Efeito do uso de um sistema adesivo experimental à base de análogos biomiméticos em dentina hígida e afetada por cárie

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorPortela, Maristela Barbosa-
Autor(es): dc.contributorLaiza, Poskus-
Autor(es): dc.contributorLourenço, Eduardo José Veras-
Autor(es): dc.contributorRossi, André-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7374992387363131-
Autor(es): dc.creatorGomes, Bianca Silva-
Data de aceite: dc.date.accessioned2024-07-11T17:41:47Z-
Data de disponibilização: dc.date.available2024-07-11T17:41:47Z-
Data de envio: dc.date.issued2020-04-24-
Data de envio: dc.date.issued2020-04-24-
Data de envio: dc.date.issued2018-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/13390-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/755586-
Descrição: dc.descriptionO objetivo deste trabalho foi avaliar a capacidade de regeneração da dentina hígida (DH) e afetada por cárie (DA) e a atividade proteolítica (AP) das proteases da matriz dentinária após o uso de um sistema adesivo experimental à base de dimetacrilato glicerol piromelítico e análogos biomiméticos. Valores de microdureza superficial (Knoop) foram utilizados para padronizar a desmineralização dos palitos de DH que ficaram expostos ou não a cultura com S.mutans para a produção de DA. O sistema adesivo de condicionamento total (com ácido fosfórico 37%) e de três passos (primer e adesivo experimental). Foram adicionados ao primer, como análogos biomiméticos, o ácido poliacrílico (5%) e o trimetafosfato de sódio (5%) e ao adesivo propriamente dito o monohidrato de fosfato monocálcico (9%), o fosfato beta tricálcico (10,5%) e o hidróxido de cálcio (0,5%), como carreadores de fosfato de cálcio. A microscopia eletrônica de transmissão (MET) foi utilizada para avaliar a nanoestrutura das amostras, em particular as interfaces adesivo-dentina e dentina desmineralizada e intacta. A composição química da dentina e do sistema adesivo foi mensurada usando a espectroscopia de energia dispersiva de raio-X e difração de elétrons de área selecionada (SAED). A AP da matriz dentinária foi mensurada através de um teste colorimétrico com Coomassie Blue G-250 tendo o BSA como substrato. As proteases dentinárias foram extraídas previamente de pós de DH e DA tratados e não-tratados com o sistema adesivo. Ambos os testes foram realizados em dois tempos: imediato e 3 meses. As análises de MET mostraram que não houve regeneração ou remineralização expressiva de dentina sobre o colágeno desmineralizado tanto em DH como em DA. Embora seja possível observar a presença de cristais fosfato de cálcio, não se pode afirmar que são cristais neoformados de hidroxiapatita. Os dados recolhidos na avaliação da AP foram levados a análise estatística. Não foi evidenciada inativação da AP. A AP foi semelhante entre DH e DA mesmo com o uso do adesivo bioativo. Mesmo após 3 meses da aplicação do sistema adesivo, a AP aumentou significativamente nos dois substratos de dentina-
Descrição: dc.descriptionThe aim of this study was to evaluate the regeneration capacity of sound dentin (SD) and caries-affected dentin (CAD) and the proteolytic activity (PA) of proteases in dentin matrix after using an experimental bonding system containing pyromellitic dianhydride glycerol dimethacrylate and biomimetic analogs. Values of superficial microhardness (Knoop) were used to standardize the demineralization on beams of SD exposed or not to Streptococcus mutans culture in order to produce CAD. The bonding system used was total-etch technique (using 37% phosphoric acid) and three steps (primer and experimental adhesive). The polyacrylic acid (5%) and sodium trimetaphosphate (5%) were added to the primer as biomimetic analogs, and to the adhesive were added monocalcium phosphate monohydrate (9%), beta-tricalcium phosphate (10.5%) and calcium hydroxide (0.5%) as calcium phosphate carriers. Transmission electron microscopy (TEM) was used to evaluate sample’s nanostructure, particularly the adhesive-dentin and the desmineralized-sound dentin interfaces. Chemical composition of both dentin and bond system was measured through EDX (Energydispersive X-ray spectroscopy) and SAED (Selected area electron diffraction). The PA in dentin matrix was measured with Coomassie Blue-G250 coloring test in which BSA was used as substrate. Dentin proteases were previously extracted from SD and CAD powders untreated or treated with the bond system. Both tests were conducted in two different times: up to 7 days and three months after treatment. TEM analysis showed no expressive remineralization of the demineralized collagen present either on SD or CAD and showed no evidences of dentin regeneration and PA inactivation. Although the presence of calcium phosphate crystals was observed, there is no proof that hydroxyapatite crystals were newly formed. The statistical analysis was applied to the PA analysis using the ANOVA test. PA analysis showed similar activity in SD and CAD, even after three months of treatment with the bonding system, when PA increased significantly-
Descrição: dc.description56f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectAdesivo-
Palavras-chave: dc.subjectBiomimético-
Palavras-chave: dc.subjectHidroxiapatita-
Palavras-chave: dc.subjectMaterial biocompatível-
Palavras-chave: dc.subjectAdesivo dentinário-
Palavras-chave: dc.subjectDentina-
Palavras-chave: dc.subjectHidroxiapatita-
Palavras-chave: dc.subjectCárie dentária-
Palavras-chave: dc.subjectAdhesive-
Palavras-chave: dc.subjectBiomimetics-
Palavras-chave: dc.subjectHydroxyapatite-
Título: dc.titleEfeito do uso de um sistema adesivo experimental à base de análogos biomiméticos em dentina hígida e afetada por cárie-
Título: dc.titleEffect of an experimental bonding system biomimetic analog-based on sound and caries-affected dentin-