Atenção: Todas as denúncias são sigilosas e sua identidade será preservada.
Os campos nome e e-mail são de preenchimento opcional
Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.creator | Vieira, David Hebert | - |
Autor(es): dc.creator | Pinto, Daniel Fraga | - |
Autor(es): dc.creator | Carvalho, José Antônio Nunes de | - |
Autor(es): dc.creator | SairreBálsamo, Paulo Sérgio de | - |
Autor(es): dc.creator | Godefroid, Leonardo Barbosa | - |
Autor(es): dc.creator | Cândido, Luiz Cláudio | - |
Data de aceite: dc.date.accessioned | 2019-11-06T13:34:34Z | - |
Data de disponibilização: dc.date.available | 2019-11-06T13:34:34Z | - |
Data de envio: dc.date.issued | 2015-05-19 | - |
Data de envio: dc.date.issued | 2015-05-19 | - |
Data de envio: dc.date.issued | 2007 | - |
Fonte completa do material: dc.identifier | http://www.repositorio.ufop.br/handle/123456789/5390 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/558477 | - |
Descrição: dc.description | Avaliou-se a suscetibilidade de aços inoxidáveis ferríticos soldados com aços inoxidáveis austeníticos quanto ao fenômeno de trincamento por corrosão sob tensão (TCST), em soluções aquosas contendo 3,5% (peso) NaCl, e 42% (peso) MgCl2. As técnicas empregadas para ensaios de TCST foram: carga constante e deformação constante no eletrodo. Empregaram-se metodologias da mecânica de fratura, onde se utilizaram CPs do tipo tração-compacto, C(T). Foi verificado que os materiais em estudo foram suscetíveis a TCST em solução aquosa contendo 42% MgCl2, na temperatura de ebulição. Notou-se que o trincamento por CST ocorre a partir da pré-trinca, na zona austenítica, e prossegue para a região ferrítica. Análises microfractográficas indicaram que tanto na região da fratura por TCST quanto na zona de arrancamento final por tração a fratura foi frágil. __________________________________________________________________________________________ | - |
Descrição: dc.description | ABSTRACT: The behavior in stress corrosion cracking (SCC) of ferritic stainless steels welded with austenitic stainless steels was evaluated in aqueous solutions containing 3.5 (weight%) NaCl, and 42 (weight%) MgCl2 have been employed. The experiments included constant load and constant deformation of the electrode. Metodology of mechanical fracture was applied where precracked compact type – C(T)s – specimens have been used. Their fractographic aspects after SCC were analyzed. It was verified that the materials in study were SCC susceptible in aqueous solution containing 42 weight% MgCl2. It was noticed that the cracks start from the precrack in the austenitic area and it continues inside the ferritic area. | - |
Idioma: dc.language | pt_BR | - |
Direitos: dc.rights | Autorização concedida ao Repositório Institucional da UFOP pela Tecnologia em Metalurgia Materiais e Mineração em 22/11/2013 para depositar uma cópia eletrônica dos artigos publicados por esse periódico em que ao menos um dos autores é aluno ou professor da UFOP. | - |
Palavras-chave: dc.subject | Aços inoxidáveis | - |
Palavras-chave: dc.subject | Welding | - |
Palavras-chave: dc.subject | Corrosão sob tensão | - |
Título: dc.title | Comportamento em corrosão de juntas soldadas de aços inoxidáveis em meios contendo íons cloretos. | - |
Título: dc.title | Corrosion behavior of stainless steels welds in chloride solutions | - |
Aparece nas coleções: | Repositório Institucional - UFOP |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: