Influência de silicato de sódio de diferentes módulos e fluorsilicato de sódio na flotação direta de minério de ferro.

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.contributorLima, Rosa Malena Fernandes-
Autor(es): dc.creatorArantes, Renato de Souza-
Data de aceite: dc.date.accessioned2019-11-06T13:28:41Z-
Data de disponibilização: dc.date.available2019-11-06T13:28:41Z-
Data de envio: dc.date.issued2013-06-19-
Data de envio: dc.date.issued2013-06-19-
Data de envio: dc.date.issued2012-
Fonte completa do material: dc.identifierhttp://hdl.handle.net/123456789/2944-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/556117-
Descrição: dc.descriptionPara o aproveitamento de minérios de baixos teores, é necessário realizar estudos mais detalhados de caracterização tecnológica dos mesmos, visando obter informações tanto para o estabelecimento de rotas de processos mais eficientes, quanto para a previsão do comportamento desses minérios frente ao processo. Portanto, o objetivo deste trabalho é estudar a viabilidade de concentração de amostras de minérios de ferro por flotação aniônica direta. O minério utilizado nos testes foi fornecido pela mina de Fábrica Nova, da Vale, com 3,94 g/cm3 de densidade e d80 em 121 μm. Os principais minerais encontrados foram a hematita, a goethita e o quartzo. O mecanismo de adsorção para todos os reagentes testados (coletores oleato de sódio e hidroxamato e depressores silicato de sódio de módulos 1, 2,26 e 3,33 e flluorsilicato de sódio) foi adsorção específica, de acordo com os ensaios de potencial zeta realizados com os minerais hematita e quartzo. Para os estudos de flotação em bancada, é possível perceber que o fluorsilicato de sódio se tornou mais promissor usado com o hidroxamato como coletor, e que o oleato de sódio foi mais eficaz quando o silicato de sódio de módulo 3,33 foi utilizado para deprimir SiO2. __________________________________________________________________________________________-
Descrição: dc.descriptionABSTRACT: In order to take advantage of low grade ores is necessary to realize advanced researches of technological characterization of then, in the hope to acquire report as many to establish more effective means of process, as to forethought the behavior of this ores in the process. Therefore, the objective of this work is establishing the feasibility of concentration of iron ore samples by means of anionic flotation. The ore used in this work was provided by Vale’s Fábrica Nova mining, with density of 3.94 g/cm3, 6.65% of humidity, d80 of 121 μm. The mean ores found was hematite, goethite and quartz. The adsorption mechanism for all the reagents tested (sodium oleate and hidroxamate collectors and sodium silicate of modulus 1, 2.26 and 3.33 and sodium fluorsilicate depressants) was specific adsorption, according to the zeta potential assays realized with hematite and quartz. In the bench-scale flotation assays, were possible perceive that sodium fluorsilicate depressant was the more promising when used associated with hidroxamate as collector, whereas sodium oleate collector was more effective when sodium silicate of modulus 3.33 was used to depress SiO2.-
Idioma: dc.languagept_BR-
Publicador: dc.publisherPrograma de Pós-Graduação em Engenharia Mineral. Departamento de Engenharia de Minas, Universidade Federal de Ouro Preto.-
Palavras-chave: dc.subjectMinério de ferro-
Palavras-chave: dc.subjectFlotação aniônica-
Palavras-chave: dc.subjectOleato de sódio-
Palavras-chave: dc.subjectTratamento de minérios-
Título: dc.titleInfluência de silicato de sódio de diferentes módulos e fluorsilicato de sódio na flotação direta de minério de ferro.-
Tipo de arquivo: dc.typelivro digital-
Aparece nas coleções:Repositório Institucional - UFOP

Não existem arquivos associados a este item.