Autor(es): dc.contributor | Lins, Jefferson Fabrício Cardoso | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/7528952471956006 | - |
Autor(es): dc.contributor | Siqueira, Rodrigo Pinto de | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/9567411447388614 | - |
Autor(es): dc.contributor | Gabriel, Sinara Borborema | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/9994985665512071 | - |
Autor(es): dc.contributor | http://lattes.cnpq.br/5592318592559129 | - |
Autor(es): dc.creator | Pereira, Rodrigo Esteves | - |
Data de aceite: dc.date.accessioned | 2024-07-11T17:27:58Z | - |
Data de disponibilização: dc.date.available | 2024-07-11T17:27:58Z | - |
Data de envio: dc.date.issued | 2022-11-09 | - |
Data de envio: dc.date.issued | 2022-11-09 | - |
Fonte completa do material: dc.identifier | http://app.uff.br/riuff/handle/1/26910 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/750860 | - |
Descrição: dc.description | Após processamento via prensagem em canal equiangular (da língua inglesa – Equal Channel Angular Pressing ECAP) em uma amostra de nióbio laminada a frio, buscouse no presente trabalho as caracterizações microestruturais das amostras processadas, analisando, por comparação, se o processamento via ECAP implicou em mudanças importantes em termos de homogeneização microestrutural e aumento de resistência mecânica. O material de partida utilizado se tratou de uma amostra de nióbio altamente pura, oligocristalina e que foi submetida à redução de 80% em área via laminação. Tal material foi cortado em dimensões de 9,0mm x 9,0mm x 50 mm e levado posteriormente à prensagem. A prensagem foi realizada em um único passe numa matriz com ângulo de interseção entre os canais de ɸ=90° e arco de curvatura Ψ=37°, o qual submeteu o material à deformação equivalente de ε≈1. Além disso, uma velocidade de processamento constante de 5 mm/min foi imposta. As caracterizações microestruturais foram restritas à região interna de um único grão, sendo as análises feitas nas seções longitudinal e transversal da amostra processada via ECAP e nas seções correspondentes do material laminado. Os resultados obtidos foram através de microscópio eletrônico de varreduraMEV, microscópio ópticoMO, medidas de microdureza (sendo cada seção 225 medidas) e mapa de distribuição de durezas. Na seção longitudinal, foi verificado que as estruturas de deformação foram distribuídas mais uniformemente e com regiões bandeadas orientadas preferencialmente de 45 a 60° em relação à direção de extrusão. Já na seção transversal, também ocorreu uma distribuição mais uniforme das estruturas de deformação, apresentando características de bandas se interceptando em várias direções. Quanto à resistência mecânica, ambas as seções apresentaram maior uniformidade na distribuição de durezas após passe de ECAP, mas sem aumento significativo no valor médio de dureza. O valor médio de dureza na seção longitudinal foi de 118 Vickers (inicialmente era de 112 Vickers) e na seção transversal o valor médio encontrado foi de 111 Vickers (inicialmente era 106 Vickers). A pesquisa constatou que a rota de processamento utilizada provocou homogeneização microestrutural e que não houve aumento significativo de dureza após passe ECAP devido ao processo de recuperação dinâmica. | - |
Descrição: dc.description | Coordenação de Aperfeiçoamento de Pessoal de Nível Superior | - |
Descrição: dc.description | Conselho Nacional de Desenvolvimento Científico e Tecnológico | - |
Descrição: dc.description | After processing by equiangular channel pressing (ECAP) in a coldrolled niobium sample, the microstructural characterizations of the processed samples were analyzed by comparing if the Processing via ECAP implied important changes in terms of microstructural homogenization and increase of mechanical resistance. The starting material used was a highly pure, oligocrystalline niobium sample which was subjected to 80% reduction via cold rolling. Such material was cut in dimensions of 9.0mm x 9.0mm x 50mm and taken after the pressing. The pressing was performed in a single pass in a matrix with an angle of intersection between the channels of ɸ = 90 ° and arc of curvature Ψ = 37 °, which subjected the material to the equivalent strain of ε≈1. In addition, a constant processing speed of 5 mm / min was imposed. The microstructural characterizations were restricted to the internal region of a single grain, and the analyzes were done in the longitudinal and transverse sections of the sample processed via ecap and in the corresponding sections of the laminate. The results were obtained by scanning electron microscope (SEM), optical microscope (OM), microhardness measurements (each section being 225 measurements) and hardness distribution map. In the longitudinal section, it was found that the deformation structures were distributed more evenly and with banding regions oriented preferably from 45 to 60º in relation to the extrusion direction. In the cross section, a more uniform distribution of the deformation structures occurred also, presenting characteristics of intercepting bands in several directions and with a coarser appearance. Regarding mechanical strength, both sections showed a greater uniformity in the hardness distribution after ECAP pass, but without a significant increase in the mean hardness value. The average hardness value in the longitudinal section was 118 Vickers (initially 112 Vickers) and in the cross section the average value found was 111 Vickers (initially it was 106 Vickers). The research found that the processing route used resulted in microstructural homogenization and that there was no significant increase in hardness after ECAP pass due to the dynamic recovery process. | - |
Descrição: dc.description | 54 p. | - |
Formato: dc.format | application/pdf | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Open Access | - |
Direitos: dc.rights | CC-BY-SA | - |
Palavras-chave: dc.subject | ECAP | - |
Palavras-chave: dc.subject | Laminação a frio | - |
Palavras-chave: dc.subject | Nióbio | - |
Palavras-chave: dc.subject | Prensagem em canal equiangular | - |
Palavras-chave: dc.subject | Deformação plástica | - |
Palavras-chave: dc.subject | Microestrutura | - |
Palavras-chave: dc.subject | Engenharia Metalúrgica | - |
Palavras-chave: dc.subject | Produção intelectual | - |
Palavras-chave: dc.subject | ECAP | - |
Palavras-chave: dc.subject | Cold rolling | - |
Palavras-chave: dc.subject | Niobium | - |
Título: dc.title | Caracterização microestrutural de nióbio oligocristalino laminado a frio e posteriormente deformado via ECAP | - |
Tipo de arquivo: dc.type | Dissertação | - |
Aparece nas coleções: | Repositório Institucional da Universidade Federal Fluminense - RiUFF |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: