Caracterização microestrutural da liga AL AA1070 deformada via prensagem em canais equiangulares a frio através das rotas BA e BC

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorLins, Jefferson Fabrício Cardoso-
Autor(es): dc.contributorhttp://lattes.cnpq.br/7528952471956006-
Autor(es): dc.contributorCampos, Marcos Flavio de-
Autor(es): dc.contributorhttp://lattes.cnpq.br/5526383460332378-
Autor(es): dc.contributorHupalo, Marcio Ferreira-
Autor(es): dc.contributorhttp://lattes.cnpq.br/8329328114313600-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4795432585496326-
Autor(es): dc.creatorHauegen, Christien Guisard-
Data de aceite: dc.date.accessioned2024-07-11T17:27:31Z-
Data de disponibilização: dc.date.available2024-07-11T17:27:31Z-
Data de envio: dc.date.issued2022-10-26-
Data de envio: dc.date.issued2022-10-26-
Fonte completa do material: dc.identifierhttp://app.uff.br/riuff/handle/1/26702-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/750703-
Descrição: dc.descriptionO principal objetivo deste trabalho foi investigar o comportamento da textura cristalográfica a partir do refinamento microestrutural de uma liga Al AA1070, comercialmente pura, deformada severamente via prensagem em canais equiangulares (ECAP – Equal Channel Angular Pressing). A microestrutura de partida era composta por grãos grosseiros advindos de um processo industrial de laminação a quente. A técnica de DPS (Deformação Plástica Severa) utilizada consiste na prensagem de um tarugo previamente lubrificado que é forçado a escoar repetidas vezes através de dois canais idênticos. A liga de alumínio investigada foi submetida a 5 passes de deformação via as rotas BA e BC numa matriz em que os canais formavam ângulo de 90° entre si. O processamento do material ocorreu a temperatura ambiente e acumulou deformação de 5,95. Foram utilizadas técnicas de Microscopia Eletrônica de Varredura (MEV) e difração de elétrons retroespalhados (EBSD – Electron Backscatter Diffraction) para a realização de uma análise sistemática da evolução da microestrutura e da textura cristalográfica do material. Foram observadas bandas de deformação com a aplicação dos primeiros passes independente da rota utilizada. Índícios de nucleação de novos grãos foram evidenciados a partir da análise dos níveis de fator de Taylor e dos mapas de Kernel de microestruturas do material após o 3º passe de deformação. A deformação cisalhante que ocorreu na interseção entre os canais durante o processamento via ECAP permitiu um intenso refinamento dos grãos associado a uma competição entre recristalização e recuperação dinâmicas. Foi possível notar que os mecanismos responsáveis pela redução do tamanho de grão foram a partir de processos de subdivisão por meio de fragmentação e rotação de grãos. Os contornos variam (Δ ≈ 0,12­0,14) no 3° e 4° passe até que no 5º passe de deformação a mesma intensidade de fibras foi apresentada em φ2 = 25­30°. A dureza do material atingiu um estado estacionário logo ao primeiro passe de deformação não apresentando variação de suas características a partir da aplicação dos passes subseqüentes.-
Descrição: dc.descriptionThe main objective of this study was to investigate the behavior of crystallographic texture obtained from the microstructural refinement of an Al AA1070 commercially pure alloy, severely deformed via ECAP (Equal Channel Angular Pressing). The starting microstructure was composed of coarse grains from the industrial hot rolling process. This SPD (Severe Plastic Deformation) technique is the pressing of a prelubricated billet which is forced to flow repeatedly through two identical channels. This investigation was subjected to 5 passes through the routes BA and BC. The processing was iniciated at room temperature and the accumulated 5,95 of strain. Techniques of Scanning Electron Microscopy (SEM) and Electron Backscatter Diffraction (EBSD) were used to perform a systematic analysis of the microstructure evolution and crystallographic texture of the material. Deformation bands were observed after the first pass. The 3rd deformation pass of the investigated routes found new grains from the microstructure map analysis with Taylor factor concepts and Kernel maps. The shear deformation that occurred at the intersection between channels during processing via ECAP allowed an intensive grain refinement associated with a competition between recrystallization and dynamic recovery. We observed that the mechanisms responsible for the reduction of grain size was from subdivision process through fragmentations and grain rotations. The contours range (Δ ≈ 0,12 ­ 0,14 ) in the 3rd and 4th pass. The 5th deformation pass shown the same intensity of fibers in φ2 = 25­30°. The mechanical properties of hardness reached a steady state with the first pass application showing no changes in its characteristics.-
Descrição: dc.description93 p.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsOpen Access-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectEBSD-
Palavras-chave: dc.subjectECAP-
Palavras-chave: dc.subjectRefinamento de grão-
Palavras-chave: dc.subjectTextura cristalográfica-
Palavras-chave: dc.subjectPrensagem em canais equiangulares-
Palavras-chave: dc.subjectDifração de elétrons retroespalhados-
Palavras-chave: dc.subjectRefinamento de grãos-
Palavras-chave: dc.subjectEngenharia Metalúrgica-
Palavras-chave: dc.subjectProdução intelectual-
Palavras-chave: dc.subjectEBSD-
Palavras-chave: dc.subjectAluminum-
Palavras-chave: dc.subjectECAP-
Palavras-chave: dc.subjectGrain refinement-
Palavras-chave: dc.subjectCrystallographic texture-
Título: dc.titleCaracterização microestrutural da liga AL AA1070 deformada via prensagem em canais equiangulares a frio através das rotas BA e BC-
Tipo de arquivo: dc.typeDissertação-