Efeito do tratamento térmico de solubilização na microestrutura e dureza da liga Co-Cr-Mo-W

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorLins, Jefferson Fabrício Cardoso-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7528952471956006-
Autor(es): dc.contributorFerreira, Alexandre Furtado-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8648089123168415-
Autor(es): dc.contributorHabibe, Alexandre Fernandes-
Autor(es): dc.contributorhttp://lattes.cnpq.br/5673713175312070-
Autor(es): dc.contributorhttp://lattes.cnpq.br/6388814218613054-
Autor(es): dc.creatorMendes, Priscila Sousa Nilo-
Data de aceite: dc.date.accessioned2024-07-11T17:52:40Z-
Data de disponibilização: dc.date.available2024-07-11T17:52:40Z-
Data de envio: dc.date.issued2022-11-10-
Data de envio: dc.date.issued2022-11-10-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26922-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/759307-
Descrição: dc.descriptionO presente trabalho teve como objetivo a caracterização microestrutural e mecânica da liga metálica a base de Co-Cr-Mo-W na condição bruta de fundição e após tratamento térmico de solubilização a 1200°C por 1h e 6h. Foram utilizadas as técnicas de microscopia óptica (MO), microscopia eletrônica de varredura (MEV), espectrometria por energia dispersiva (EDS), difração de raios X e ensaio de dureza Vickers. Com os resultados encontrados foi possível observar a formação de uma fase rica em cobalto de estrutura cristalina (CFC), sendo que o cobalto puro possui estrutura cristalina (HC), essa mudança na estrutura cristalina é devido a matriz que incorpora os átomos de cromo, molibdênio e tungstênio como uma solução sólida, com o acréscimo de Mo e W houve um aumento da distância interplanar. A microestrutura da liga na condição bruta de fundição foi caracterizada por uma matriz dendrítica Co-CFC com a presença de precipitados nas zonas interdendríticas e contornos de grão. Após tratamento térmico de solubilização a 1200°C por 1h e 6h tem-se a diminuição do caráter dendrítico. Com relação aos carbonetos M23C6 encontrados nas ligas tratadas foi observado simultaneamente uma diminuição no tamanho, esferoidização e transformação em carbonetos M6C. O tamanho e a quantidade de carbonetos diminuem com o aumento do tempo de solubilização, cerca de 40% e 33% para a liga TT-1h e TT-6h respectivamente. As amostras solubilizadas a 1200°C, durante o tempo de 1 hora e 6 horas e resfriadas em água em temperatura ambiente, apresentaram menores valores de dureza (312 HV e 304 HV respectivamente) quando comparadas aos valores no estado bruto de fundição (332 HV).-
Descrição: dc.descriptionCoordenação de Aperfeiçoamento de Pessoal de Nível Superior-
Descrição: dc.descriptionThe present work had as objective the microstructural and mechanical characterization of CoCr-Mo-W based metal alloy in as-cast condition after thermal treatment of solubilisation on 1200°C for 1h and 6h. Optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectrometry (EDS), X-ray diffraction and micro hardness Vickers test (HV) techniques have been used. With the results found, it was possible to observe the formation of a rich cobalt phase of fcc lattice structure, where pure cobalt has hc lattice structure, this change in structure is due to the matrix which absorb the chromium, molybdenum and tungsten as a solid solution, with the addition of Mo and W there has been an increase in the interplanar distance. The as-cast alloy microstructure was characterized by a dentritic Co-fcc with the presence of precipitates in interdentritics zones and grain boundaries. After thermal treatment of solubilisation on 1200°C for 1h and 6h, a decrease of the dentritic aspect occurred. In relation to M23C6 carbides found on the treated alloys, it has been observed a simultaneously size decrease, globularizing and transformation in M6C carbides. The size and quantity of carbides are reduced with the increase in solution time, around 40% and 33% for the TT-1h alloy and TT-6h respectively. The solubilized samples on 1200°C during the time of 1 hour and 6 hours and then cooled in room temperature, showed lower hardness values (312 HV and 304 HV respectively) when compared to the as-cast values (332 HV).-
Descrição: dc.description90 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectLigas Co-Cr-Mo-W-
Palavras-chave: dc.subjectCaracterização-
Palavras-chave: dc.subjectMicroestrutura-
Palavras-chave: dc.subjectCarbonetos-
Palavras-chave: dc.subjectTratamento térmico de solubilização-
Palavras-chave: dc.subjectCobalto-
Palavras-chave: dc.subjectCromo-
Palavras-chave: dc.subjectMolibdênio-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectProduçao intelectual-
Palavras-chave: dc.subjectCo-Cr-Mo-W alloys-
Palavras-chave: dc.subjectCharacterization-
Palavras-chave: dc.subjectMicrostructure-
Palavras-chave: dc.subjectCarbide-
Título: dc.titleEfeito do tratamento térmico de solubilização na microestrutura e dureza da liga Co-Cr-Mo-W-