Avaliação da técnica de dupla camada com soldagem GMAW em aço ASTM A36

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorLins, Jefferson Fabrício Cardoso-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7528952471956006-
Autor(es): dc.contributorFerreira, Alexandre Furtado-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8648089123168415-
Autor(es): dc.contributorXavier, Carlos Roberto-
Autor(es): dc.contributorhttp://lattes.cnpq.br/3156647464982290-
Autor(es): dc.creatorSilva, Felipe Ribeiro da-
Data de aceite: dc.date.accessioned2024-07-11T17:38:36Z-
Data de disponibilização: dc.date.available2024-07-11T17:38:36Z-
Data de envio: dc.date.issued2022-11-16-
Data de envio: dc.date.issued2022-11-16-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26976-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/754480-
Descrição: dc.descriptionO objetivo deste trabalho foi caracterizar o efeito da técnica de soldagem em dupla camada em um aço ASTM A36 a partir de chapas comerciais com arame ER110S­G utilizados na indústria de óleo e gás. Esta técnica de reparo de soldagem é aplicada para a recuperação das peças sem tratamento térmico posterior e sua metodologia se baseia na sobreposição de ciclos térmicos com o refino e revenimento da zona afetada pelo calor com grãos grosseiros da primeira camada pelo aporte térmico da segunda camada. Foram realizadas soldagem automatizada GMAW com energias de 1,6 KJ, 2,2 KJ e 3,1 KJ em peças de camada simples e camada dupla e utilizados microscopia ótica e microscopia eletrônica de varredura para avaliar o efeito na microestrutura que o aporte térmico da camada superior realizou sobre a camada inferior. Para caracterização mecânica foi utilizado o ensaio de dureza Vickers para avaliação das regiões do primeiro passe, segundo passe e ZTA. Os resultados concluíram que a soldagem em dupla camada mostrou­se uma boa opção para técnica de reparo de soldagem sem necessidade de tratamento térmico posterior por propiciar uma microestrutura mais homogênea na região de ZACGG e pela diminuição da dureza nestas regiões.-
Descrição: dc.descriptionThe objective of this work was to characterize the effect of double layer welding technique using ASTM A36 steel and ER110S­G wire used in the oil and gas industry. This welding technique repair is applied for recovery parts without subsequent heat treatment and its methodology is based on the overlapping of thermal cycles refining and tempering the zone affected by the heat with coarse grains of the first layer by the thermal input of the second layer. GMAW automated welding with 1.6 KJ, 2.2 KJ and 3.1 KJ energies were performed in single layer and double layer pieces and used optical microscopy and scanning electron microscopy to evaluate the effect on the microstructure that the thermal input of the the top layer held on the bottom layer. For mechanical characterization, the Vickers hardness test was used to evaluate the regions of the first pass, second pass and HAZ. The results concluded that double­layer welding proved to be a good option for welding repair technique without the subsequent heat treatment due to a greater refining of the grains in the grain regions and the reduction of hardness in these regions.-
Descrição: dc.description75 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectSoldagem GMAW automatizada-
Palavras-chave: dc.subjectDupla camada-
Palavras-chave: dc.subjectRevenimento-
Palavras-chave: dc.subjectTratamento térmico pós-­soldagem (TTPS)-
Palavras-chave: dc.subjectAço ASTM A36-
Palavras-chave: dc.subjectSoldagem-
Palavras-chave: dc.subjectProcesso GMAW-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectProdução intelectual-
Palavras-chave: dc.subjectGMAW weld-
Palavras-chave: dc.subjectDouble layer-
Palavras-chave: dc.subjectASTM A36-
Palavras-chave: dc.subjectMetallography-
Palavras-chave: dc.subjectPost weld heat treatment-
Título: dc.titleAvaliação da técnica de dupla camada com soldagem GMAW em aço ASTM A36-