Efeito da deformação plástica na formação de maclas de recozimento em uma superliga inconel 718

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorLins, Jefferson Fabrício Cardoso-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7528952471956006-
Autor(es): dc.contributorNogueira, Tania Maria Cavalcanti-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1309300835320812-
Autor(es): dc.contributorRodrigues, Geovani-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9578900283345548-
Autor(es): dc.contributorhttp://lattes.cnpq.br/3997482105545958-
Autor(es): dc.creatorFerreira, André Diniz Clotildes-
Data de aceite: dc.date.accessioned2024-07-11T17:42:15Z-
Data de disponibilização: dc.date.available2024-07-11T17:42:15Z-
Data de envio: dc.date.issued2022-11-07-
Data de envio: dc.date.issued2022-11-07-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26861-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/755749-
Descrição: dc.descriptionA superliga de níquel Inconel 718 é uma liga que apresenta elevada resistência mecânica a temperaturas extremas e resistência à corrosão. Essa liga é endurecível por precipitação, com a formação das fases ' e ''. O material de partida do proposto trabalho é proveniente de uma superliga Inconel 718 a partir de corpos-de-prova com comprimento útil de 85 mm e espessura de 0,37 mm. As amostras foram submetidas ao ensaio de tração com ruptura. Os corpos-de-prova foram deformados a 5%, 25% e 35% através de um ensaio de tração sem ruptura e recozidos a 700, 750, 900 e 1000°C por 30 minutos. A caracterização microestrutural foi avaliada através da microscopia eletrônica de varredura (MEV). Ensaios de dureza Vickers foram realizados para avaliar o comportamento mecânico do material. A microtextura e a macrotextura serão observadas por meio da técnica de difração de elétrons retroespalhados (EBSD). Para os corpos-de-prova submetidos ao ensaio de tração com ruptura, foram observados grãos equiaxiais longe da ruptura e bandeamento próximo da ruptura. Foram analisados os dados do ensaio de tração e de dureza do material. Foram observadas maclas de recozimento após deformação proveniente do ensaio de tração sem ruptura e tratamento térmico. A interpretação dos resultados por medidas de EBSD foi realizada através de figuras de pólo direta e inversa, perfil de distribuição de diferenças de orientação, mapa qualidade de imagem e função distribuição de orientação. Amostras recozidas a 700°C e a 750°C apresentaram elevada dureza devido à precipitação das fases '' e ' e amostras recozidas a 900°C e a 1000°C apresentaram baixa dureza com a dissolução dessas fases. As maclas de recozimento foram geradas em grande quantidade.-
Descrição: dc.descriptionCoordenação de Aperfeiçoamento de Pessoal de Nível Superior-
Descrição: dc.descriptionThe Inconel 718 nickel superalloy is an alloy that shows high strength at extreme temperatures and corrosion resistance. This alloy is precipitation hardenable, through the ' and '' phases. The starting material of the proposed work is an Inconel 718 superalloy derived from tension specimens with useful length of 85 mm and thickness of 0,37 mm. The specimens were subjected to tension tests with rupture. The test specimens were deformed at 5%, 25% and 35% through tension test without rupture and annealed at 700, 750, 900 and 1000°C for 30 minutes. The microstructural characterization was analysed through the Scanning Electron Microscopy (SEM). Vickers hardness test was performed to analyse the mechanical behavior of the material. The microtexture and macrotexture will be observed through the technique of Electron Backscattered Diffraction (EBSD). For the test specimens subjected to tension test with rupture, equiaxial grains were observed far from rupture and banding near the rupture. Hardness data of the material was analysed. Annealing twins were observed after deformation derived from tension test without rupture and heat treatment. The interpretation of results by EBSD measurements were performed through the direct and inverse pole figures, distribution profile differences of orientation maps, image quality and orientation distribution functions. Samples annealed at 700°C and 750°C showed high hardness due to precipitation of phases '' and ' and samples annealed at 900°C and 1000°C showed low hardness due to the dissolution of these phases. Annealing twins were generated in great quantity.-
Descrição: dc.description43 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectInconel 718-
Palavras-chave: dc.subjectMaclas de recozimento-
Palavras-chave: dc.subjectCaracterização microestrutural-
Palavras-chave: dc.subjectTextura cristalográfica-
Palavras-chave: dc.subjectDeformação plástica-
Palavras-chave: dc.subjectRecozimento (Metalurgia)-
Palavras-chave: dc.subjectLiga (Metalurgia)-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectProdução intelectual-
Palavras-chave: dc.subjectInconel 718-
Palavras-chave: dc.subjectAnnealing twin-
Palavras-chave: dc.subjectMicrostructural characterization-
Palavras-chave: dc.subjectCrystallographic texture-
Título: dc.titleEfeito da deformação plástica na formação de maclas de recozimento em uma superliga inconel 718-
Tipo de arquivo: dc.typeDissertação-
Aparece nas coleções:Repositório Institucional da Universidade Federal Fluminense - RiUFF

Não existem arquivos associados a este item.