Efeito remineralizante de sistemas adesivos experimentais com silicatos

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorSantos, Glauco Botelho dos-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8657236311638191-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4279178900289101-
Autor(es): dc.creatorFernandes, Laís Rocha-
Data de aceite: dc.date.accessioned2024-07-11T17:42:10Z-
Data de disponibilização: dc.date.available2024-07-11T17:42:10Z-
Data de envio: dc.date.issued2021-10-27-
Data de envio: dc.date.issued2021-10-27-
Data de envio: dc.date.issued2020-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/23590-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/755716-
Descrição: dc.descriptionO objetivo desse estudo foi verificar se a adição de partículas de silicatos de alumínio (SA), cálcio (SC), magnésio (SM) e sódio (SS), ao primer de um sistema adesivo autocondicionante experimental, remineraliza a dentina e não afeta as propriedades mecânicas. Foram produzidos 4 sistemas adesivos experimentais (AE) em diferentes concentrações: controle 0% (AE0), 10% (AE10), 20% (AE20) e 30% (AE30). Para responder o objetivo proposto, foram realizados testes iniciais que consistiram na determinação do tamanho das partículas, pH e grau de conversão (GC) dos AE. Em seguida, foram analisadas a resistência coesiva (n=5), com espécimes em forma de ampulheta, e a resistência de união (μTBS) à dentina (n=6), com palitos, ambas submetidas à microtração. Para μTBS foram utilizados 48 molares, sendo metade utilizada após 24h e a outra após 9 meses. Imagens de padrão de ruptura dos espécimes armazenados por 24h foram obtidas no Microscópio Eletrônico de Varredura (MEV). Esse também foi utilizado para as análises de distribuição das partículas e espectroscopia de raios x por energia dispersiva. O efeito remineralizante dos sistemas adesivos foi testado utilizando 12 dentes (n=3), em que discos de dentina hibridizados e unidos a discos dos AE foram imersos por 90 dias em saliva artificial. Em seguida, as amostras foram imersas em corante alaranjado de xilenol por 24h e analisadas em Microscopia Confocal de Varredura a Laser (CLSM). Os resultados mostraram que as partículas tinham dimensão de 3 μm (SA) a 18 μm (SM). O GC teve variação de 86% (AE30) a 92% (AE10) (p = 0,0002). O valor de pH variou de 3,25 (AE0) a 6,18 (AE20). Para resistência coesiva (p = 0,0046) o valor mais alto observado foi no AE30, igual estatisticamente ao grupo AE0. Foi encontrada diferença estatística (p=0,0004) para μTBS apenas na estocagem de 24h, sendo AE10 e AE30 os maiores valores. O padrão de ruptura foi adesiva nos AE0 e AE20 de 24h, enquanto nos demais foi mista. Nos AE de 9 meses, todos tiveram mais falhas adesivas, exceto o grupo AE0 que teve mais padrões de falha mista. Por fim, com o CLSM, foi possível observar que os AE promoveram deposição mineral terapêutica na dentina. Os demais testes indicaram que não houve alteração das propriedades mecânicas testadas. Diante disso, pode-se concluir que a inclusão de micropartículas à base de silicato na composição de um sistema adesivo autocondicionante pode promover durabilidade da resistência de união à dentina durante o período de estocagem e, sobretudo uma deposição mineral terapêutica na dentina. Houve estabilidade na, mantiveram as propriedades mecânicas testadas. Portanto, essas micropartículas podem representar componentes bioativos potenciais a serem incluídos durante a formulação de novos sistemas adesivos autocondicionantes.-
Descrição: dc.descriptionThe aim of this study was to verify whether the addition of aluminum silicate (AS), calcium (CS), magnesium (MS) and sodium (SS) particles to the primer of an experimental self-etching adhesive system remineralizes dentin and maintains its mechanical properties. Four experimental adhesive systems (EA) were produced in different concentrations: control 0% (EA0), 10% (EA10), 20% (EA20) and 30% (EA30). To address the proposed objective, initial tests were based on determining the particle size, pH and degree of conversion (DC) of the AE. Then, the cohesive strength (n=5), with hourglass-shaped specimens and the bond strength (μTBS) to dentin (n=6) with toothpicks specimens, both submitted to microtensile, were analyzed. For μTBS, 48 molars were used, half being used after 24 h and the other half after 9 months. Images of failure modes from the specimens stored for 24 h were obtained using a Scanning Electron Microscope (SEM). The SEM also used for particle distribution analysis and energy dispersive x-ray spectroscopy. The remineralizing effect of adhesive systems was tested using 12 teeth (n=3), in which hybridized dentin discs attached to EA discs were immersed for 90 days in artificial saliva. Then, the samples were immersed in xylenol orange dye for 24 hours and analyzed through Confocal Laser Scanning Microscopy (CLSM). The results showed particles size ranging from 3 μm (AS) to 18 μm (MS). The CG ranged from 86% (EA30) to 92% (EA10) (p = 0.0002). The pH values ranged from 3.25 (EA0) to 6.18 (EA20). For cohesive strength (p = 0.0046), the highest value observed was in the EA30, statistically equalto the EA0 group. A statistical difference was found (p=0.0004) for μTBS only in the 24-hour storage, with EA10 and EA30 presenting the highest values. The failure pattern was adhesive in the 24-hour EA0 and EA20, while the others presented a mixed pattern. For the 9-month EAs, all had more adhesive failures, except the EA0 group which had more mixed failure patterns. Finally, with CLSM, it was possible to conclude that EA promoted a therapeutic mineral deposition in dentin. The other tests indicated that there was no change in the mechanical properties tested. Therefore, it can be concluded that the inclusion of silicate-based microparticles in the composition of a self-etching adhesive system can promote durability of bond strength to dentin during the storage period and, above all, a therapeutic mineral deposition on dentin. There was stability in, maintained the mechanical properties tested. Therefore, these microparticles may represent potential bioactive components to be included during the formulation of new self-etching adhesive systems.-
Descrição: dc.description67f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Publicador: dc.publisherNiterói-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectinterface adesiva-
Palavras-chave: dc.subjectadesão-
Palavras-chave: dc.subjectdentina-
Palavras-chave: dc.subjectadesivo-
Palavras-chave: dc.subjectDentística reparadora-
Palavras-chave: dc.subjectDentina-
Palavras-chave: dc.subjectRemineralização dentária-
Palavras-chave: dc.subjectAdesivo dentinário-
Palavras-chave: dc.subjectSilicato-
Palavras-chave: dc.subjectSilicato de sódio-
Palavras-chave: dc.subjectadhesive interface-
Palavras-chave: dc.subjectadhesion-
Palavras-chave: dc.subjectdentin-
Palavras-chave: dc.subjectadhesive-
Título: dc.titleEfeito remineralizante de sistemas adesivos experimentais com silicatos-
Título: dc.titleRemineralizing effect of experimental adhesive systems with silicates-
Tipo de arquivo: dc.typeDissertação-
Aparece nas coleções:Repositório Institucional da Universidade Federal Fluminense - RiUFF

Não existem arquivos associados a este item.