Avaliação da qualidade superficial e das tensões residuais geradas no torneamento de liga de alumínio AA6351

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorFonseca, Maria da Penha Cindra-
Autor(es): dc.contributorBenini, Lucas-
Autor(es): dc.contributorTomaz, Ítalo do Valle-
Autor(es): dc.creatorGuerra, Victor Mallmann-
Data de aceite: dc.date.accessioned2024-07-11T17:26:24Z-
Data de disponibilização: dc.date.available2024-07-11T17:26:24Z-
Data de envio: dc.date.issued2020-11-23-
Data de envio: dc.date.issued2020-11-23-
Data de envio: dc.date.issued2019-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/16061-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/750321-
Descrição: dc.descriptionO interesse no estudo de ligas de alumínio da série 6XXX tem crescido cada vez mais, principalmente devido à crescente demanda da indústria. Essas ligas possuem alta resistência mecânica aliada à boa usinabilidade e resistência à corrosão. Visando uma extensão da vida útil dos diversos componentes mecânicos, o conhecimento do estado de tensões residuais ganhou grande relevância, pois impacta enormemente sobre a resistência à fadiga de um componente. O presente trabalho tem por objetivo estudar o comportamento das tensões residuais e a qualidade da superfície de amostras da liga de alumínio AA6351 usinadas por torneamento com diferentes parâmetros de corte. As tensões residuais foram analisadas por difração de raios-X utilizando o método do sen2ψ. Os resultados mostram que as tensões geradas no torneamento das amostras foram majoritariamente trativas. Medições de rugosidade média (Ra) foram realizadas a fim de avaliar a qualidade das superfícies geradas na usinagem e análises de variância ANOVA complementaram o estudo-
Descrição: dc.descriptionThe interest in the study of 6XXX series of aluminum alloys has increased steadily, mainly due to the growing demand from the automotive industry. These alloys are characterized by its good mechanical strength coupled with good workability and excellent corrosion resistance Aiming the extension of the lifespan of mechanical components, the study of residual stress received more relevance, because it impacts directly at the fatigue strength of the material. This work intent to study the behavior of surface residual stresses and surface quality of AA 6351 aluminum alloy machined by turning, with different cutting parameters. Surface residual stresses were analyzed by X-ray diffraction by the sen2ψ method, the results show that the residual stress generated by the turning was mostly tensile. Mean surface roughness (Ra) was measured aiming to evaluate the surface quality of the machined material. Analysis of variance by the ANOVA method complemented the study-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectLiga de alumínio AA6351-
Palavras-chave: dc.subjectTorneamento-
Palavras-chave: dc.subjectTensões residuais-
Palavras-chave: dc.subjectDifração de raios-X-
Palavras-chave: dc.subjectRugosidade-
Palavras-chave: dc.subjectLiga de alumínio-
Palavras-chave: dc.subjectTorneamento-
Palavras-chave: dc.subjectTensão residual-
Palavras-chave: dc.subjectDifração de raios X-
Palavras-chave: dc.subjectAA6351 aluminum alloy-
Palavras-chave: dc.subjectTurning-
Palavras-chave: dc.subjectResidual stress-
Palavras-chave: dc.subjectX-ray diffraction-
Palavras-chave: dc.subjectSurface roughness-
Título: dc.titleAvaliação da qualidade superficial e das tensões residuais geradas no torneamento de liga de alumínio AA6351-
Tipo de arquivo: dc.typeTrabalho de conclusão de curso-