras-chave: dc.subjectDentística reparadora-
Palavras-chave: dc.subjectRestauração dentária-
Palavras-chave: dc.subjectCerâmica-
Palavras-chave: dc.subjectResistência à tração-
Palavras-chave: dc.subjectMicroscopia eletrônica-
Palavras-chave: dc.subjectVitroceramics-
Palavras-chave: dc.subjectlithium disilicate-
Palavras-chave: dc.subjectAdhesion-
Palavras-chave: dc.subjectsurface treatment-
Palavras-chave: dc.subjectthermomechanical cycling-
Título: dc.titleAbordagens de tratamentos de superfícies de vitrocerâmica: estabilidade de adesão e análise morfológica-
Título: dc.titleApproaches to glass ceramic surface treatment: adhesion stability and morphological.-
Tipo de arquivo: dc.typeDissertação-