Comportamento das tensões residuais no tratamento térmico do aço AISI 4340

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorFonseca, Maria da Penha Cindra-
Autor(es): dc.contributorMartins, Tabatta Regina de Brito-
Autor(es): dc.contributorSouza, Marcel Freitas de-
Autor(es): dc.contributorPardal, Juan Manuel-
Autor(es): dc.creatorTorres, Caio Sérgius Maquito de Paiva-
Autor(es): dc.creatorSilva, Leticia Fernandes da-
Data de aceite: dc.date.accessioned2024-07-11T17:48:06Z-
Data de disponibilização: dc.date.available2024-07-11T17:48:06Z-
Data de envio: dc.date.issued2018-09-21-
Data de envio: dc.date.issued2018-09-21-
Data de envio: dc.date.issued2018-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/7617-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/757779-
Descrição: dc.descriptionOs tratamentos térmicos são indispensáveis na indústria, pois promovem melhorias nas propriedades mecânicas e microestruturais dos aços, sendo aplicáveis no produto final ou em etapas intermediárias do processo de fabricação. No presente trabalho, foi estudado o comportamento das tensões residuais e das propriedades mecânicas, tais como dureza e tenacidade ao impacto, do aço AISI 4340 quando temperado a 860°C em óleo, e revenido a diferentes temperaturas. As tensões residuais foram medidas por difração de raios-X, utilizando o método do sen^2 ψ e comparadas com a análise das propriedades magnéticas obtidas por ruído magnético Barkhausen. Após a têmpera, foram encontradas tensões residuais de natureza trativa em todas as amostras. O tratamento térmico de revenido provocou relaxação das tensões em todas as temperaturas estudadas, porém permanecendo trativas nas amostras revenidas a 350°C e 450°C, tornando-se compressivas somente no grupo revenido a 550°C. Com o aumento da temperatura de revenido, observou-se uma redução significativa na dureza do material, em oposição ao RMB e à tenacidade ao impacto, que apresentaram aumento proporcional ao aumento de temperatura de encharque de revenido-
Descrição: dc.descriptionHeat treatments are indispensable in the industry, as they promote improvements in the mechanical and microstructural properties of steels, being applicable to the final product or to intermediate stages of the manufacturing process. In the present work, the behavior of the residual stresses and the mechanical properties such as hardness and impact toughness of AISI 4340 steel when quenched at 860°C in oil and tempered at different temperatures were studied. The residual stresses were measured by X-ray diffraction using the sen^2 ψ method and compared with the magnetic properties analysis obtained from the Magnetic Barkhausen Noise. After quenching, residual stresses of tensile nature were found in all samples. The heat treatment of tempering caused stress relaxation at all temperatures studied, but remained tensile in the samples tempered at 350°C and 450°C, becoming compressive only in the group tempered at 550°C. With the increase of tempering temperature, a significant reduction in the hardness of the material was observed, as opposed to the MBN and the impact toughness, which increased proportionally to the increase of the tempering soaking temperature-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectAço AISI 4340-
Palavras-chave: dc.subjectTratamentos térmicos-
Palavras-chave: dc.subjectTensões residuais-
Palavras-chave: dc.subjectPropriedades mecânicas-
Palavras-chave: dc.subjectDifração de raios-X-
Palavras-chave: dc.subjectRuído magnético Barkhausen-
Palavras-chave: dc.subjectAço AISI-
Palavras-chave: dc.subjectTratamento térmico-
Palavras-chave: dc.subjectTensão residual-
Palavras-chave: dc.subjectDifração de raios X-
Palavras-chave: dc.subjectAISI 4340 steel-
Palavras-chave: dc.subjectHeat treatment-
Palavras-chave: dc.subjectMechanical properties-
Palavras-chave: dc.subjectResidual stresses-
Palavras-chave: dc.subjectX-ray diffraction-
Palavras-chave: dc.subjectMagnetic Barkhausen noise-
Título: dc.titleComportamento das tensões residuais no tratamento térmico do aço AISI 4340-
Tipo de arquivo: dc.typeTrabalho de conclusão de curso-