Síntese e caracterização de compósitos restauradores remineralizantes com partículas nanoporosas de sílica-hidroxiapatita (Si-HAp) carregadas com NaF

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorSilva, Eduardo Moreira da-
Autor(es): dc.contributorNoronha Filho, Jaime Dutra-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8108314314986712-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0084980191573168-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1785530002642447-
Autor(es): dc.creatorReis, Dirciane Perpétuo-
Data de aceite: dc.date.accessioned2024-07-11T17:41:40Z-
Data de disponibilização: dc.date.available2024-07-11T17:41:40Z-
Data de envio: dc.date.issued2020-12-03-
Data de envio: dc.date.issued2020-12-03-
Data de envio: dc.date.issued2017-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/16211-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/755544-
Descrição: dc.descriptionO objetivo deste estudo foi a síntetizar e caracterizar compósitos restauradores remineralizantes com partículas nanoporosas de sílica-hidroxiapatita (Si-HAp) carregadas com fluoreto de sódio (NaF). A produção das partículas nanoporosas de Si-HAp foi feita através da sinterização de nanopartículas primárias de sílica e hidroxiapatita sintética à temperatura de 900°C. Foram produzidos quatro compósitos experimentais (SiLF, SiL, F e NT) com 40 %p/p de matriz orgânica (Bis- GMA/TEGDMA, 70/30 %p/p), 0,5 %p/p de canforoquinona, 1 %p/p de etil N,N- dimetil-4aminobenzoato (EDMAB) para atuarem como sistema de fotoiniciação e 60 %p/p de partículas nanoporosas de Si-HAp. Nos compósitos SiLF e F, as partículas foram previamente imersas durante 24 h em solução aquosa de NaF na concentração de 10% e secas durante 7 dias em estufa a 40 °C. A seguir, os compósitos SiLF e SiL tiveram as partículas silanizadas com γ-metacriloxipropil-1- trimetoxisilano. O compósito NT não recebeu tratamento prévio de suas partículas. O nanocompósito comercial Z350 (3M ESPE) foi utilizado como controle comercial. A análise do potencial remineralizante foi feita através da obteção das imagens no micro-CT e os perfis de densidade foram avaliados utilizando o software Dataviewer e imageJ. Para a caracterização do compósito foram feitos os seguintes ensaios: Grau de conversão (GC%), reistência à flexão (RF), módulo de elasticidade (ME), rugosidade, dureza, cor, translucidez, absorção e solubilidade. Os dados obtidos foram analisados com os modelos estatísticos adequados com nível de significância de (α = 0,05). O potencial remineralizador foi estatisticamente diferente para todos os grupos ( F > SiLF > NT > SiL). O NT apresentou o maior valor de GC% (63,84%). Para RF e ME, os grupos SiLF e F apresentaram menores valores que os grupos SiL e NT. Para a rugosidade, o grupo SiLF apresentou o maior valor (1,68 µm). Não houve diferença entre os grupos para a dureza e cor. Para a translucidez somente o NT foi diferente (0,54 TP). Para a absorção, o SiLF apresentou o maior valor (25,66 µg /mm 3 ). Em relação a solubilidade, todos os grupos foram diferentes entre si ( F > SiLF > SiL > NT ). Conclui-se que o tratamento com o NaF foi capaz de remineralizar a estrutura dentária e alterar as propriedades físico-químicas, ópticas, bem como os parâmetros de degradação hidrolítica dos compósitos.-
Descrição: dc.descriptionThe purpose of this study was to synthesize and characterize remineralizing restorative composites with sintering silica-hydroxyapatite (Si-HAp) nanoporous fillers loaded with sodium fluoride (NaF). It were produced four experimental composites (SiLF, SiL, F and NT). In SiLF and F composites, the particles were previously immersed for 24 h in 10% NaF aqueous solution, and maintained for 7 days in a dryer at 40°C. Afterwards, SiLF and SiL composites had their particles silanized with y-methacryloxypropyl-1-trimethoxysilane. The particles of NT composite were not treated. Z350 (3M ESPE) nanocomposite was used as a commercial reference for the enamel remineralization analysis. The remineralizing potential was evaluated by using micro-CT. The following properties were characterized: degree of conversion (DC%), flexural strength (FS), Young’s modulus (YM), roughness (R a ), hardness (KHN), color (ΔE), translucency (TP), water sorption (W sp ), and water solubility (W sl ). The remineralizing potential was statistically different for all groups (F > SiLF > NT > SiL). The NT showed the highest DC% (63,84%). SiLF and F showed lower FS and YM than SiL and NT. The highest roughness was presented by SiLF (1,68µm). No significant difference in R a and ΔE was found for all composites. NT presented the highest translucency (TP = 0,54). The highest W sp was presented by SiLF (25,66 µg / mm³). W sl was as follow: F > SiLF > SiL > NT). It was concluded that the treatment of Si- HAp particles with NaF improved the enamel remineralization.-
Descrição: dc.description52f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectCompósitos restauradores remineralizantes-
Palavras-chave: dc.subjectPartículas nanoporosas-
Palavras-chave: dc.subjectHidroxiapatita-
Palavras-chave: dc.subjectMateriais resposivos-
Palavras-chave: dc.subjectFluoreto-
Palavras-chave: dc.subjectHidroxiapatita-
Palavras-chave: dc.subjectFluoreto de sódio-
Palavras-chave: dc.subjectCompósito-
Palavras-chave: dc.subjectResin-based composites remineralizing-
Palavras-chave: dc.subjectNano-porous fillers-
Palavras-chave: dc.subjectHydroxyapatite-
Palavras-chave: dc.subjectResponsive materials-
Palavras-chave: dc.subjectFluoride-
Título: dc.titleSíntese e caracterização de compósitos restauradores remineralizantes com partículas nanoporosas de sílica-hidroxiapatita (Si-HAp) carregadas com NaF-
Título: dc.titleSynthesis and characterization of remineralizing restorative composites with silica-hydroxyapatite nanoporous fillers (Si-HAp) loaded with NaF-