Decomposição da fase majoritária do cimento Portland - Parte II: alita com adições de Fe e Al

Registro completo de metadados
MetadadosDescriçãoIdioma
Autor(es): dc.creatorTenório, Jorge Alberto Soares-
Autor(es): dc.creatorAraújo, Fernando Gabriel da Silva-
Autor(es): dc.creatorPereira, Sérgio Sônego Raymundo-
Autor(es): dc.creatorFerreira, Andréa Vidal-
Autor(es): dc.creatorEspinosa, Denise Crocce Romano-
Autor(es): dc.creatorBarros, Alexandre Martins-
Data de aceite: dc.date.accessioned2019-11-06T13:25:57Z-
Data de disponibilização: dc.date.available2019-11-06T13:25:57Z-
Data de envio: dc.date.issued2012-12-14-
Data de envio: dc.date.issued2012-12-14-
Data de envio: dc.date.issued2003-
Fonte completa do material: dc.identifierhttp://hdl.handle.net/123456789/2028-
Fonte: dc.identifier.urihttp://educapes.capes.gov.br/handle/capes/555245-
Descrição: dc.descriptionAs propriedades do cimento Portland estão diretamente relacionadas às concentrações de suas fases constituintes, principalmente a alita, a belita, a fase ferrítica e o aluminato. A alita, de composição 3CaO.SiO2 e abreviada por C3S, deve ser o constituinte majoritário do clínquer após o processamento, pois é sua reação de hidratação que confere a resistência mecânica ao cimento curado. A belita, de composição 2CaO.SiO2 e abreviada por C2S, está presente como o primeiro complexo de cal e sílica formado no aquecimento e, sendo mais estável a baixas temperaturas que o C3S, volta a se formar no resfriamento. O aluminato está presente principalmente na forma de 3CaO.Al2O3, abreviado por C3A, enquanto a ferrita aparece como constituinte principalmente na forma 4CaO.Al2O3.Fe2O3, abreviada por C4AF. Os teores de ferrita e alumina, no entanto, alteram a estabilidade da alita, com conseqüentes alterações na reatividade do cimento. O presente trabalho estuda os efeitos de adições de Fe2O3- e Al2O3 sobre a estabilidade da alita e apresenta diagramas CCT para a decomposição da alita na presença desses compostos. ____________________________________________________________________________________________________-
Descrição: dc.descriptionAbstract: The properties of Portland cement are directly related to the concentrations of its major phases, i.e., alite, belite, the ferritic phase and the aluminate phase. Alite, with the composition 3CaO.SiO2, known as C3S, should be the major component of the clinker after processing, once its hydration produces the high yield strengths of cured cement. Belite, with the composition 2CaO.SiO2, known as C2S, is the first lime and silica complex, formed during the heating process. It presents higher stability at low temperatures than C3S, so that it tends to be formed again during the cooling cycle, from the decomposition of alite. The aluminate phase appears mainly with the composition 3CaO.Al2O3, known as C3A, and the ferritic phase appears with the composition 4CaO.Al2O3.Fe2O3, known as C4AF. However, the ferrite and alumina contents affect the alite stability, and consequently, its reactivity. This paper studies the effects of Fe2O3 and Al2O3 additions over the alite stability and presents CCT diagrams for the alite decomposition in the presence of these compounds.-
Idioma: dc.languagept_BR-
Direitos: dc.rightsAutorização concedida ao Repositório Institucional da UFOP pela Revista Escola de Minas em 12/09/2013 para depositar uma cópia eletrônica dos artigos publicados por esse periódico em que ao menos um dos autores é aluno ou professor da UFOP.-
Palavras-chave: dc.subjectCimento-
Palavras-chave: dc.subjectDecomposição alita-
Palavras-chave: dc.subjectEfeitos de Fe e Al-
Palavras-chave: dc.subjectCement-
Palavras-chave: dc.subjectAlite decomposition-
Palavras-chave: dc.subjectFe and Al effects-
Título: dc.titleDecomposição da fase majoritária do cimento Portland - Parte II: alita com adições de Fe e Al-