Influência dos parâmetros de corte nas tensões residuais geradas na usinagem de aço inoxidável duplex 2205

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorFonseca, Maria da Penha Cindra-
Autor(es): dc.contributorPardal, Juan Manuel-
Autor(es): dc.contributorChuvas, Tatiane de Campos-
Autor(es): dc.contributorSilveira, Raphael José Elino da-
Autor(es): dc.creatorMagalhães, Henrique Pereira-
Data de aceite: dc.date.accessioned2024-07-11T17:55:19Z-
Data de disponibilização: dc.date.available2024-07-11T17:55:19Z-
Data de envio: dc.date.issued2017-09-19-
Data de envio: dc.date.issued2017-09-19-
Data de envio: dc.date.issued2017-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/4544-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/760131-
Descrição: dc.descriptionO estudo das tensões residuais é de suma importância para projetos de peças industriais. Estas tensões são geradas no material após qualquer processo de fabricação, e sua natureza (trativa ou compressiva) e magnitude são fatores de risco ou de segurança para estes componentes, como por exemplo, na vida em fadiga e na resistência à corrosão sob tensão. Por esta razão, diversas pesquisas e estudos são realizados para entender, prever e comparar tanto os valores quanto os efeitos das tensões residuais, na vida em serviço do componente. O presente trabalho tem como objetivo a análise das tensões residuais geradas no processo de usinagem por torneamento de acabamento em amostras de aço inoxidável duplex UNS 31803, com diferentes velocidades de corte. As tensões residuais foram analisadas por difração de raios-X, usando o método do sen2. A caracterização da integridade superficial do material foi feita com análises de microdureza Vickers e medidas de rugosidade (Ra), assim como a macrografia da superfície. Os resultados mostraram que o torneamento gerou tensões residuais trativas em ambas as direções analisadas-
Descrição: dc.descriptionThe study of residual stresses is of utmost importance to the project of industrial components. These stresses are generated after all manufacturing process, and its superficial values are factors of risk or security to these components, for example in the case of fatigue life and corrosion under stress. For this reason, several researches and studies are made to understand, predict and compare the values and effects of the residuals stresses. The objective of this work is to evaluate the residual stresses generated in the machining process of finish turning in duplex stainless steel UNS 31803 specimens, with different cutting speeds. The residuals stresses were evaluated by X-ray diffraction with sin² method. The surface integrity analysis of the machined surface was made through the evaluation of the surface roughness (Ra) and micro hardness Vickers, as well as the surface macrography. The results showed the residual stresses were always tensile in nature, in both directions analyzed-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectTensões residuais-
Palavras-chave: dc.subjectTorneamento-
Palavras-chave: dc.subjectAço inoxidável duplex UNS 31803-
Palavras-chave: dc.subjectDifração de raios-X-
Palavras-chave: dc.subjectTensão residual-
Palavras-chave: dc.subjectAço inoxidável-
Palavras-chave: dc.subjectDifração de raios X-
Palavras-chave: dc.subjectTorneamento-
Palavras-chave: dc.subjectResidual stresses-
Palavras-chave: dc.subjectTurning-
Palavras-chave: dc.subjectDuplex stainless steel UNS 31803-
Palavras-chave: dc.subjectX-ray diffraction-
Título: dc.titleInfluência dos parâmetros de corte nas tensões residuais geradas na usinagem de aço inoxidável duplex 2205-
Tipo de arquivo: dc.typeTrabalho de conclusão de curso-
Aparece nas coleções:Repositório Institucional da Universidade Federal Fluminense - RiUFF

Não existem arquivos associados a este item.