Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Fonseca, Gláucio Soares da | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/9663765935778795 | - |
Autor(es): dc.contributor | Moreira, Luciano Pessanha | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/5673024226638200 | - |
Autor(es): dc.contributor | Delgado Júnior, Horácio Guimarães | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/0640487521165463 | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/4807409173984002 | - |
Autor(es): dc.creator | Bertuci, Paulo Junior Faria | - |
Data de aceite: dc.date.accessioned | 2024-07-11T17:50:33Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T17:50:33Z | - |
Data de envio: dc.date.issued | 2022-11-09 | - |
Data de envio: dc.date.issued | 2022-11-09 | - |
Fonte completa do material: dc.identifier | http://app.uff.br/riuff/handle/1/26912 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/758611 | - |
Descrição: dc.description | O aço inoxidável austenítico 304L, que foi estudado no presente trabalho, tem sido muito utilizado em aplicações na indústria química e equipamentos para vasos de pressão e indústria de petróleo. Quando deformado, esse material pode apresentar transformação induzida por plasticidade, o chamado efeito TRIP – Transformation Induced Plasticity, que corresponde a transformação de fase austenita (CFC) → martensita (CCC). O aço AISI 304L é considerado um aço TRIP de alta liga, e a transformação induzida pela deformação plástica incrementa significativamente suas características de resistência mecânica. Neste trabalho são avaliados os efeitos da formação de martensita-α’ nas propriedades mecânicas de um aço AISI 304L deformado por laminação em diferentes reduções e avaliada a redução de tamanho de grão após o recozimento para reversão da martensita-α’. Com a laminação, foi possível obter transformação quase completa da austenita em martensita-α’, elevando a dureza do material de 210 para 490 HV. Após os recozimentos para reversão, os melhores resultados obtidos, ou seja, os menores tamanhos de grão médios, foram com a temperatura de 750°C. A reversão nessa temperatura pelo tempo de 5 minutos de recozimento possibilitou a reversão completa, e obtevese o limite de escoamento de 720 MPa comparado a 320 MPa para a condição como recebido, e o limite de resistência foi de 860 MPa comparado a 712 MPa da amostra como recebida. Para as análises foram utilizadas as técnicas de difração de raios X, Microscopia Óptica, MEV (microscopia eletrônica de varredura), dilatometria e medidas de microdureza e ensaios de tração. | - |
Descrição: dc.description | The 304L Stainless Steel, that was studied in this work, has been very used in applications in chemical industry and equipments for pressure vessels and oil industry. When deformed, this material can transform by transformation induced plasticity called TRIP effect, from austenite to martensite austenite (FCC) → martensite (BCC). The 304L Stainless Steel is considered a high alloy TRIP Steel, and the Transformation induced by plastic deformation increases significantly the mechanical properties of 304L steel. In this work are assessed the effects of formation of α’-martensite in the mechanical properties of a 304L stainless steel deformed by rolling at different percentages, and reported the grain refinement after a heat treatment in order to revert the α’-martensite, as well the effect on the mechanical properties of the material. With rolling, it was possible to obtain almost complete transformation of austenite into α'martensite, increasing the hardness of the material from 210 to 490 HV. After annealing to reversion, the best results, that means, the lowest average grain size, were with a temperature of 750 °C. The reversion at this temperature by the time of 5 minutes of annealing allowed the complete reversion. The yield strength obtained was 720 MPa compared to 320 MPa and condition as received. The tensile strength was 860 MPa compared to 712 MPa for the sample as received. For the analysis will be used the following techniques: Xray diffraction, Optical Microscopy, Scanning Electronic Microscope (SEM), dilatometry, microhardness tests and tension test. | - |
Descrição: dc.description | 93 p. | - |
Formato: dc.format | application/pdf | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Open Access | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | Aço inoxidável austenítico 304L | - |
Palavras-chave: dc.subject | Efeito TRIP | - |
Palavras-chave: dc.subject | Transformação martensítica | - |
Palavras-chave: dc.subject | Reversão da martensita-α' | - |
Palavras-chave: dc.subject | Refino de grão | - |
Palavras-chave: dc.subject | Engenharia Metalúrgica | - |
Palavras-chave: dc.subject | Processamento e caracterização de materiais | - |
Palavras-chave: dc.subject | Aço inoxidável austenítico | - |
Palavras-chave: dc.subject | Transformação martensítica | - |
Palavras-chave: dc.subject | Deformação | - |
Palavras-chave: dc.subject | Produção intelectual | - |
Palavras-chave: dc.subject | 304L Austenitic stainless steel | - |
Palavras-chave: dc.subject | TRIP effect | - |
Palavras-chave: dc.subject | Martensitic transformation | - |
Palavras-chave: dc.subject | α’ martensite reversion | - |
Palavras-chave: dc.subject | Grain refinement | - |
Título: dc.title | Estudo do efeito da transformação martensítica induzida por deformação e da reversão sobre propriedades mecânicas do aço 304L | - |
Tipo de arquivo: dc.type | Dissertação | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: