Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.creator | Manhabosco, Taíse Matte | - |
Autor(es): dc.creator | Barboza, A. P. M. | - |
Autor(es): dc.creator | Batista, Ronaldo Junio Campos | - |
Autor(es): dc.creator | Neves, B. R. A. | - |
Autor(es): dc.creator | Muller, Iduvirges Lourdes | - |
Data de aceite: dc.date.accessioned | 2019-11-06T13:32:21Z | - |
Data de disponibilização: dc.date.available | 2019-11-06T13:32:21Z | - |
Data de envio: dc.date.issued | 2015-03-12 | - |
Data de envio: dc.date.issued | 2015-03-12 | - |
Data de envio: dc.date.issued | 2013 | - |
Fonte completa do material: dc.identifier | http://www.repositorio.ufop.br/handle/123456789/4621 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/557561 | - |
Descrição: dc.description | This work presents a comparative wear, corrosion and wear–corrosion (the last one in a simulated physiological solution) study of graphite-like a-C:H (GLCH) films deposited on bare and nitrided Ti6Al4V alloy. Films, deposited by r.f. PACVD, presented low porosity and promoted high corrosion resistance. The friction coefficient of the films was very lowwith appreciablewear resistance at roomconditions. However, due to the simultaneous action of both load and the corrosive environment in wear–corrosion tests a marked reduction in the coating lifetime was observed. Unexpectedly, films deposited on the nitrided alloy presented a lifetime at least ten times shorter than that of films on bare alloy. We explain such a result in terms of film/substrate interaction. The weak GLCH/nitride alloy interaction facilitates fluid penetration between the film and the substratewhich leads to a fast film delamination. Such an interpretation is supported by force curve measurements, which show that the interaction between GLCH and nitrided alloy is four times weaker than that between GLCH and bare alloy. | - |
Idioma: dc.language | en | - |
Direitos: dc.rights | O Periódico Diamond and Related Materials concede permissão para depósito do artigo no Repositório Institucional da UFOP. Número da licença: 3566050324673. | - |
Palavras-chave: dc.subject | Diamond-like carbon | - |
Palavras-chave: dc.subject | Tribology | - |
Palavras-chave: dc.subject | Corrosion | - |
Palavras-chave: dc.subject | Scanning probe techniques | - |
Título: dc.title | Corrosion, wear and wear–corrosion behavior of graphite-like a-C:H films deposited on bare and nitrided titanium alloy. | - |
Aparece nas coleções: | Repositório Institucional - UFOP |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: