Autor(es): dc.contributor | Castro, José Adilson de | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/4613010410524009 | - |
Autor(es): dc.contributor | Demarque, Rudineli | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/3808161204518595 | - |
Autor(es): dc.contributor | Fonseca, Gláucio Soares da | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/9663765935778795 | - |
Autor(es): dc.contributor | Delgado Júnior, Horácio Guimarães | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/0640487521165463 | - |
Autor(es): dc.contributor | Xavier, Carlos Roberto | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/3156647464982290 | - |
Autor(es): dc.creator | Silva, Rafaela dos Santos | - |
Data de aceite: dc.date.accessioned | 2024-07-11T17:41:43Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T17:41:43Z | - |
Data de envio: dc.date.issued | 2022-11-10 | - |
Data de envio: dc.date.issued | 2022-11-10 | - |
Fonte completa do material: dc.identifier | http://app.uff.br/riuff/handle/1/26930 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/755558 | - |
Descrição: dc.description | A soldagem de juntas dissimilares Inconel 718 x AISI 316L é um processo que vem sendo empregado em diferentes ramos industriais, principalmente em indústrias químicas e nucleares, sendo aplicável, por exemplo, em tubulações e varetas combustível. Devido à sua importância, no presente estudo foram analisadas juntas dissimilares de Inconel 718 e AISI 316L soldadas por meio processo TIG sob diferentes parâmetros, sendo verificada a presença da fase indesejável Laves. Foi feita análise microestrutural, por meio de microscopia óptica e microscopia eletrônica de varredura, de ambas as ligas na condição como recebida e na condição de junta dissimilar, sendo feita a medição do tamanho de grão e da dureza das amostras como recebidas, medição do espaçamento entre ferritas δ das amostras soldadas e análise da fração volumétrica de ferrita δ e de fase Laves presentes na zona fundida. Foi feita análise macroestrutural das juntas soldadas, sendo medida a largura, profundidade de penetração e área do metal de solda. As amostras soldadas também foram submetidas a ensaio de microdureza Vickers e análise EDS da fase Laves e das regiões da solda dissimilar. Além disso, foi realizado estudo da cinética de crescimento da fase Laves em duas das amostras soldadas, sendo feita comparação da fração volumétrica obtida experimentalmente com a fração volumétrica obtida por meio da equação de JMAK (Johnson-Mehl-Avrami-Kolmogorov). Os resultados mostraram que maiores aportes térmicos implicam em menores frações volumétricas de ferrita δ, maiores espaçamentos entre ferritas, maiores dimensões do metal de solda e menores valores de microdureza. A análise EDS mostrou que na junta dissimilar ocorre mistura da composição química de ambos os materiais. Quanto à análise da fase Laves, observou-se que a temperatura de interpasse possui maior influência na formação dessa fase do que o aporte térmico, sendo que a fração volumétrica de fase Laves é diretamente proporcional a ambos os parâmetros. A análise EDS da fase Laves confirmou que a fase formada se trata de um constituinte eutético formado por Laves e austenita interlamelar, como encontrado na literatura. No estudo da cinética de crescimento da fase Laves, observou-se que ocorreu um erro significativo entre a fração volumétrica de fase Laves obtida experimentalmente e a fração volumétrica obtida por meio da equação de JMAK. | - |
Descrição: dc.description | Coordenação de Aperfeiçoamento de Pessoal de Nível Superior. | - |
Descrição: dc.description | The welding of dissimilar joints Inconel 718 x AISI 316L is a process that has been used in different industrial branches, mainly in chemical and nuclear industries, being applicable, for example, in pipes and fuel rods. Due to their importance, in the present study dissimilar joints of Inconel 718 and AISI 316L were welded by TIG process under different parameters, being verified the presence of the undesirable Laves phase. Microstructural analysis was performed, using optical microscopy and scanning electron microscopy, of both alloys in the condition as received and in the condition of dissimilar joint, the grain size and the hardness of the samples as received was measured, as well as the spacing between δ ferrites of the welded samples, the δ ferrite volumetric fraction and Laves phase present in the fusion zone was analysed. Macro-structural analysis of the welded joints was performed, measuring the width, depth of penetration and area of the weld metal. The welded samples were also subjected to Vickers microhardness testing and EDS analysis of the Laves phase and the dissimilar weld regions. In addition, a study of the growth kinetics of the Laves phase in two of the welded samples, comparing the volumetric fraction obtained experimentally with the volumetric fraction obtained using the JMAK equation (Johnson-Mehl-Avrami-Kolmogorov). The results showed that higher heat inputs imply smaller volumetric fractions of δ ferrite, greater spacing between ferrites, larger dimensions of the weld metal and lower values of microhardness. The EDS analysis showed that in the dissimilar joint the chemical composition of both materials is mixed. Regarding the analysis of the Laves phase, it was observed that the interpass temperature has a greater influence on the formation of this phase than the thermal input, and the Laves phase volume fraction is directly proportional to both parameters. The EDS analysis of the Laves phase confirmed that the formed phase is an eutectic constituent formed by Laves and interlamellar austenite, as found in the literature. In the study of the growth kinetics of the Laves phase, it was observed that a significant error occurred between the Laves phase volumetric fraction obtained experimentally and the volumetric fraction obtained through the JMAK equation. | - |
Descrição: dc.description | 134 p. | - |
Formato: dc.format | application/pdf | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Open Access | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | AISI 316L | - |
Palavras-chave: dc.subject | Inconel 718 | - |
Palavras-chave: dc.subject | Fase laves | - |
Palavras-chave: dc.subject | Junta dissimilar | - |
Palavras-chave: dc.subject | Processo TIG | - |
Palavras-chave: dc.subject | Cinética de crescimento de fase | - |
Palavras-chave: dc.subject | Microestrutura | - |
Palavras-chave: dc.subject | Soldagem | - |
Palavras-chave: dc.subject | Juntas dissimulares | - |
Palavras-chave: dc.subject | Aço inoxidável austenítico | - |
Palavras-chave: dc.subject | Fase laves | - |
Palavras-chave: dc.subject | Processamento e caracterização de materiais | - |
Palavras-chave: dc.subject | Engenharia Metalúrgica | - |
Palavras-chave: dc.subject | Produção intelectual | - |
Palavras-chave: dc.subject | AISI 316l | - |
Palavras-chave: dc.subject | Inconel 718 | - |
Palavras-chave: dc.subject | Laves phase | - |
Palavras-chave: dc.subject | Dissimilar joint | - |
Palavras-chave: dc.subject | TIG process | - |
Palavras-chave: dc.subject | Phase growth kinetics | - |
Título: dc.title | Avaliação microestrutural com ênfase na formação da fase laves e ensaios de microdureza em juntas dissimilares de aço inoxidável austenítico AISI 316L e inconel 718 soldadas pelo processo tig autógeno | - |
Tipo de arquivo: dc.type | Dissertação | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: