Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Portela, Maristela Barbosa | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/0894755778517106 | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/7374992387363131 | - |
Autor(es): dc.creator | Santos, Juliane Cuciniello dos | - |
Data de aceite: dc.date.accessioned | 2024-07-11T17:41:36Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T17:41:36Z | - |
Data de envio: dc.date.issued | 2021-05-20 | - |
Data de envio: dc.date.issued | 2021-05-20 | - |
Data de envio: dc.date.issued | 2020 | - |
Fonte completa do material: dc.identifier | https://app.uff.br/riuff/handle/1/22145 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/755514 | - |
Descrição: dc.description | O objetivo do estudo foi caracterizar um adesivo experimental de três passos com análogos biomiméticos de proteínas não colagenosas da dentina (EXP AB) e verificar sua estabilidade adesiva em dentina afetada por cárie comparando com dentina hígida. Para a síntese do primer com análogos biomiméticos foi preparada uma mistura dos monômeros 2-hidroxietil metacrilato (HEMA) 40% p/p e dimetacrilato gliceril dianidrido piromelítico (PMGDM) 20% p/p; dos solventes etanol (35% p/p) e água (4% p/p); dos fotoiniciadores canforoquinona (0,5% p/p) e etil-4-dimetilaminobenzoato (EDMAB) 0,5% p/p; e dos análogos biomiméticos ácido poliacrílico (APA 5% p/p) e trimetafosfato de sódio (TMPS 5% p/p). O adesivo com análogos biomiméticos foi preparado com a mistura de bisfenol glicidil dimetacrilato (Bis-GMA) 70% p/p, HEMA (29% p/p), canforoquinona (0,5% p/p), EDMAB (0,5% p/p), acrescido de partículas de cálcio-fosfato (Ca/P – 20% p/p) que foram constituídas pela mistura de monohidratado de fosfato monocálcio (MFMC 9% p/p), fosfato beta-tricálcico (þTCP 10,5% p/p) e Ca(OH)2 (0,5% p/p). No adesivo experimental controle (EXP CT), não foram acrescidos os análogos biomiméticos e os carreadores de cálcio e fósforo no primer e no adesivo. O sistema adesivo Adper Scotchbond Multipurpose (SB) foi utilizado como controle comercial. Foram realizados testes de caracterização do sistema adesivo experimental, como grau de conversão, sorção e solubilidade. Além disso, foi avaliada a estabilidade adesiva através da resistência de união (microtração) após 24h e 12 meses de estocagem em saliva artificial. A partir de uma amostra de 60 dentes, os espécimes foram divididos de acordo com o sistema adesivo, tipo de substrato (dentina hígida e afetada por cárie) e tempo de estocagem (24 horas e 12 meses). Após condicionamento com ácido fosfórico e aplicação do sistema adesivo, os blocos de dentina foram restaurados com incrementos de resina composta e cortados em palitos. Não foi observada diferença no grau de conversão entre adesivo com os análogos biomiméticos e o experimental controle, apesar do mesmo ter apresentado maior solubilidade. Contudo, identificou-se um aumento significativo da resistência 10 de união do sistema adesivo EXP AB (28,41±4,27) em dentina afetada por cárie após 12 meses de estocagem comparado com os grupos EXP CT (20,29±1,47 MPa) e SB (20,11±2,96 MPa). A análise de falhas evidenciou a predominância de falhas mistas em todos os grupos. Conclui-se que a incorporação de análogos biomiméticos de proteínas não colagenosas ao sistema adesivo não interferiu no grau de conversão, apesar de ter aumentado a solubilidade. Quanto a estabilidade na interface adesiva, foi aumentada no grupo do substrato de dentina afetada por cárie após 12 meses de estocagem em saliva artificial e mantida nos demais grupos | - |
Descrição: dc.description | The study's objective was to characterize an experimental three-step adhesive with biomimetic analogs of non-collagenous dentin proteins (a-AB) and to verify its adhesive stability in dentine affected by caries compared to healthy dentin. For the synthesis of the primer with biomimetic analogs, a mixture of monomers 2-hydroxyethyl methacrylate (HEMA) 40% w / w and dimeracrylate glyceryl pyromelitic dianhydride (PMGDM) 20% w / w was prepared; the solvents ethanol (35% w / w) and water (4% w / w); the photoinitiators camphorquinone (0.5% w / w) and ethyl-4-dimethylaminobenzoate (EDMAB) 0.5% w / w; and the biomimetic analogs polyacrylic acid (APA) 5% w / w and sodium trimetaphosphate (TMPS) 5% w / w. The adhesive with biomimetic analogs was prepared with a mixture of bisphenol glycidyl dimethacrylate (Bis-GMA) 70% w / w, HEMA (29% w / w), camphorquinone (0.5% w /w), EDMAB (0.5 % w / w), plus calcium-phosphate particles (Ca / P - 20% w / w) that were constituted by the mixture of monocalcium phosphate monohydrate (MFMC - 45% mol), beta-tricalcium phosphate (þTCP - 45 mol%) and Ca (OH)2 (10 mol%). In the experimental control adhesive (EXP CT), biomimetic analogs and calcium and phosphorus carriers were not added to the primer and adhesive. The Adper Scotchbond Multipurpose (SB) adhesive system was used as a commercial control. The experimental adhesive system's characterization tests were performed, such as degree of conversion, sorption, and solubility. Also, adhesive stability was evaluated through bond strength (microtensile) after 24h and 12 months of storage in artificial saliva. From a sample of 60 teeth, the specimens were divided according to the adhesive system, type of substrate (healthy and caries-affected dentin), and storage time (24 hours and 12 months). After etching with phosphoric acid and applying the adhesive system, the dentin blocks were restored with composite resin increments and cut into toothpicks. There was no difference in the degree of conversion between adhesive with the biomimetic analogs and the experimental control, even though it showed superior solubility. However, a significant increase in bond strength of the EXP AB adhesive system (28.41 ± 4.27) was identified in dentine affected by caries after 12 months of storage compared to the EXP CT groups (20.29 ± 1.47 MPa ) and SB (20.11 ± 2.96 MPa). Failure analysis showed the predominance of mixed failures in all groups. It is concluded that the incorporation of biomimetic analogues of noncollagenous proteins to the adhesive system does not interfere in the degree of conversion and increases the bond strength in dentin affected by caries after 12 months of storage in artificial saliva | - |
Descrição: dc.description | 44f. | - |
Formato: dc.format | application/pdf | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Open Access | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | Adesivo | - |
Palavras-chave: dc.subject | Interface adesiva | - |
Palavras-chave: dc.subject | Dentina afetada | - |
Palavras-chave: dc.subject | Análogos biomiméticos | - |
Palavras-chave: dc.subject | Adesivo dentinário | - |
Palavras-chave: dc.subject | Resistência à tração | - |
Palavras-chave: dc.subject | Dentina | - |
Palavras-chave: dc.subject | Cárie dentária | - |
Palavras-chave: dc.subject | Adhesive | - |
Palavras-chave: dc.subject | Adhesive interface | - |
Palavras-chave: dc.subject | Affected dentin | - |
Palavras-chave: dc.subject | Biomimetic analogues | - |
Título: dc.title | Adesivo experimental com análogos biomimétricos pode influenciar na estabilidade da interface adesiva em dentina afetada por cárie? | - |
Tipo de arquivo: dc.type | Dissertação | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: