Metadados | Descrição | Idioma |
---|---|---|
Autor(es): dc.contributor | Cota, André Barros | - |
Autor(es): dc.creator | Alcântara, Árysson Penna de | - |
Data de aceite: dc.date.accessioned | 2019-11-06T13:27:18Z | - |
Data de disponibilização: dc.date.available | 2019-11-06T13:27:18Z | - |
Data de envio: dc.date.issued | 2013-03-13 | - |
Data de envio: dc.date.issued | 2013-03-13 | - |
Data de envio: dc.date.issued | 2008 | - |
Fonte completa do material: dc.identifier | http://hdl.handle.net/123456789/2540 | - |
Fonte: dc.identifier.uri | http://educapes.capes.gov.br/handle/capes/555697 | - |
Descrição: dc.description | O presente estudo constitui na análise de falha e na caracterização microestrutural e comportamental de um aço empregado em segmentos de mandril de bobinadeira de um laminador de tiras a quente. A análise de falhas envolveu os procedimentos convencionais para avaliação das causas de fratura do componente estrutural, notadamente análise macroscópica e microfratográfica da fratura, assim como a checagem das especificações para o aço. A caracterização microestrutural foi realizada por microscopia ótica e difratometria de raios-X. A avaliação comportamental envolveu ensaios de tenacidade à fratura (integral J e curva de resistência), ensaios de crescimento de trinca por fadiga, e uma tentativa de simulação de comportamento real do aço, através de ensaios com aplicação de ciclos térmicos. O processo de degradação do material foi caracterizado como sendo de fadiga térmica. O aço apresentou um comportamento mecânico relativamente frágil, indicando a possibilidade de substituição por outro material mais tenaz. A simulação de fadiga térmica foi insuficiente para iniciar o trincamento no material estudado. __________________________________________________________________________________________ | - |
Descrição: dc.description | ABSTRACT: This study is based on analysis of failure and microstructural and behavioral characterization of a steel used in coiler mandrel segments of hot strip mill. The failures analysis involving the conventional procedures for assessing causes of fracture of the structural component, especially macroscopic and microscopic analysis of the fracture as well as checks in the steel specifications. The microstructural characterization was carried out by optical microscopy and X-ray diffraction. The evaluation involved behavioral tests of the fracture toughness (J integral and resistance curve), testing for crack growth caused by fatigue, and an attempt to simulate the actual behavior of steel, through testing with application of thermal cycles. The material degradation process was characterized as being of thermal fatigue. The steel mechanical behavior showed a relatively weak, indicating the possibility of change by other materials more tenacious. The thermal simulation fatigue was insufficient to start the crack in the material studied. | - |
Idioma: dc.language | pt_BR | - |
Publicador: dc.publisher | Programa de Pós-Graduação em Engenharia de Materiais. Rede Temática em Engenharia de Materiais, Pró-Reitoria de Pesquisa e Pós-Graduação, Universidade Federal de Ouro Preto. | - |
Palavras-chave: dc.subject | Escareadores | - |
Palavras-chave: dc.subject | Aço inoxidável | - |
Palavras-chave: dc.subject | Bobinadeiras | - |
Palavras-chave: dc.subject | Metais | - |
Palavras-chave: dc.subject | Engenharia de materiais | - |
Palavras-chave: dc.subject | Mandril | - |
Palavras-chave: dc.subject | Bobinadeira | - |
Palavras-chave: dc.subject | Mandrel | - |
Palavras-chave: dc.subject | Coiler | - |
Palavras-chave: dc.subject | Engenharia metalúrgica | - |
Palavras-chave: dc.subject | Fadiga | - |
Título: dc.title | Estudo da fadiga termo-mecânica em um aço inoxidável martensítico da série X22 | - |
Tipo de arquivo: dc.type | livro digital | - |
Aparece nas coleções: | Repositório Institucional - UFOP |
O Portal eduCAPES é oferecido ao usuário, condicionado à aceitação dos termos, condições e avisos contidos aqui e sem modificações. A CAPES poderá modificar o conteúdo ou formato deste site ou acabar com a sua operação ou suas ferramentas a seu critério único e sem aviso prévio. Ao acessar este portal, você, usuário pessoa física ou jurídica, se declara compreender e aceitar as condições aqui estabelecidas, da seguinte forma: