Síntese e caracterização de compósitos restauradores remineralizantes com partículas de ionômero vidro-Ca pré-reagidas (PRG-Ca)

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorSilva, Eduardo Moreira da-
Autor(es): dc.contributorhttp://lattes.cnpq.br/3739830657171909-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0084980191573168-
Autor(es): dc.creatorMaia, Juliana Nunes da Silva Meirelles Doria-
Data de aceite: dc.date.accessioned2024-07-11T17:32:48Z-
Data de disponibilização: dc.date.available2024-07-11T17:32:48Z-
Data de envio: dc.date.issued2020-02-20-
Data de envio: dc.date.issued2020-02-20-
Data de envio: dc.date.issued2017-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/12936-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/752502-
Descrição: dc.descriptionEste estudo teve como objetivo sintetizar e caracterizar compósitos restauradores experimentais (CRE) com partículas de ionômero de vidro-cálcio pré-reagidas (PRGCa). As partículas de PRG-Ca foram preparadas a partir da síntese de um vidro de cálcio fluoraluminosilicato e sua reação com ácido poliácrilico. As partículas de PRGCa foram silanizadas e sete CRE foram produzidos: E0, E1, E2, E3, E4, E5 e E6. A matriz orgânica (40% p/p) foi composta de Bis-GMA / TEGDMA (70/30% p/p) e canforoquinona / etil N,N-dimetil-4aminobenzoato (0,5/1% p/p). O compósito base (E0) continha 60% p/p de partículas de bário-boro-silicato (BaBSi), sendo o grupo controle. Em E1, E2, E3, E4, E5 e E6, as partículas de BaBSi foram parcialmente substituídas por 10, 20, 30, 40, 50 e 60% p/p de partículas de PRG-Ca, respectivamente. O compósito restaurador Empress Direct (ED) foi a referência comercial utilizada. Para caracterização dos compósitos restauradores, as seguintes análises foram realizadas: potencial remineralizante (PR) através de microtomografia computadorizada, grau de conversão (GC%), rugosidade (Ra), dureza Knoop (DK), resistência à flexão (RF), módulo de flexão (MF), absorção (Ab), solubilidade (Sl), brilho (GU), translucidez (PT) e cor (ΔE). Os dados foram submetidos à Análise de variância de um fator e ao teste de Tukey HSD post-hoc (α = 0,05). Quanto à Ra, DK e GU, não houve diferença entre os CRE. O aumento da concentração das partículas de PRG-Ca diminuiu GC%, RF, MF e PT; e aumentou PR, Ab, Sl e ΔE. Na maioria das análises realizadas, ED apresentou comportamento intermediário aos CRE. E0 e ED não apresentaram PR. E4 apresentou o melhor desempenho geral. A incorporação de partículas de PRG-Ca em compósitos restauradores teve um efeito significativo no potencial remineralizante do esmalte, sem comprometer a maioria das propriedades, mostrando uma aplicação promissora como materiais bioativos em restaurações permanentes.-
Descrição: dc.descriptionThis study aimed to prepare and characterize experimental restorative composites (ERC) with calcium type pre-reacted glass-ionomer (PRG-Ca) fillers. The PRG-Ca fillers were prepared by the synthesis of a calcium fluoroaluminosilicate glass and its reaction with polyacrylic acid. The PRG-Ca fillers were silanized and seven ERC were produced: E0, E1, E2, E3, E4, E5 and E6. The organic matrix (40 wt%) was composed by Bis-GMA / TEGDMA (70/30 wt%) and camphorquinone / ethyl N,Ndimethyl-4-aminobenzoate (0.5/1 wt%). The base composite (E0 - control group) contained 60 wt% of barium borosilicate glass (BaBSi) fillers. In the experimental groups E1, E2, E3, E4, E5 and E6, the BaBSi fillers were partially replaced by 10, 20, 30, 40, 50 and 60 wt% of PRG-Ca fillers, respectively. The restorative composite IPS Empress Direct (ED) was used as a commercial reference. To characterize the restorative composites, the following analyses were performed: remineralizing potential (RP) using computerized microtomography, degree of conversion (DC%), roughness (Ra), Knoop hardness (KHN), flexural strength (FS), flexural modulus (FM), water sorption (Wsp), water solubility (Wsl), gloss (GU), translucency (TP) and color (ΔE). Data were submitted to one-way ANOVA and the Tukey’s HSD post hoc test (α = 0.05). Regarding Ra, KH and GU, there was no difference among the ERC. Increasing the concentration of PRG-Ca fillers increased RP, Wsp, Wsl and ΔE; and decreased DC%, FS, FM and TP. For the majority of the analyzed properties, ED presented an intermediate behavior compared to the ERC. E0 and ED did not present RP. E4 presented the best overall performance. The incorporation of PRGCa fillers into restorative composites had a significant effect on the remineralizing potential of enamel, without jeopardizing most properties, having a promising application as bioactive materials in permanent restorations.-
Descrição: dc.description56f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectResinas compostas-
Palavras-chave: dc.subjectPartículas de ionômero de vidro pré-reagidas-
Palavras-chave: dc.subjectRemineralização dentária-
Palavras-chave: dc.subjectMicro-TC-
Palavras-chave: dc.subjectPropiedades físicas e químicas-
Palavras-chave: dc.subjectResina composta-
Palavras-chave: dc.subjectCimento ionômero de vidro-
Palavras-chave: dc.subjectRemineralização dentária-
Palavras-chave: dc.subjectPropriedade física-
Palavras-chave: dc.subjectPropriedade química-
Palavras-chave: dc.subjectDiagnóstico por imagem-
Palavras-chave: dc.subjectResin composite-
Palavras-chave: dc.subjectPre-reacted glass-ionomer fillers-
Palavras-chave: dc.subjectRemineralization-
Palavras-chave: dc.subjectMicro-CT-
Palavras-chave: dc.subjectChemical and physical properties-
Título: dc.titleSíntese e caracterização de compósitos restauradores remineralizantes com partículas de ionômero vidro-Ca pré-reagidas (PRG-Ca)-
Título: dc.titlePreparation and characterization of experimental dental restorative composites with calcium type pre-reacted glass-ionomer (PRG-Ca) fillers [-