Atenção: Todas as denúncias são sigilosas e sua identidade será preservada.
Os campos nome e e-mail são de preenchimento opcional
Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Godefroid, Leonardo Barbosa | - |
Autor(es): dc.contributor | Cândido, Luiz Cláudio | - |
Autor(es): dc.creator | Viana, Thiago Gomes | - |
Data de aceite: dc.date.accessioned | 2019-11-06T13:34:59Z | - |
Data de disponibilização: dc.date.available | 2019-11-06T13:34:59Z | - |
Data de envio: dc.date.issued | 2015-10-26 | - |
Data de envio: dc.date.issued | 2015-10-26 | - |
Data de envio: dc.date.issued | 2015 | - |
Fonte completa do material: dc.identifier | http://www.repositorio.ufop.br/handle/123456789/5699 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/558656 | - |
Descrição: dc.description | Programa de Pós-Graduação em Engenharia de Materiais. Rede Temática em Engenharia de Materiais, Pró-Reitoria de Pesquisa e Pós-Graduação, Universidade Federal de Ouro Preto. | - |
Descrição: dc.description | A indústria ferroviária tem como um dos principais modos de falhas a fratura por fadiga iniciada no boleto de trilhos e com sentido de propagação transversal em direção à alma e patim do trilho, gerando paralisação da via permanente e muitas vezes acidentes de proporções catastróficas. Três tipos de trilhos (aços) premium (alta resistência mecânica) foram estudados pela caracterização metalúrgica e mecânica, principalmente por intermédio de conceitos da Mecânica de Fratura, através dos ensaios de propagação de trinca por fadiga (da/dN x ΔK) e de tenacidade à fratura (KIC). Os aços estudados foram: 1. tratado térmicamente no boleto e microligado ao vanádio, 2. tratado térmicamente no boleto e hipereutetóide e 3. tratado térmicamente na profundidade do boleto. Nos resultados obtidos o aço tratado térmicamente no boleto e hipereutetóide mostrou-se com o melhor desempenho em relação a propagação de trinca por fadiga, além de mostrar-se com maior tenacidade à fratura. Desta forma, o aço tratado térmicamente no boleto e hipereutetóide pode utilizar ciclos mais longos (espaçados) de manutenção preventiva como inspeção por ultrassom, esmerilhamento e substituição, tornando-se o mais recomendado a ser adotado na via permanente entre os aços estudados. _________________________________________________________________________________________ | - |
Descrição: dc.description | ABSTRACT: The railway industry has as a major failure modes fatigue fracture started in the rail head and with direction of propagation to the web and base of rail, causing interruption of railway and often accidents of catastrophic proportions. Three types of rails (steel) premium (high strength) were studied by metallurgical and mechanical characterization, principally by concepts of Fracture Mechanics, through the crack fatigue propagation tests (da / dN x ΔK) and of Fracture Toughness (KIC). The steels studied were: 1. Heat treated in rail head and micro alloyed by vanadium, 2. Heat treated in rail head and hypereutectoid and 3. Heat treated in the depth of rail head. In the results obtained the steel heat treated in rail head and hypereutectoid showed with the best performance in relation to the crack propagation fatigue, and showed with better fracture toughness. The steel heat treated in rail head and hypereutectoid needs longer cycles (spaced) of preventive maintenance inspection as ultrasound, grinding and replacement, becoming the most recommended to be adopted in railway between the studied steels. | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Autorização concedida ao Repositório Institucional da UFOP pelo autor, 07/07/2015, com as seguintes condições: disponível sob Licença Creative Commons 4.0, que permite copiar, distribuir e transmitir o trabalho, desde que seja citado o autor e licenciante. Não permite o uso para fins comerciais nem a adaptação desta. | - |
Palavras-chave: dc.subject | Análise e seleção de materiais | - |
Palavras-chave: dc.subject | Aço | - |
Palavras-chave: dc.subject | Falhas estruturais | - |
Palavras-chave: dc.subject | Fadiga dos materiais | - |
Título: dc.title | Estudo comparativo do comportamento de aços (trilhos) premium na tenacidade à fratura e na propagação de trinca por fadiga, de aplicação ferroviária. | - |
Tipo de arquivo: dc.type | livro digital | - |
Aparece nas coleções: | Repositório Institucional - UFOP |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: