Atenção: Todas as denúncias são sigilosas e sua identidade será preservada.
Os campos nome e e-mail são de preenchimento opcional
Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Lins, Jefferson Fabrício Cardoso | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/7528952471956006 | - |
Autor(es): dc.contributor | Bertagnolli, Denise de Castro | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/6727744713310620 | - |
Autor(es): dc.contributor | Mulinari, Daniella Regina | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/6707823025115119 | - |
Autor(es): dc.contributor | Nogueira, Tânia Maria Cavalcanti | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/1309300835320812 | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/7421429616454089 | - |
Autor(es): dc.creator | Mesquita, Anna Paula Rollemberg | - |
Data de aceite: dc.date.accessioned | 2024-07-11T17:41:08Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T17:41:08Z | - |
Data de envio: dc.date.issued | 2022-11-16 | - |
Data de envio: dc.date.issued | 2022-11-16 | - |
Fonte completa do material: dc.identifier | http://app.uff.br/riuff/handle/1/26966 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/755360 | - |
Descrição: dc.description | Os aços duplex são ligas metálicas com uma microestrutura bifásica constituída de uma matriz ferrítica com ilhas de austenita. Essa microestrutura é estabilizada por elementos de liga, os quais em teores apropriados e submetidos a tratamentos térmicos em faixas de temperatura estáveis, vão conferir a esse material uma combinação de excelência em suas propriedades como, por exemplo, magnânimas resistência mecânica e resistência a corrosão. Assim, a manutenção da composição das fases dessa estrutura cristalina é essencial para continuidade dessas propriedades. Em contrapartida, a presença de diversos elementos de liga na constituição desses materiais, faz com que os mesmo tenham um perfil de precipitação extremamente complexo, o qual varia com a temperatura, afetando dessa forma os teores de elementos estabilizadores na microestrutura do material, afetando suas propriedades. Com isso, o intuito desse trabalho foi analisar a formação dessas fases intermetálicas, sob a ação de recozimento a 850 ºC, em três tempos distintos, 25 horas, 50 horas e 100 horas, avaliar o efeito de sua formação nos valores de dureza das amostras e em seguida realizar sua extração química utilizando o método de dissolução da matriz com reagente de Berzelius, cuja a metologia é pouco estudada e aplicada aos aços duplex, na qual, posteriormente o precipitado formado é filtrado à vácuo utilizando filtros quantitativos e membranas filtrantes de acetato de celulose, e em seguida caracteriza-se as fases intermetálicas por meio da técnica de difração de raios-x. A partir do ensaio de dureza começou-se a ter indícios da formação de fases intermetálicas, uma vez que essa propriedade tinha seus valores ascendente em relação ao tempo de recozimento. Em seguida, a extração química foi realizada obtendo-se êxito nas extrações dos precipitados e desse modo os mesmos foram retidos por filtração e então levados a análise de difração raios x. A partir desse fato, foram feitas comparações dos difratogramas obtido para as amostras com a literatura, sendo constatados presença de nitreto de cromo, em todos os tempos de exposição, e fase chi, a partir de 100 horas de recozimento, concluindo-se dessa forma um retardo na sua formação, o que pode ser associado ao baixo teor de molibdênio da amostra. | - |
Descrição: dc.description | Coordenação de Aperfeiçoamento de Pessoal de Nível Superior | - |
Descrição: dc.description | Duplex steels are metal alloys with a biphasic microstructure consisting of a ferritic matrix with austenite islands. This microstructure is stabilized by alloying elements which, at suitable temperatures and subjected to heat treatments in stable temperature ranges, will give this material a combination of excellence in its properties such as, for example, magnanimous mechanical resistance and corrosion resistance. Thus, the maintenance of the composition of the phases of this crystalline structure is essential for the continuity of these properties. On the other hand, the presence of several alloying elements in the formation of these materials causes them to have an extremely complex precipitation profile, which varies with the temperature, thus affecting the stabilizer element contents in the microstructure of the material, affecting its Properties. The purpose of this work was to analyze the formation of these intermetallic phases under annealing at 850 ºC, in three different times, 25 hours, 50 hours and 100 hours, to evaluate the effect of their formation on the hardness values of the samples. Then carry out its chemical extraction using the matrix dissolution method with Berzelius reagent, whose methodology is little studied and applied to the duplex steels, in which the precipitate formed is then vacuum filtered using quantitative filters and acetate filter membranes Of cellulose, and then the intermetallic phases are characterized by the X-ray diffraction technique. From the hardness test we began to have indications of the formation of intermetallic phases, since this property had its values ascending with respect to the time of annealing. Subsequently, the chemical extraction was performed with success in extractions of the precipitates and thereby they were retained by filtration and then taken to x-ray diffraction analysis. From this fact, we made comparisons of the diffractograms obtained for the samples with the literature, being verified the presence of chromium nitride in all exposure times, and chi phase, from 100 hours of annealing, concluding in this way A delay in its formation, which may be associated with the low molybdenum content of the sample. For the formation of nitrites, it was concluded that it is formed due to a significant content of manganese, which was responsible for the supersaturation of nitrogen in the matrix and the consequent formation of this intermetallic phase. | - |
Descrição: dc.description | 79 p. | - |
Formato: dc.format | application/pdf | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Open Access | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | Duplex UNS 32304 | - |
Palavras-chave: dc.subject | Extração | - |
Palavras-chave: dc.subject | Precipitado | - |
Palavras-chave: dc.subject | Recozimento | - |
Palavras-chave: dc.subject | Liga metálica | - |
Palavras-chave: dc.subject | Tratamento térmico | - |
Palavras-chave: dc.subject | Aço inoxidável duplex | - |
Palavras-chave: dc.subject | Engenharia Metalúrgica | - |
Palavras-chave: dc.subject | Produção intelectual | - |
Palavras-chave: dc.subject | UNS Duplex 32304 | - |
Palavras-chave: dc.subject | Extraction | - |
Palavras-chave: dc.subject | Precipitate | - |
Palavras-chave: dc.subject | Thermal annealing | - |
Título: dc.title | Caracterização de fases intermetálicas via difração de raios X no aço duplex UNS 32304 recozido | - |
Tipo de arquivo: dc.type | Dissertação | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: