Análise imediata e a longo prazo da adesividade do Biodentine a dentina radicular

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorGouvêa, Cresus Vinicius Depes de-
Autor(es): dc.contributorVianna, Gustavo André De-Deus Carneiro-
Autor(es): dc.contributorhttp://lattes.cnpq.br/4330919500365686-
Autor(es): dc.contributorhttp://lattes.cnpq.br/9924799549240650-
Autor(es): dc.creatorFerreira, Caroline Baptista-
Data de aceite: dc.date.accessioned2024-07-11T17:26:24Z-
Data de disponibilização: dc.date.available2024-07-11T17:26:24Z-
Data de envio: dc.date.issued2019-03-15-
Data de envio: dc.date.issued2019-03-15-
Data de envio: dc.date.issued2014-
Fonte completa do material: dc.identifierhttps://app.uff.br/riuff/handle/1/8815-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/750318-
Descrição: dc.descriptionO objetivo deste trabalho foi avaliar a adesividade à dentina radicular do BiodentineT através de um ensaio de resistência ao cisalhamento por extrusão (push-out). O MTA branco foi o material de referência utilizado para comparação. Foram utilizados seis caninos superiores, os quais tiveram suas raízes seccionadas, perpendicularmente ao seu longo eixo, em fatias de 1 mm de espessura. Porém, apenas a primeira fatia de cada terço radicular foi selecionada, dando em um total de 18 fatias. Em cada fatia foram realizados 4 orifícios na região de dentina radicular, resultando em 64 orifícios. Após isso, as fatias foram divididas ao meio no intuito de se obter dois orifícios em cada metade, onde um orifício foi obturado com Biodentine e o outro com MTA branco. Todas as fatias foram armazenadas em solução tampão fosfato salina (PBS) até a realização do push out. Dois tempos experimentais foram utilizados: imediato (7 dias) e tardio (60 dias). Com iss o, 4 grupos experimentais (n = 18 por grupo) foram criados: grupo I - Biodentine aos 7 dias; grupo II - MTA branco aos 7 dias; grupo III - Biodentine aos 60 dias; e grupo IV - MTA branco aos 60 dias. Os resultados mostraram que tanto o Biodentine como o MTA branco apresentaram uma adesividade aumentada aos 60 dias quando comparada aos 7 dias. Entretanto, os valores de adesão do Biodentine foram superiores aos valores do MTA branco em ambos os tempos experimentais. Concluiu-se então que a força de adesão à dentina radicular do Biodentine foi significantemente superior a do MTA branco nos dois tempos experimentais.-
Descrição: dc.descriptionThe purpose of this study was to evaluate the adhesion to root dentin BiodentineT through a trial by extrusion shear strength ( push-out ) . White MTA was the reference material used for comparison. Six upper canines, which roots were sectioned perpendicular to the long axis in slices of 1 mm thickness were used. However, only the first slice of each root third was selected , giving a total of 18 slices . In each slice 4 holes were made in the area of root dentin , resulting in holes 64 . After that, the slices were halved in order to obtain two holes in each half of a hole which were filled with white and the other Biodentine MTA. All slices were stored in phosphate buffered saline (PBS) until the completion of the push October Instant (7 days ) and late (60 days) Two time points were used. With iss , 4 experimental groups ( n = 18 per group ) were created : group I - Biodentine at 7 days ; Group II - white MTA after 7 days; Group III - Biodentine at 60 days ; and group IV - white MTA after 60 days. The results showed that both Biodentine as white MTA had increased at 60 days when compared at 7 days adhesiveness . However, the values of the membership Biodentine were higher than white MTA in both experimental periods . It was concluded that the strength of adhesion to root dentin of Biodentine was significantly higher than that of white MTA in both experimental periods .-
Descrição: dc.description48f.-
Formato: dc.formatapplication/pdf-
Idioma: dc.languagept_BR-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightsopenAccess-
Direitos: dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/-
Direitos: dc.rightsCC-BY-SA-
Palavras-chave: dc.subjectAdesividade-
Palavras-chave: dc.subjectCimentos reparadores a base de silicato-
Palavras-chave: dc.subjectMTA-
Palavras-chave: dc.subjectBiodentine-
Palavras-chave: dc.subjectCimento de silicato-
Palavras-chave: dc.subjectDentina-
Palavras-chave: dc.subjectMaterial dentário-
Palavras-chave: dc.subjectAdhesion-
Palavras-chave: dc.subjectSilicate-based repaired cement-
Palavras-chave: dc.subjectMTA-
Palavras-chave: dc.subjectBiodentine-
Título: dc.titleAnálise imediata e a longo prazo da adesividade do Biodentine a dentina radicular-
Tipo de arquivo: dc.typeDissertação-