Avaliação do grau de conversão e da degradação de cimentos resinosos em soluções simuladoras do meio oral

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorSilva, Eduardo Moreira da-
Autor(es): dc.contributorhttp://lattes.cnpq.br/1785530002642447-
Autor(es): dc.contributorhttp://lattes.cnpq.br/0084980191573168-
Autor(es): dc.creatorNoronha Filho, Jaime Dutra-
Data de aceite: dc.date.accessioned2024-07-11T17:29:51Z-
Data de disponibilização: dc.date.available2024-07-11T17:29:51Z-
Data de envio: dc.date.issued2019-03-25-
Data de envio: dc.date.issued2019-03-25-
Data de envio: dc.date.issued2010-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/8899-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/751528-
Descrição: dc.descriptionO objetivo desta pesquisa foi avaliar a influência do ácido lático na degradação de quatro cimentos resinosos: Rely-X (RX) - 3M ESPE, Enforce (EN) - Dentsply, ALL CEM (AC) – FGM, Variolink II (VL) – Ivoclar/Vivadent. Água destilada e saliva artificial foram utilizados como controle. Foram utilizados dois métodos de ativação: química (Q) e dual (D). Na ativação dual, um disco de cerâmica com 2 mm de espessura (IPS EMPRESS) foi interposto entre o espécime e a ponta do fotoativador (650mW/cm2 / 40s). Na ativação química as pastas base e catalisadora foram misturadas conforme a orientação do fabricante. Para a análise do grau de conversão foram confeccionados espécimes ( = 6mm e h = 1mm) utilizando os métodos de ativação (Q) e (D). Os espécimes foram analisados através de espectroscopia FTIR-ATR para a determinação do grau de conversão. O subgrupo RX/D apresentou o maior valor de grau de conversão (48,0 % ± 0,7) e o subgrupo VL/Q apresentou o menor (13,6 % ± 5,0). Os espécimes ( = 6mm e h = 1mm) foram imersos e pesados diariamente durante os sete primeiros dias e, em seguida, durante 14, 21, 28, 90 e 180 dias a 37 ± 1°C, em água destilada (A, controle), saliva artificial (SA) e solução aquosa de ácido lático 0,02M – pH 4,0 (AL). Os dados obtidos foram submetidos à análise de variância e teste de Tukey (α = 0,05). O subgrupo que obteve o maior valor de absorção foi o VA /D /Dia 180/Ac = 10,31 ± 0,64 µg/mm3 e o subgrupo que apresentou o menor valor foi o RX / D / A/Dia 1 = 4,34 ± 0,56 µg/mm3. O subgrupo que apresentou o maior valor desolubilidade foi o VL / Q /Sa = 6,21 ± 0,37 µg/mm3, enquanto o subgrupo que apresentou o menor valor de absorção foi o RX / D / A =4,36 ± 0,56 µg/mm3. Concluiu-se que o ácido lático aumentou a degradação dos cimentos avaliados.-
Descrição: dc.descriptionThe aim of this study was to evaluate the influence of lactic acid on degradation of four resin-based cements used in restorative dentistry. Four resin cements were analyzed: Rely-X (RX) - 3M ESPE, Enforce (EN) - Dentsply, ALL, CEM (AC) - FGM, Variolink II (VL) - Ivoclar / Vivadent. Two activation methods were used: chemical (Q) and dual (D). In the dual activation, a ceramic disk with a thickness of 2 mm (IPS Empress) was interposed between the specimen and the tip of the curing unit (650mW/cm2 / 40s). The base and catalyst pastes were mixed according to the manufacturer's instructions in chemical activation. Additionally, the degradation resistance was evaluated trough storage in solutions that simulate the oral environment, which were distilled water, artificial saliva and lactic acid 0.2 M. Specimens ( = 6mm and h = 1 mm) were prepared in order to analyze the degree of conversion by FTIR-ATR spectroscopy. For degradation resistance tests, the specimens ( = 6mm h = 1 mm) were immersed daily for the first seven days and then for 14, 21, 28, 90 and 180 days at 37 ± 1 °C in the media: distilled water (A, control), artificial saliva (AS) and aqueous lactic acid solution 0.02 M - pH 4.0 (AL). The data were submitted to ANOVA and Tukey’s test (α = 0.05). The subgroup RX / D showed the highest degree of conversion of 48.0% ± 0.7, whereas the subgroup VL / Q had the lowest 13.6% ± 5.0. The highest solubility value was observed for VL / Q /Sa = 6,21 ± 0,37 µg/mm3, whereas the subgroup RX / D / A/Dia 1 = 4,34 ± 0,56 µg/mm3 showed the lowest ones. The subgroup which showed the highest absorption was the VA /D /D 180/Ac = 10,31 ± 0,64 µg/mm3, while the subgroup with the lowest value of absorption was the RX / D / A/Dia 1 = 4,34 ± 0,56 µg/mm3. It was concluded that lactic acid increase de degradation of the four resin-based cements evaluated.-
Descrição: dc.description86f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectDegradação-
Palavras-chave: dc.subjectCimentos resinosos-
Palavras-chave: dc.subjectÁcido lático-
Palavras-chave: dc.subjectCimento de resina-
Palavras-chave: dc.subjectÁcido láctico-
Palavras-chave: dc.subjectDegradação-
Palavras-chave: dc.subjectDegradation-
Palavras-chave: dc.subjectResin cements-
Palavras-chave: dc.subjectLactic acid-
Título: dc.titleAvaliação do grau de conversão e da degradação de cimentos resinosos em soluções simuladoras do meio oral-