Avaliação da superfície de instrumentos de níquel-titânio antes e após o uso por meio da perfilometria óptica tridimensional sem contato

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorScelza, Miriam Zaccaro-
Autor(es): dc.contributorhttp://lattes.cnpq.br/5221058665417202-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9170739787154187-
Autor(es): dc.creatorFerreira, Fabiano Guerra-
Data de aceite: dc.date.accessioned2024-07-11T17:48:45Z-
Data de disponibilização: dc.date.available2024-07-11T17:48:45Z-
Data de envio: dc.date.issued2020-03-23-
Data de envio: dc.date.issued2020-03-23-
Data de envio: dc.date.issued2016-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/13132-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/758009-
Descrição: dc.descriptionO propósito deste estudo foi avaliar e comparar, qualitativa e quantitativamente, e em escala nanométrica, as características da topografia da superfície de instrumentos de níquel-titânio (NiTi) antes e após o uso por meio da perfilometria óptica tridimensional sem contato. Verificou-se, ainda, a acuidade do método inovador empregado para as análises. Instrumentos reciprocantes de NiTi com calibre 25/.08 (n=5, Reciproc; n=5, WaveOne) foram submetidos a testes em canais radiculares simulados em blocos de resina transparente. Para a realização das análises, foi estabelecido um procedimento original para permitir a repetibilidade e reprodutibilidade precisas para a medição das mesmas áreas da lâmina de corte situadas a 3 mm da ponta dos instrumentos, antes e após os testes. Todas as análises foram realizadas em áreas de 210 x 210 µm por meio do software do equipamento. A avaliação quantitativa das superfícies foi realizada por meio da análise dos valores registrados pelos parâmetros de amplitude Sa, Sq e Sz. Os dados obtidos foram submetidos à análise estatística no nível de significância de 5%. Aumentos significativos de desgaste nas superfícies de ambos os grupos de instrumentos foram observados após o segundo teste. Imagens tridimensionais de alta resolução mostraram marcantes alterações na topografia da superfície da lâmina de corte dos instrumentos, antes e após o uso. Observou-se, ainda, a presença de irregularidades nas superfícies tais como como deformações, sulcos, fissuras, degraus e microcavidades, sendo mais predominantes nos instrumentos WaveOne. A perfilometria óptica demonstrou ser um método acurado para a análise qualitativa e quantitativa das mesmas superfícies antes e após o uso. A estabilidade e repetibilidade da técnica permite uma compreensão mais abrangente dos efeitos do desgaste na superfície dos instrumentos endodônticos.-
Descrição: dc.descriptionThe aim of this study was to, qualitatively and quantitatively, evaluate and compare, nanoscale features on the surface topography of nickel-titanium (NiTi) instruments before and after use by means of using non-contact three-dimensional optical profilometry, and to verify the accuracy of the innovative method used for the investigation. NiTi reciprocating instruments 25 / .08 (five Reciproc and five WaveOne ) were subjected to tests in simulated root canals in clear resin blocks. For the investigation, an original procedure was established to allow accurate repeatability and reproducibility for the measurement of similar areas of the cutting blade located 3 mm from the tip of the instruments before and after the tests. The analysis were performed in areas measuring 210 x 210 μm using the software of the equipment. The quantitative assessment of the surfaces was performed by the analysis of the amplitude parameters Sa, Sq and Sz. The data were submitted to statistical analysis at a significance level of 5%. Significant increases of wear on the surfaces of both groups of instruments were observed after the second test. High-resolution three-dimensional images showed clear alterations on the surface topography of the cutting blades of the instruments, before and after use. The presence of surface irregularities such as deformations, burrs, steps, cracks and microcavities were observed, being more predominant in the WaveOne instruments. Optical profilometry proved to be an accurate method for the qualitative and quantitative evaluation of similar surfaces before and after use. The stability and repeatability of the technique allows a more comprehensive understanding of the effects of surface wear on endodontic instruments.-
Descrição: dc.description45f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectEndodontia-
Palavras-chave: dc.subjectPreparo de canal radicular-
Palavras-chave: dc.subjectTeste de materiais-
Palavras-chave: dc.subjectEndodontia-
Palavras-chave: dc.subjectTeste de material-
Palavras-chave: dc.subjectPerfilometria optica-
Palavras-chave: dc.subjectPreparo do canal radicular-
Palavras-chave: dc.subjectEndodontics-
Palavras-chave: dc.subjectMaterials testing-
Palavras-chave: dc.subjectRoot canal preparation-
Título: dc.titleAvaliação da superfície de instrumentos de níquel-titânio antes e após o uso por meio da perfilometria óptica tridimensional sem contato-
Título: dc.titleEvaluation of the suface of nickel-titanium instruments before and after use by means of non-contact three-dimensional optical profilometry-