Atenção: Todas as denúncias são sigilosas e sua identidade será preservada.
Os campos nome e e-mail são de preenchimento opcional
Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Cândido, Luiz Cláudio | - |
Autor(es): dc.creator | Lacerda, José Carlos de | - |
Data de aceite: dc.date.accessioned | 2019-11-06T13:27:59Z | - |
Data de disponibilização: dc.date.available | 2019-11-06T13:27:59Z | - |
Data de envio: dc.date.issued | 2013-04-26 | - |
Data de envio: dc.date.issued | 2013-04-26 | - |
Data de envio: dc.date.issued | 2007 | - |
Fonte completa do material: dc.identifier | http://hdl.handle.net/123456789/2799 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/555928 | - |
Descrição: dc.description | A grande aplicação do aço inoxidável ferrítico AISI 409 na construção de reservatórios de líquidos diversos, caldeiras, radiadores e mais recentemente nos sistemas de exaustão de gases de veículos automotores, tem despertado um grande interesse em se conhecer melhor o comportamento mecânico de soldas destes aços inoxidáveis, sobretudo no que diz respeito à sua transição dúctil-frágil. Sabendo-se que a variação do aporte térmico tem efeito significativo no ciclo térmico de soldagem, trabalhou-se com dois diferentes valores, visando observar o seu efeito correlacionado com as duas misturas de gases de proteção empregadas no comportamento dúctil- frágil do material soldado pelo processo GMAW (Gas Metal Arc Welding). Assim, neste trabalho, buscou-se investigar o comportamento dúctil- frágil na zona fundida e zona termicamente afetada de um aço inoxidável AISI 409, soldado pelo processo GMAW em duas condições de energia de soldagem e misturas de gases de proteção da solda, empregando-se ensaios de impacto Charpy, ensaios de microdureza Vickers, análise de imagens microfratográficas e de microestrutura. Como resultado constatou-se que a adição de nitrogênio ao argônio na atmosfera de proteção da solda praticamente não exerceu nenhum efeito na zona termicamente afetada comparado com a atmosfera de argônio sem a adição de nitrogênio. No entanto, na zona fundida, as soldas com atmosfera de proteção com argônio sem a adição de nitrogênio obteve-se resistência ao impacto praticamente o dobro das soldas cuja atmosfera de proteção não tinha a adição de nitrogênio. __________________________________________________________________________________________ | - |
Descrição: dc.description | ABSTRACT: The wide application of ferritic stainless steels AISI 409 in construction of liquid storage reservoirs, boilers, radiators and, more recently, exhaust systems for motor vehicles, has raised a large interest in knowing more about the mechanical behavior of welds of these stainless steels, especially with respect to their ductile-brittle transition zone. Knowing that the variation of the heat input has significant effect over the thermal cycle of welding, it is proposed its variation in order to correlate its influence associated to the variation of composition of the shielding gas, over the brittle-ductile behavior of the material welded by the GMAW (Gas Metal Arc Welding) process. Thus, in this work, it is sought to investigate the ductile-brittle behavior in the molten zone and heat-affected-zone of AISI 409 stainless steel, welded by GMAW process in various conditions of welding energy and compositions of the weld shielding gas, utilizing Charpy impact tests, Vickers hardness tests, fracture and microstructure analysis. The result verified was that addition of nitrogen to argon in weld shielding gas was not cause influence in weld heat-affected-zone compared with weld shielding gas without addition of nitrogen. However, in molten zone, the weld with addition nitrogen to argon shielding gas showed double impact resistance compared with the other weld without addition nitrogen in shielding gas. | - |
Idioma: dc.language | pt_BR | - |
Publicador: dc.publisher | Programa de Pós-Graduação em Engenharia de Materiais. Rede Temática em Engenharia de Materiais, Pró-Reitoria de Pesquisa e Pós-Graduação, Universidade Federal de Ouro Preto. | - |
Palavras-chave: dc.subject | Aço inoxidável | - |
Palavras-chave: dc.subject | Aporte térmico | - |
Palavras-chave: dc.subject | Microfratografias | - |
Palavras-chave: dc.subject | Solda e soldagem | - |
Palavras-chave: dc.subject | Nitrogênio | - |
Título: dc.title | Efeito do aporte térmico e adição de nitrogênio no gás de proteção na transição dúctil-frágil de um aço inoxidável AISI 409 soldado pelo processo GMAW | - |
Tipo de arquivo: dc.type | livro digital | - |
Aparece nas coleções: | Repositório Institucional - UFOP |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: