Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Lins, Jefferson Fabrício Cardoso | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/7528952471956006 | - |
Autor(es): dc.contributor | Souza, José Vitor Candido de | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/1237480074022693 | - |
Autor(es): dc.contributor | Ferreira, Flavio | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/8741029675242016 | - |
Autor(es): dc.contributor | Mulinari, Daniella Regina | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/6707823025115119 | - |
Autor(es): dc.contributor | Castro, José Adilson de | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/4613010410524009 | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/5673713175312070 | - |
Autor(es): dc.creator | Habibe, Alexandre Fernandes | - |
Data de aceite: dc.date.accessioned | 2024-07-11T17:48:34Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T17:48:34Z | - |
Data de envio: dc.date.issued | 2022-11-24 | - |
Data de envio: dc.date.issued | 2022-11-24 | - |
Fonte completa do material: dc.identifier | http://app.uff.br/riuff/handle/1/27077 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/757947 | - |
Descrição: dc.description | Este trabalho teve por objetivo o desenvolvimento de pós metálicos a base de uma liga contendo 65%Co, 23%Cr, 6%Mo e 6%W para aplicações em processos de prototipagem rápida por sinterização seletiva a laser para uso na odontologia. A liga foi fundida a partir de pós elementares e, em seguida, o lingote foi submetido à usinagem, gerando-se cavacos metálicos de característica frágil com tamanho inferior a 3mm. Os cavacos foram submetidos à moagem em moinho planetário, variando-se a relação de massa de pó/esferas e tempo de moagem. No estudo de moagem, relações de esfera/pó de 4:1, 6:1, 8:1 e 10:1 foram investigadas. Além disso, tempos de moagem variando de 15min a 120min foram avaliados. Partículas de morfologia e tamanhos variados foram obtidas e em função do aumento de tempo de moagem e da relação de esfera / pó, o tamanho médio sofreu significativas mudanças. Os resultados indicaram que a condição de moagem ideal p/ criação de partículas com boa receptividade (tamanho e formato) foram àquelas moídas em 60 ± 15 min. e com relação esfera / pó de 6:1. Este pó foi tratado termicamente a 1000°C por 120 min em atmosfera de argônio e em seguida, o pó foi desaglomerado. Os aspectos morfológicos encontrados se adaptam às exigências de processo e do equipamento de sinterização a laser. Os resultados indicam redução do tamanho do cristalito dos pós moídos, da ordem de 50% quando submetidos a moagem durante 120 minutos, utilizando relação esfera pó de 6:1. O processo permite a aglomeração semi-esferoidizada das partículas com redução de seu tamanho médio, porém a utilização de tratamento térmico apresentou tendência a esferoidização quando a 1000°C com patamar de 120 min. Com relação a pós comerciais avaliados obtidos por atomização, estes apresentam similaridade relativa às fases cristalinas presentes no cobalto metálico. A morfologia apresenta como dominante o formato esférico com variação de tamanho. A avaliação da sinterabilidade em maquina de sinterização a laser destes pós moído sem comparação a pós atomizados indicou que a densificação utilizando pós moídos gerou corpos com densidade relativa em torno de 93,2% ao passo que o uso de pó atomizado alcançou densidade relativa de 96,1%. Porém estas diferenças não foram significativas para geração de variações consideráveis na dureza e modulo de elasticidade dos corpos sinterizados, os quais apresentaram dureza da ordem de 364 e 340HV para uso do pó moído e atomizado, respectivamente. O módulo de elasticidade médio obtido foi de 210GPa para os dois materiais, e os resultados indicam que ambos os produtos sinterizados atendem a especificação das normas ASTM F75 e F1537, para ligas de Co-Cr para aplicações como biomateriais. | - |
Descrição: dc.description | Fundação Carlos Chagas Filho de Amparo à Pesquisa do Estado do Rio de Janeiro | - |
Descrição: dc.description | This work aimed at the development of metal powders based on an alloy containing 65%Co, 23% Cr, 6% Mo and6% W for applications in rapid prototyping processes for the selective laser sintering for use in dentistry. The alloy was cast from elemental powders and then the ingot was subjected to machining, thus generating metallic chips fragile characteristic size less than 3mm. The chips were subjected to grinding in a planetary mill, by varying the mass ratio of beads / powder and milling time. In the study milling, ball relationships / 4 powder: 1, 6: 1, 8: 1 and 10: 1 were investigated. Furthermore, milling times ranging from 15min 120min were evaluated. Particle morphology and varying sizes were obtained and due to the increase of milling time and ball ratio / powder, the average size has undergone significant changes.The results indicate reduction of the crystallite size of the powders ground, of the order of 50% when subjected to grinding for 120 minutes using ball powder ratio of 6: 1. The process allows the semi-spheroidized particle agglomeration with a reduction of their average size, but the use of heat treatment tended to spheroidizing as 1000 ° C with a 120 min level. Regarding the assessed commercial powders obtained by atomization, they present relative similarity to the crystalline phases present in the cobalt metal. The morphology shows how dominant the spherical shape with varying size. The evaluation of sinterability in laser sintering machine of these milled powders compared with atomized powder indicated that the milled powders produced using densification bodies with a relative density of about 93.2% while the use of atomized powder achieved a relative density of 96,1%. But these differences were not significant for generating considerable variation in hardness and elastic modulus of the sintered bodies, which showed hardness of 364 and 340HV order to use the ground powder and atomized, respectively. The obtained elastic modulus was 210GPa for the two materials, and the results indicate that both the sintered products meet the specification of ASTM F75 and F1537 requirements for Co-Cr alloys for applications as biomaterials. | - |
Descrição: dc.description | 160 p. | - |
Formato: dc.format | application/pdf | - |
Idioma: dc.language | pt_BR | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Open Access | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | Moagem de alta energia | - |
Palavras-chave: dc.subject | Sinterização a laser seletiva | - |
Palavras-chave: dc.subject | Matérias-primas | - |
Palavras-chave: dc.subject | Pós-nanoestruturados | - |
Palavras-chave: dc.subject | Ligas metálicas Co-Cr-Mo-W | - |
Palavras-chave: dc.subject | Carbono | - |
Palavras-chave: dc.subject | Cromo | - |
Palavras-chave: dc.subject | Molibdênio | - |
Palavras-chave: dc.subject | Tungstênio | - |
Palavras-chave: dc.subject | Engenharia Metalúrgica | - |
Palavras-chave: dc.subject | Produção intelectual | - |
Palavras-chave: dc.subject | High-energy milling | - |
Palavras-chave: dc.subject | Sintering selective laser | - |
Palavras-chave: dc.subject | Raw materials | - |
Palavras-chave: dc.subject | Postnanostructured | - |
Palavras-chave: dc.subject | Metal alloys Co-Cr-Mo-W | - |
Título: dc.title | Processamento aplicado à liga metálica biocompatível do sistema Co-Cr-Mo-W obtida por moagem de alta energia | - |
Tipo de arquivo: dc.type | Tese | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: