Atenção: Todas as denúncias são sigilosas e sua identidade será preservada.
Os campos nome e e-mail são de preenchimento opcional
Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Cândido, Luiz Cláudio | - |
Autor(es): dc.creator | Silva, José Geraldo Araújo | - |
Data de aceite: dc.date.accessioned | 2019-11-06T13:36:26Z | - |
Data de disponibilização: dc.date.available | 2019-11-06T13:36:26Z | - |
Data de envio: dc.date.issued | 2016-01-28 | - |
Data de envio: dc.date.issued | 2016-01-28 | - |
Data de envio: dc.date.issued | 2001 | - |
Fonte completa do material: dc.identifier | http://www.repositorio.ufop.br/handle/123456789/6244 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/559256 | - |
Descrição: dc.description | Programa de Pós Graduação em Engenharia Civil. Departamento de Engenharia Civil, Escola de Minas, Universidade Federal de Ouro Preto. | - |
Descrição: dc.description | Este trabalho apresenta o estudo do comportamento de juntas soldadas de um aço estrutural, do tipo SAC 50, sob fadiga. O material foi soldado através do emprego do processo ao arco elétrico com eletrodo revestido. Além dos ensaios mecânicos tradicionais, aplicou-se metodologias da Mecânica de Fratura, através de ensaios de tenacidade à fratura (COD e Integral J), e ensaios de propagação de trincas por fadiga. Avaliou-se as características comportamentais das três regiões do material: zona fundida, zona termicamente afetada e metal base. Verificou-se, em termos de tenacidade, que as três regiões do material, pelo efeito da soldagem, apresentaram comportamento semelhante. Correlacionou-se os valores obtidos nos ensaios de tenacidade com ensaios de impacto Charpy. A zona fundida apresentou valor de COD, δm, maior que a zona termicamente afetada e o metal base, o que significa maior resistência à propagação de trincas. O efeito do fator R não influenciou significativamente o posicionamento das curvas de propagação de trinca por fadiga na região II. No entanto, para R = 0,7, o valor limiar (threshold), ΔKth, sofreu uma alteração significativa, diminuindo para o caso do metal base. Pôde-se verificar, também, que para o ensaio de propagação de trinca por fadiga, o valor limiar, para o metal base foi inferior às outras regiões do CP, caracterizando um pior desempenho. A partir do ensaio de Integral J pôde-se estimar um valor de JQ para o metal base. E ainda, fez-se análises microfractográficas dos CPs ensaiados. Verificou-se o aspecto dúctil das fraturas do material, através de “dimples”. No entanto, para ensaios de impacto Charpy, em ‘baixas” temperaturas, o material apresentou o aspecto frágil das fraturas através da presença de facetas de clivagem. ______________________________________________________________________________________________ | - |
Descrição: dc.description | ABSTRACT : This work studied the behavior of welded joints of structural steel type “SAC 50” under fatigue. The material was welded using the process of electric arc with coated electrodes. Besides using the traditional mechanical tests, methods of fractures mechanics were applied through tests of fracture resistance (COD and J integral) and of the fatigue crack propagation. The behavioral features of three areas of interest (cast zone, heat affected zone and base metal) were determined. In terms of strength, the conclusions were that the three areas presented similar behavior considering the welding effect. The values obtained from resistance tests were later related to those from Charpy impact tests. The cast zone presented a higher COD value than the base metal i.e. higher fracture toughness. The effect of the R factor did not present a strong influence in the position of the fatigue crack propagation curves caused by fatigue. However, for R = 0.7, the threshold value (ΔKth), was slightly altered, being reduced in the case of the base metal. For the fatigue crack propagation test, the threshold value for the base metal was lower than that in the another areas of the specimens, indicating a worse performance. Considering the J integral test, it is possible to estimate a JQ value for the base metal. Also, microfractography analyses of specimen were made. The ductile aspect of the material fractures was revealed by the existence of dimples, although, for the Charpy impact test performed under low temperature, the brittle aspect was revealed by. | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Open access. | - |
Palavras-chave: dc.subject | Aço estrutural patinável | - |
Palavras-chave: dc.subject | Junta soldada | - |
Palavras-chave: dc.subject | Metais - fadiga | - |
Título: dc.title | Avaliação comportamental de juntas soldadas de um aço estrutural do tipo SAC 50 sob fadiga. | - |
Tipo de arquivo: dc.type | livro digital | - |
Aparece nas coleções: | Repositório Institucional - UFOP |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: