Autor(es): dc.creator | Frazão, Camila Oliveira Borges | - |
Data de aceite: dc.date.accessioned | 2024-07-11T17:45:58Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T17:45:58Z | - |
Data de envio: dc.date.issued | 2020-08-31 | - |
Data de envio: dc.date.issued | 2020-08-31 | - |
Data de envio: dc.date.issued | 2015 | - |
Fonte completa do material: dc.identifier | https://app.uff.br/riuff/handle/1/14816 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/757055 | - |
Descrição: dc.description | Os cimentos de ionômero de vidro (CIV) são materiais amplamente utilizados na prática odontológica, em função de suas propriedades anticariogênicas e adesivas. O objetivo do presente estudo foi avaliar in vitro, por meio de microscopia de força atômica (MFA), as alterações provocadas pelo desafio cariogênico na superfície de um CIV de alta viscosidade [Ketac Molar Easymix™ (KM)] e um CIV modificado por resina [Vitremer™ (VT)]. Para tal, foram confeccionados 15 corpos-de-prova com dimensões padronizadas (8,0mm de diâmetro e 2,0mm de espessura) de cada material que foram divididos em 03 grupos experimentais (n=5), definidos de acordo com o meio de armazenamento: Grupo AD (água destilada); Grupo B (BHI suplementado com 2% de sacarose e inóculo de cepas de S. mutans [ATCC 25175]) e Grupo S (BHI suplementado com 2% de sacarose sem inóculo). Depois de mantidos em imersão por 07 dias, e os respectivos meios trocados a cada 24h, a superfície de cada espécime foi avaliada em um microscópio de força atômica a partir do qual foram determinados os valores de rugosidade superficial média (Ra). Os dados obtidos foram submetidos à análise estatística com os testes de Kruskal-Wallis e Mann-Whitney (α=5%). De acordo com os resultados, para o KM, o maior valor de Ra foi registrados no grupo B (p<0.05). Para o VT, o grupo S apresentou o maior valor de Ra (p<0.05), enquanto os grupos DW e B não apresentaram diferença estatisticamente significante. Portanto, a formação de biofilme a partir de S. mutans na superfície de ambos os materiais resultou no aumento da Ra e em alterações na topografia dos espécimes. Para o CIV VitremetTM, o acúmulo de sacarose também apresentou uma influência significativa na Ra. | - |
Descrição: dc.description | Glass ionomer cements (GIC) are materials widely used in dental practice, due to their anticariogenic and adhesive properties. The aim of this study was to evaluate in vitro using an atomic force microscopy (AFM), the changes caused by cariogenic challenge on the surface of a high-viscosity GIC [Ketac Molar Easymix ™ (KM)] and resin modified GIC [Vitremer ™ (VT)] induced. For this, 15 specimens were prepared with standardized dimensions (8.0 mm in diameter and 2.0 mm thick) of each material, that were divided into 03 experimental groups (n = 5), determined in accordance with how it group was storaged: Group DW (distilled water); Group B (BHI supplemented with 2% sucrose and inoculum of strains of S. mutans [ATCC 25175]) and Group S (BHI supplemented with 2% sucrose without inoculum). After kept in immersion for 07 days, and their respective media changed every 24 hours, the surface of the each specimen was evaluated in an atomic force microscope (AFM) from which was determined the average values of surface roughness (Ra). Data were statistically analyzed with the Kruskal-Wallis and Mann-Whitney test (α = 5%). According to the results, for the KM, the largest value of Ra was recorded in group B (p <0.05). For the VT, group S had highest value of Ra (p<0.05), while groups DW and B showed no statistically significant difference. Therefore, the formation of biofilm from S. mutans on the surface of both materials resulted in the increase of Ra and changes in topography of the specimens. To the GIC VitremerTM, the sucrose accumulation also had a significant influence on Ra. | - |
Descrição: dc.description | 32f. | - |
Formato: dc.format | application/msword | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | openAccess | - |
Direitos: dc.rights | openAccess | - |
Direitos: dc.rights | http://creativecommons.org/licenses/by-nc-nd/3.0/br/ | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | Microscopia de força atômica | - |
Palavras-chave: dc.subject | Cimentos de ionômero de vidro | - |
Palavras-chave: dc.subject | Rugosidade da superfície | - |
Palavras-chave: dc.subject | Cimento ionômero de vidro | - |
Palavras-chave: dc.subject | Rugosidade (Superfície) | - |
Palavras-chave: dc.subject | Atomic force microscopy | - |
Palavras-chave: dc.subject | Glass ionomer cements | - |
Palavras-chave: dc.subject | Surface roughness | - |
Título: dc.title | Análise no MFA da rugosidade e topografia superficial de dois cimentos de ionômero de vidro submetidos ao desafio cariogênico: estudo in vitro | - |
Título: dc.title | MFA analysis of roughness and surface topography of two glass ionomer cements submitted to cariogenic challenge: in vitro study | - |
Tipo de arquivo: dc.type | Dissertação | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: